Chen, J., Xiong, X., Xiao, P. and Zhang, H.B. (2010) The Catalytic Effect of Boric Acid on Polyacrylonitrile-Based Carbon Fibers and the Thermal Conductivity of Carbon/Carbon Composites Produced from Them. Carbon, 48, 2341-2346.
http://dx.doi.org/10.1016/j.carbon.2010.03.012

has been cited by the following article:

• TITLE: Thermal Conductivity of Carbon/Carbon Composites with the Fiber/Matrix Interface Modified by Silicon Carbide Nanofibers

  AUTHORS: Jie Chen, Xiang Xiong, Peng Xiao

  KEYWORDS: Silicon Carbide Nanofiber, Chemical Vapor Infiltration, Interface Bonding, Thermal Property

  JOURNAL NAME: Advances in Chemical Engineering and Science, Vol.6 No.4, October 26, 2016

  ABSTRACT: Silicon carbide nanofibers grew on the surface of carbon fibers of a unidirectional carbon preform by CCVD and then chemical vapor infiltration was used to densify the preform to get the SiCNF-C/C composite. The effects of silicon carbide nanofibers on the microstructure of the pyrolytic carbon and the thermal conductivity of the SiCNF-C/C composite were investigated. Results show that silicon carbide nanofibers on the surface of carbon fibers induce the deposition of high texture pyrolytic carbon around them. The interface bonding between carbon fibers and pyrolytic carbon is well adjusted. So the efficiency of heat transfer in the interface of the composite is well enhanced. The thermal conductivity of the SiCNF-C/C composite is greater than that of the C/C composite, especially the thermal conductivity perpendicular to the fiber axis.