• TITLE: Rietveld Refinement of Nanocrystalline LiFeO2 Synthesized by Sol-Gel Method and Its Structural and Magnetic Properties

  AUTHORS: K. Vijaya Kumar, A. Sangeetha, A. T. Raghavender, Z. Skoko, G. Nanda Kumar

  KEYWORDS: Nanoparticles; LiFeO2; Structural and Magnetic Properties

  JOURNAL NAME: Journal of Crystallization Process and Technology, Vol.2 No.4, October 17, 2012

  ABSTRACT: Nanocrystalline lithium iron oxide LiFeO2 was synthesized using sol-gel method. Rietveld analysis was performed to confirm the different phases associated in the formation of LiFeO2. Quantitative Rietveld refinement revealed that sample contains: 39.9 wt% of cubic α – LiFeO2 phase, 58.5 wt% of monoclinic β - LiFeO2 and tetragonal 1.7 wt%. of γ - LiFeO2. The nanocrystalline nature of the prepared samples was confirmed by SEM analysis. The magnetic properties of LiFeO2 showed ferromagnetic property at room temperature.