Carbon Fibre Reinforced Concrete : Dependency of Bond Strength on Tg of Yarn Impregnating Polymer

In this paper, a method for the evaluation of the influence of different polymer suspensions and environmental conditions on adhesion between an impregnated carbon fibre heavy tow and concrete for reinforcement will be proposed. For this purpose, the impregnation material itself was investigated as a polymer film before and after incubation in water and aqueous suspensions, such as NaOH and a cementitious solution, in terms of its thermal properties, swelling behaviour and morphology. Thin polymer films were manufactured and subsequently investigated with quantification of the swelling for 28 d by thermal and scanning electron microscope analysis. The effect of pull-out shear stress was evaluated to investigate parameters such as high temperature and moisture on adhesion to concrete. Contact angle measurements were used to determine the surface energy of the polymer films. All incubated polymer films yielded a change in both surface morphology and specific residues on the polymer film surface, e.g. in the form of calcium carbonate, but no change in glass-transition temperature. A high correlation between glass-transition temperature and measured shear stress was shown during single yarn pull-out tests. Furthermore, the water treatment of pull-out samples strengthened the influence for the glass-transition temperature during the adhesion test. No influence of the surface energy of the used polymer impregnation for carbon fibres on the pull-out test was detected.


Introduction
Textile reinforcements for concrete structures have been more and more accepted in the building industry since they offer several advantages over conventional steel reinforcement [1] [2].A composite made of concrete and textile is typically named Textile Reinforced Concrete (TRC).This textile reinforcement consists of high-performance fibres such as alkali-resistant glass, aramid, or carbon fibres (CF).CF are not corrosive in an alkaline environment, have a high tensile strength and modulus of elasticity in the longitudinal direction of the fibre, thus they are largely suitable for use as structural reinforcement in concrete elements or for the strengthening of concrete structures [3] [4] [5].Due to their superior mechanical and chemical properties, CF increasingly replace alkali-resistant glass fibres, which have been used in concrete for decades.Depending on the geometry of concrete elements and the loading of carbon reinforcement, CF can be shaped to rebars, biaxial grids, or multi-axial warp knitted fabrics [6].
TRC is a multi-level composite.Concrete matrix is a composite-consisting of mineral aggregates, cement particles, hydrated cement phases, water and pores Moreover, textile reinforcement can be seen as a composite as well.At the single fibre level, each carbon filament (having a diameter of 6 µm to 7 µm) is covered by a sizing, which enables the processing of carbon fibre and defines its surface characteristics [7] [8].At the yarn level, a bundle of a thousand single filaments is impregnated by a polymer in order to ensure load transfer from the outer filaments (which are in contact to the concrete matrix) to the majority of inner filaments of the yarn.Impregnation is inevitable since even the smallest particles in fresh concrete suspension are too large to penetrate the yarn effectively and assure sufficient inner bonding between all filaments.Consequently, TRC can be described as a multi-component system-characterised by carbon fibres, sizing, impregnation (also often called coating) and concrete.With respect to the components, different interfaces have to be taken into account.Firstly, the interface between carbon filament and sizing is an immutable factor, dependent on the supplier and manufacturing process.Secondly, the interface between sizing and coating defines the load transmission inside the filament bundle, which the textiles are made of.Thirdly, the interface between coating and inorganic cementitious matrix is responsible for the force transfer between yarn and matrix, and additionally, for the mechanical properties of the entire composite.
Due to their application in buildings, bridges and other structures and specific properties of the cementitious matrix, the CF reinforcement faces numerous challenges including heat and cold, moisture, salt, as well as a high-alkaline environment and crystallization of minerals due to cement hydration.These challenges test various properties of CF reinforcement.With regard to the bulk material, the main determining performance factors are surface functional groups, aging behaviour, thermal stability, creep behaviour, as well as strength and stiffness of carbon yarns.In terms of the textile, further factors to consider include and degree/thickness of yarn coating due to the impregnation process.Furthermore, the following mechanisms have to be taken into account with respect to bond behaviour: chemical adhesion by covalent bonds, physical adhesion by polar forces, frictional resistance of surface against slip and surface roughness as mechanical interlock [3] [9].By means of coating, the chemical inertness of carbon must be overcome so that a favourable adhesion to the cementitious matrix can be established.As the polymer coating is applied to the entire yarn, it tends to fill all spaces in between the filaments.Therefore, inside the yarn the polymer acts as an impregnation, which assures the load transmission from outer to inner filaments and guarantees a quasi-uniform stress and strain distribution over the yarn cross-section.It was shown in previous studies that coatings especially designed for alkali-resistant glass (AR-glass) improved the adhesion as well