Ye, L., Friedrich, K., Kastel, J. and Mai, Y. (1995) Consolidation of Unidirectional CF/PEEK Composites from Commingled Yarn Prepreg. Composites Science and Technology, 54, 349-358.
https://doi.org/10.1016/0266-3538(95)00061-5

has been cited by the following article:

• TITLE: Improvement of Bending Strength of Carbon Fiber/Thermoplastic Epoxy Composites —Effects of Molecular Weight of Epoxy on Carbon Fiber/Matrix Interfacial Strength and Connection of Cracks in Matrix

  AUTHORS: Hironori Nishida, Kazuya Okubo, Toru Fujii, Valter Carvelli

  KEYWORDS: Thermoplastic Epoxy Composites, Weight-Average Molecular Weight, Interfacial Shear Strength, Crack Propagation, Crack Connecting Probability

  JOURNAL NAME: Open Journal of Composite Materials, Vol.7 No.4, July 27, 2017

  ABSTRACT: The bending strength of carbonfiber/thermoplastic epoxy composites(CF/TP-EP Compo.)hadbi-linear increasewith increase of weight-average molecular weight (Mw) of matrix. The transition in the bending strength appeared at around 55k of Mw (“k”means 103). SEM observation of fractured surface of CF/TP-EP Compo. showed that the fracture mode changed from interfacial failure to fiber breakage dominated failure. The smooth surface of carbon fibers appeared at lower Mw than 55k while some resin remained on the fibers indicating good adhesion between carbon fiber and matrix at higher Mw than 55k. The interfacial shear strength between carbon fiber and matrix bi-linearly increased with an increase of Mw similarly to the bending strength of the composite, measured by the micro droplet test. The dynamic loss tanδof the matrix measured at 2Hz also showed a bi-linear relationship with respect to Mw having a knee point at Mw = 55k. The connection probability of two cracks introduced oneach side of specimens also confirmed that the interfacial strength between carbon fiber and matrix is the key for the mechanical performance of CF/TP-EP Compo. in bending.