• TITLE: The Preparation of Mn-Fe/CNTs Catalyst at the Low-Temperature Selective Catalytic Reduction of NO with NH3

  AUTHORS: Bingnan Ren

  KEYWORDS: Carbon Nanotubes, Catalyst, Low-Temperature Selective Catalytic Reduction

  JOURNAL NAME: Journal of Materials Science and Chemical Engineering, Vol.6 No.12, December 31, 2018

  ABSTRACT: The metal oxide catalyst was prepared by loading MnOx and FeOx on carbon nano-tubes (CNTs) with impregnation method. Then the catalyst was characterized by BET and XPS, and the effect of adding FeOx on MnOx/CNTs catalyst at the low-temperature selective catalytic reduction of NO with NH3 was investigated. The results showed that the active components were loaded suc-cessfully and easily on the carriers by impregnation. The Mn-Fe/CNTs catalyst was chose 10% Fe(NO3)3 solution to impregnate Mn-Fe/CNTs. The species of active components loaded on the catalyst were Fe2O3. The different concentration of impregnant solution played an important role for NO conversion in SCR with NH3. With the increase of the concentration of impregnant solution, the NO conversion of catalysts was increasing initially then decreasing.