as the strength of these fibres in concrete [10] [11].Besides the requirements of chemically adjusting to the sized fibre surface and of hydrating the cement-based matrix, mechanical performance, durability in an alkaline and moist environment as well as the coating temperature resistance are very important.To describe the temperature behaviour of a polymer coating, the glass-transition temperature (T g ) is an essential parameter in the context of elastic modulus and origins of the molecular structure of the polymer.For a good heat resistance and high elastic modulus, a high degree of crystallinity and high cross-linking density is needed, which can be indicated by a high T g of polymers [12] [13].As is known for fibre reinforced plastic rebars, the mechanical performance of polymers decrease if the temperature approaches T g .Therefore, the load transfer into the cementitious matrix is no longer guaranteed [14].In previous works, different types of polymers were used as matrix material for fibre rebars or for the impregnation of textile structures-both for use as reinforcement in concrete-(e.g.vinylesters, epoxy resins, polyurethanes, polyesters, poly-(styrol-butadiene)) and as polysiloxane coatings [10] [15] [16] [17].The T g of thermoset resins range between 65˚C and 120˚C.Since poly-(styrol-butadiene), polyacrylates and polyurethanes are generated by an impregnation technique based on aqueous suspensions, their expected T g is only roughly between −50˚C and 40˚C.A promising approach to increase the heat resistance of CF reinforcement for concrete is the impregnation by mineral particle suspensions, which was recently suggested by Schneider et al. and Nadiv et al. [18] [19].
Coated yarns were tested using uniaxial tension tests, by which the influence of different coatings on coherence between filaments could be assessed [20].
High-performance filaments and their interaction with different sizings were evaluated in a single-fibre tensile test [10].However, existing testing techniques do not provide a full picture for the behaviour of the multi-component system TRC and its components under thermal and alkaline exposure as mentioned before.Initial approaches investigated the durability of sized filaments or impregnated yarns in an alkaline environment by immersion in alkaline solutions (e.g. Materials Sciences and Applications 1 M NaOH, pH = 14).After exposure to elevated temperature for various time periods, the samples were extracted and tested with regard to their mechanical performance.Surface characterisation via scanning electron microscopy (SEM) helps to explain the observed mechanical behaviour.As another approach, commercially used glass fibre fabrics were tested after 28 d according to the standard of European Organisation for Technical Approvals [21].Such an aqueous alkaline solution is composed of NaOH, KOH and Ca(OH) 2 to simulate the conditions in concrete during processing, curing and service life [21].The bond performance between yarn and concrete and its durability can be assessed by pull-out tests.Butler et al. [22] proposed a double-sided pull-out test, whereby single yarns were embedded in concrete matrix.The samples were stored at 40˚C in a fog chamber for time periods ranging from 28 d to 360 d.The measured pull-out curve was assessed in close consideration of the findings with respect to interphase morphology, which was visualised via SEM.Lorenz et al. [23] executed pull-out tests and tension tests on textile reinforced concrete specimens.In the pull-out tests, a short yarn segment inside the textile structure was isolated and pulled out from the surrounding concrete matrix.The test was also performed at elevated temperatures of up to 500˚C.By means of tension tests on TRC plates, the complete stress-strain curve of the composite was assessed.It is the standard test method for the characterisation of the basic mechanical properties of cement-based textile-reinforced composites.
No systematic work has been published as yet on extracting and evaluating the impact of each single component of multi-component system TRC.The article at hand presents an investigation on the stability of different coatings based on aqueous suspension.For this purpose, polymer films were prepared and characterised with special respect to their swelling in various alkaline and aqueous solutions for 28 d.Additionally, thermal analysis and single-fibre pull-out tests after storage in various aqueous solutions and at different temperatures was performed to characterise the chemical and mechanical interactions of composite components under varying environmental conditions.

Carbon Fibres
The commercially available carbon fibre Sigrafil  C T50-4.0/240-E100 was purchased from SGL Carbon GmbH (Germany).It has an epoxy sizing, a fineness of 3300 tex, 50 K and a single filament diameter of 7 µm.

Concrete
The composition of the concrete used for evaluating bond performance between impregnated carbon yarn and concrete is given in Table 1.The binder "Dyckerhoff NANODUR  compound 5941" is commercially available [27] and composed of Portland cement clinker, ground granulated blast-furnace slag and quartz powder.The aggregates were added in two portions as natural quartz sand 0/2 mm and crushed granite 2/5 mm.The workability of fresh concrete was adjusted by adding a superplasticizer to a spread of 260 mm (small cone flow table without strokes, EN 1015-3).Therefore, the concrete was suitable for casting processes.The concrete exhibited fast hardening, high compressive strength (95 MPa after 7 days, 100 MPa after 28 days), enhanced durability and moderate shrinkage (0.57 mm/m).The hardening of concrete occurred under defined climate conditions (1 day in formwork, after storage in air at 20˚C and 65% RH).

