QD Wang, J Wu, CP Chen, ZP Li, “An investigation of the mechanical behavior of hydrogen storage metal beds on hydriding and dehydriding and several methods of preventing the damage of hydride containers caused by the expansion of hydrogen storage metals,” Journal of the Less-Common Metals, Vol. 131, 1987, pp. 399-407.

has been cited by the following article:

• TITLE: Mechanism Analysis on Stress Accumulation in Cylindrical Vertical-Placed Metal Hydride Reactor

  AUTHORS: Xiaochen Hu, Zhaogang Qi, Feng Qin, Jiangping Chen

  KEYWORDS: Metal Hydride, Stress Accumulation, Pulverization, Densification

  JOURNAL NAME: Energy and Power Engineering, Vol.3 No.4, September 27, 2011

  ABSTRACT: It’s known that the pulverization-densification mechanism of metal hydride may cause the stress accumulation in metal hydrides reactors. In this paper, this idea is proved based on granulometry and a new idea of cycling compression effect is presented, which is caused by the friction between wall and metal hydrides. Through theoretical analysis, the cycling compression effects is shown to increase the localized packing rate from top to down in vertical-placed reactors and thus lead to the maximum deformation in the bottom of reactors, proving that it is the interaction of pulverization-densification effect and cycling compression effect resulting in the stress problems of vertical-placed reactors. Further study points that the effective methods relieving the cycling compress effect are to decrease hydrogen absorption/desorption cycle number, slenderness ratio of reactor, wall friction factor and initial packing rate, or to lower the thermal conductivity and the volume expansion coefficient of metal hydrides.