J. S. Beck, J. C. Vartuli, W. J. Roth, M. E. Leonowics, C. T. Kresge, K. D. Schmitt, C. T. –W. Chu, D. H. Olson, E. W. Sheppard, S. B. McCullen, J. B. Higgins and J. L. Schlenker, A new family of mesoporous molecular sieves prepared with liquid crystal templates, J. Am. Chem. Soc. 114 (1992)10834–10843. doi:10.1021/ja00053a020

has been cited by the following article:

• TITLE: Keggin Structure and Surface Acidity of 12-Phosphotungstic Acid Grafted Zr-MCM-48 Mesoporous Molecular Sieves

  AUTHORS: Zhiqi Wang, Juan Navarrete

  KEYWORDS: Zr-MCM-48; Surface Acidity; Heteropolyacid; Spectroscopic Characterization

  JOURNAL NAME: World Journal of Nano Science and Engineering, Vol.2 No.3, September 28, 2012

  ABSTRACT: A zirconium modified MCM-48 mesoporous material was synthesized by surfactant-templated method. Surface grafting Zr-MCM-48 with tungstophosphoric acid led to a great enhancement of both the number of the Br?nsted acid sites and acidity strength in comparison with the bare support. At 100°C, the 30 wt% H3PW12O40/Zr-MCM-48 contained 174 μmol/g Br?nsted acid sites which were 14.5 times greater than that of Zr-MCM-48. The Keggin structure of the grafted heteropolyacid was rather stable after calcination at 400°C for 2 h, approximately 93.3% of Keggin structure in the dispersed heteropolyacid were remained without destruction but slightly distorted in some degree, as evidenced by FTIR characterization and 31P NMR-MAS analysis. This H3PW12O40/Zr-MCM-48 solid with three dimensional mesoporous system, large surface area and very strong Br?nsted acidity will be a promising catalyst for acid catalytic reactions.