SCIRP Mobile Website
Paper Submission

Why Us? >>

  • - Open Access
  • - Peer-reviewed
  • - Rapid publication
  • - Lifetime hosting
  • - Free indexing service
  • - Free promotion service
  • - More citations
  • - Search engine friendly

Free SCIRP Newsletters>>

Add your e-mail address to receive free newsletters from SCIRP.

 

Contact Us >>

WhatsApp  +86 18163351462(WhatsApp)
   
Paper Publishing WeChat
Book Publishing WeChat
(or Email:book@scirp.org)

Article citations

More>>

Shang, J.K. and Ritchie, R.O. (1989) Crack Bridging by Uncracked Ligaments during Fatigue-Crack Growth in SiC-Reinforced Aluminum-Alloy Composites. Metallurgical and Materials Transactions A, 20, 897-908.
https://doi.org/10.1007/BF02651656

has been cited by the following article:

  • TITLE: Crack Growth Behavior in Cemented Carbide by Repeated Thermal Shock

    AUTHORS: Sotomi Ishihara, Hiroshi Shibata, Kenichi Masuda, Hiroko Mikado, Minoru Ishiguro

    KEYWORDS: Fatigue, Cemented Carbide, Repeated Thermal Shock, Fatigue Crack Growth

    JOURNAL NAME: Materials Sciences and Applications, Vol.9 No.4, April 11, 2018

    ABSTRACT: In this study, fatigue crack growth (FCG) behavior of cemented carbide under the repeated thermal shock (RTS) was experimentally evaluated by using the thermal-shock experiment method developed by the authors. Tests were carried out using cemented carbide having two different WC crystal grain sizes. In addition, FCG behavior under rotating bending fatigue (RBF) test was investigated using the same cemented carbides. Then the FCG results obtained by the RTS test and the results of the RBF test obtained at stress ratio, R = -1, were compared with each other. Here, the stress ratio R is defined as, R = σmin/σmax; σmin and σmax are the minimum and the maximum stresses, respectively. From this comparison, it was found that the relation between the rate of fatigue crack growth (FCG) and the maximum stress intensity factor in the RTS tests was equivalent to the one obtained under the RBF tests at stress ratio of -1. From a practical point of view, this result is important as it indicates that it is not necessary to purposely perform RTS experiments. In this research, the effect of WC grain size on the short surface FCG behavior of the cemented carbide was also studied and discussed.