H. Samata, Y. Saeki, S. Mizusaki, Y. Nagata, T. C. Oza- wa and A. Sato, “Electro-chemical Crystal Growth of Pe- rovskite Ruthenates,” Journal of Crystal Growth, Vol. 311, No. 3, 2009, pp. 623-626. doi:10.1016/j.jcrysgro.2008.09.042

has been cited by the following article:

• TITLE: Synthesis and Characterization of CaPd3O4 Crystals

  AUTHORS: Hiroaki Samata, Satoshi Tanaka, Soichiro Mizusaki, Yujiro Nagata, Tadashi C. Ozawa, Akira Sato, Kosuke Kosuda

  KEYWORDS: Single Crystal; Electrochemical Technique; CaPd3O4

  JOURNAL NAME: Journal of Crystallization Process and Technology, Vol.2 No.1, January 13, 2012

  ABSTRACT: A new method for the crystal growth of alkaline-earth palladate CaPd3O4 was developed. The crystals were synthesized on a voltage-applied electrode in a molten chloride solvent. The maximum length of the crystal was about 1.5 mm. The X-ray diffraction data were refined well by assuming a cubic structure of the space group Pm n, and the lattice constant a was 5.7471 (10) ?. The temperature dependence of the resistivity showed semiconductor-like characteristics with a very small activation energy Ea of 0.45 meV at low temperatures, and the resistivity at 300 K was 0.1 cm. The temperature dependence of the molar magnetic susceptibility showed the Curie-Weiss paramagnetic behavior with a small molar Curie constant Cmol of 5.0(1) × 10-3 emu K/(mol Oe), indicating the existence of localized spin moments.