Chapetti, M.D., Miyata, H., Tagawa, T., Miyata, T. and Fujioka, M. (2005) Fatigue Crack Propagation Behaviour in Ultra-Fine Grained Low Carbon Steel. International Journal of Fatigue, 27, 235-243.
https://doi.org/10.1016/j.ijfatigue.2004.07.004

has been cited by the following article:

• TITLE: The Influence of Abnormal Segregation Band on Mechanical Properties of Hot Rolled Ferrite/Pearlite Steel Plate

  AUTHORS: Rui Feng, Benkui Gong, Hongwei Cui, Yaokun Pan, Jiahui Bao

  KEYWORDS: Ferrite/Pearlite Steel Plate, Segregation, Microstructure, Laminated Fracture

  JOURNAL NAME: Materials Sciences and Applications, Vol.9 No.1, January 10, 2018

  ABSTRACT: In order to further reveal the influence of abnormal segregation band on mechanical properties of hot rolled ferrite/pearlite steel plate, especially on laminated tensile fracture, the experimental method of delamination tension was adopted. In this paper, the thin tensile samples with 3 mm thickness from the surface, 1/4 positions and center along the thickness orientation of test plate were measured, also the relationship between microstructure and mechanical properties was probed. The results show that the center region of hot rolled ferrite/pearlite steel plate exists granular bainite and ferrite mixed grains, which leads to lower plasticity and toughness of this region. During the tensile process, microcracks are generated and extended at the center of steel plate due to the inconsistency of deformation and fracture on the adjacent structures, finally leading to laminated fracture of steel plate.