Q. A. Yuan, S. Liao, Z. F. Tong, J. Wu and Z. Y. Huang, “Synthesis of Nanoparticle Zinc Phosphate Dihydrate by Solid State Reaction at Room Temperature and Its Thermochemical Study,” Materials Letters, Vol. 60, No. 17- 18, 2006, pp. 2110-2114.

has been cited by the following article:

• TITLE: One-Step Preparation and Characterization of Zinc Phosphate Nanocrystals with Modified Surface

  AUTHORS: Jian Dong Wang, Da Li, Jin Ku Liu, Xiao Hong Yang, Jia Luo He, Yi Lu

  KEYWORDS: Synthesis, Ultrasonic, Microwave, Zinc Phosphate, Nanocrystals, Anti-Corrosion

  JOURNAL NAME: Soft Nanoscience Letters, Vol.1 No.3, July 20, 2011

  ABSTRACT: The surface-modified zinc phosphate (Zn3(PO4)2) nanocrystals were synthesized by a facile and efficient one-step ultrasonic-template-microwave (UTM) assisted route. The crystal structure, optical properties and morphologies of zinc phosphate nanocrystals were characterized by X-ray diffraction, Fourier transform infrared spectroscopy, Raman spectroscopy and transmission electron microscope. And the TEM image showed that the product had good dispersion with a particle size of 30 – 35 nm. The anti-corrosion function of anti-corrosive paint using zinc phosphate nanocrystals was researched and the experiment result showed that the salt atmosphere–resistant time was 158 h longer than that of zinc phosphate bulk materials on market. The performance of zinc phosphate nanocrystals with modified surface synthesized by one-step UTM assisted route was improved 63.2% compared with the bulk materials.