S. A. Khan, M. Zulfequar and M. Husain, “Laser-Induced Amorphisation and Crystallization on Se80Te20–xPbx Thin Films,” Vacuum, Vol. 72, No. 3, 2004, pp. 291-296. doi:10.1016/j.vacuum.2003.08.006

has been cited by the following article:

• TITLE: Thermal Characterization of Se80-xTe20Inx Glasses Using Iso-Conversional Methods

  AUTHORS: Renu Shukla, Pragya Agarwal, Ashok Kumar

  KEYWORDS: Crystallization Kinetics; DSC; Iso-Conversional Methods

  JOURNAL NAME: Journal of Crystallization Process and Technology, Vol.2 No.2, April 24, 2012

  ABSTRACT: Alloys of Se80-xTe20Inx glassy system are obtained by quenching technique and crystallization kinetics has been studied using Differential Scanning Calorimetric [DSC] technique. Well defined endothermic and exothermic peaks are ob- served at glass transition temperature (Tg) and crystallization temperature (Tc). From DSC scans, Tc is obtained at dif- ferent heating rates (5, 10, 15, 20, 25 K/min). It is observed that Tc increases with increasing heating rate for a particular glassy alloy. Activation energy of crystallization (Ec) has been calculated by different Non-isothermal Iso-conversional methods, i.e., Kissinger-Akahira-Sunose [KAS], Friedman, Flynn-wall-Ozawa [FWO], Friedman-Ozawa [FO] and Sta-rink methods. It is observed that Ec is dependent on extent of crystallization (α). Activation energy is also found to vary with atomic percentage of In in ternary Se80-xTe20Inx glassy system. The compositional dependence of Ec shows a re-versal in the trend at x = 15 in Se80-xTe20Inx, which is explained in terms of mechanically stabilized structure at this composition.