Wang, J.P., Zhang, Y.M. and Li, H.Q. (2000) Experimental Study of Projection Algorithm in Ion Size Measurement. Journal of Tianjin University, 33, 460-463.

has been cited by the following article:

  • TITLE: The Microwave Synthesis and Photocatalytic Activity of W6+-Doped TiO2 Nanocomposite

    AUTHORS: Yulin Tang, Shuibin Yang, Quanxin Zhu, Xuehong Liao

    KEYWORDS: W6+-Doping, Titanium Dioxide, Microwave Synthesis, Photocatalysis, Methyl Orange

    JOURNAL NAME: Modern Research in Catalysis, Vol.5 No.2, April 12, 2016

    ABSTRACT: W6+-doped TiO2 was prepared by sodium tungsten (VI) and titanium sulfate with sodium dodecyl sulfate as surfactant under microwave irradiation. The samples were characterized by X-ray diffraction (XRD) and Scanning electron micrograph (SEM). The results showed that the as-prepared nanocomposite of inventory molar ratio of 2% calcined at 500°C for 2 h was anatase. The SEM showed that the majority of the catalyst was a relatively flake structure, and some fine particles attached to it. We also studied the photocatalytic activity of the as-prepared samples by using degradation of methyl orange. The factors including inventory molar ratio and concentration of W6+-doped, calcined temperature, amount of hydrogen peroxide and acidity of solution were investigated. When the catalyst was 1.0 g/L, pH was 2, C(H2O2) was 3 mL/L, the degradation rate of TiO2 for methyl orange of 20 mg/L reached 79.63% in 40 min.