Jiang, H.T., Tian, S.G., Fu, Y.L., Jia, M.H. and Zhang, Y.B. (2014) Application of Wet Electrostatic Precipitator in Coal-Fired Power Plants. Power Equipment, 28, 61-64.

has been cited by the following article:

  • TITLE: Wetting Characterization of Hybrid Coatings Deposited on Carbon Steel Collectors for Hydrophilic Modification

    AUTHORS: Chunyan Xu, Jingcai Chang, Jiaqiu Song, Xiang Wang, Bo Zhang, Lin Cui, Chunyuan Ma

    KEYWORDS: WESPs, Corrosion, Water Film, Wetting Characteristic, Flushing Liquid Distribution

    JOURNAL NAME: Journal of Environmental Protection, Vol.6 No.12, December 15, 2015

    ABSTRACT: The additional anticorrosive coating and hydrophilic layer of glass fiber cloth (GFC) deposited on the carbon steel sheet (CSS) was experimented and the surface wetting characteristic of the hydrophilic modified collection electrode was investigated under single strand feed water condition. The distilled water was selected as the working fluid. The influence of Reynolds number on the surface wetting characteristic parameters and those parameters at different temperatures were specifically studied. The results indicate that the GFC surface with loose glass fiber bundles reveals remarkable surface wetting characterizations. The saturated liquid holdup of this surface is 8 - 10 times more than that of the CSS surface; the surface flowrate value is 6 - 8 percent of that of the CSS surface; the film rate of this surface is 28 - 32 times more than that of the CSS surface; the average film thickness is between a third and a half of the value of the CSS surface. Good agreement is achieved between the WESPs working temperature and the experimental temperature range with remarkable wetting characterizations that provides a theoretical basis for the industrial application. Not satisfactorily, the hydrophilic modification surface is not able to survive high temperature.