V. K. Sanda-ranarayanan and D. C. Khan, “Mechanism of the Formation of Nanoscale M-Type Barium Hexaferrite in the Citrate Precursor Method,” Journal of Magnetism and Magnetic Materials, Vol. 153, No. 2, 1996, pp. 337- 346. doi:10.1016/0304-8853(95)00537-4

has been cited by the following article:

• TITLE: Structural and Magnetic Properties of BaCoxFe12xO19 (x = 0.2, 0.4, 0.6, &1.0) Nanoferrites Synthesized via Citrate Sol-Gel Method

  AUTHORS: Sonal Singhal, Kirandish Kaur, Sheenu Jauhar, Santosh Bhukal, S Bansal

  KEYWORDS: Barium Ferrite, Magnetic Moment, Coercivity, XRD

  JOURNAL NAME: World Journal of Condensed Matter Physics, Vol.1 No.3, August 22, 2011

  ABSTRACT: Cobalt substituted barium ferrites, BaCoxFe12-xO19 (x = 0.2, 0.4, 0.6 & 1.0) have been synthesized via citrate sol-gel method. All the samples have been annealed at 1000℃ and characterized using Fourier Transform Infra Red spectroscopy, X-Ray Diffractography and Vibrating Sample Magnetometry. The FT-IR spectra of the samples exhibit two frequency bands in the range of 580 cm-1 and 460 cm-1, corresponding to the formation of metal oxides. The XRD studies reveal a crystallite size of ~55 nm. The saturation magnetization decreases from 96.3 emu/g to 47.8 emu/g with increasing concentration of cobalt due to the lower magnetic moment of Co2+ (3 µB) as compared to Fe3+ (5 µB). The coercivity values also show a decreasing behaviour from 3800 Oe to 1750 Oe with increasing cobalt concentration due to reduced magnetocrystalline anisotropy.