Thermal Analysis
The Tg was determined by differential scanning calorimetry (DSC) Q2000 from TA Instruments (New Castle, USA) under a nitrogen atmosphere with a heating rate of 5 K/min.The polymers were investigated as polymer films.Next to this reference, samples stored in tap water, aqueous NaOH solution as well as in alkaline solution were investigated.

Determination of Surface Energy
All investigated polymer suspensions were dried at 40˚C for 24 h followed by conditioning and curing at either 120˚C for 19 min or 150˚C for 5 min in a PTFE mold on a microscope slide.The contact angles were determined by a Drop Shape Analyzer DSA 100 (Krüss GmbH, Germany).The testing solvent were distilled water (72.8 mN/m), diiodomethane CH 2 I 2 (>99%, Sigma-Aldrich Chemie GmbH, Germany, 50.8 mN/m), ethylene glycol/C 2 H 6 O 2 (Sigma-Aldrich Chemie GmbH, USA, 47.7 mN/m) and glycerine/C 3 H 8 O 3 (>98% water-free, 63.4 mN/m).At least ten individual drops were measured for each sample and solvent.( ) where, superscript p and d represent polar and disperse portions of the surface energies γ, while l and s represent the liquid and solid phases, i.e. testing solvent and polymer film surface.At least two different testing fluids should be used, which differ significantly in their polar and disperse properties.500 SE (Elkem AS in Oslo/Norway) [32].The suspension was stored for at least 30 h without air contact and occasionally stirred.Finally, the suspension was filtered and used for durability tests [33].The prepared cementitious solution exhibited a pH of 12.5.The cementitious solution shall represent the concrete pore liquid which is abbreviated from hereon as CemS.

Storage
To investigate long-term behaviour, disk-shaped polymer films with a diameter

Microscopic Study
All polymer films were investigated by scanning electron microscopy before and after their incubation in aqueous solution.The samples were set on a specimen holder with a carbon pad.For the investigation of the interface between the coated fibre and inorganic matrix, the tested specimens were split along the fibre direction.No further surface functionalisation for conductibility was done.A Quanta 250 FEG ESEM TM from FEI was used at 14.00 kV and 200 Pa.

Yarn Preparation
The solid' content of the polymer dispersions was set to 30% by the addition of water.The CF yarns were impregnated by a padder bath with subsequent heating in an industrial oven including three different heating zones Δθ 1 ~120˚C, Δθ 2 ~130˚C and Δθ 2 ~175˚C with a length of 3 m each.The process is illustrated in Figure 1.The process parameters of the padder bath were 1 bar contact pressure at a velocity of 2 m/min.After drying, the final coating material content of the impregnated CF was approximately 15% by mass.

Evaluation of the Bond between Yarn and Concrete 2.7.1. Setup
The bond performance of impregnated carbon yarns to the concrete matrix was characterized by means of a single-side yarn pull-out test, illustrated in Figure 2.
The test geometry to determine the bond performance is a concrete block (dimensions: width 80 mm, depth 80 mm, height 50 mm) with a centrally positioned carbon yarn and exposed bond length of 50 mm.As an opposite bearing to the yarn, a second concrete block with a height of 90 mm was used.
During pull-out tests an increasing relative displacement s (slip) between embedded yarn and concrete along the yarns axis was measured with a relative displacement rate of 1 mm/min.The slip was recorded by two laser distance sensors positioned close to a point adjacent to the upper specimen holder, where the yarn enters the concrete block.The laser beams scanned the surface of a small aluminium clip fixed to the yarn by a small spring, which was scanned on both sides of the yarn in order to consider rotations during pull-out tests.As a result of the imposed displacement, pull-out force F is introduced into the test geometry and is counteracted at the protruding end of the carbon yarn.In order to avoid sample damage as a consequence of handling prior to testing, the lower and upper blocks were rigidly linked by a removable stainless steel frame.The frame was attached to the specimen during concrete casting and unscrewed and removed only immediately before pull-out tests.The pull-out samples were tested at different content and temperature moisture states (see Table 2).Since the upper concrete block featured a relatively high mass and compact geometry and thus a high thermal capacity as well as the overall duration of the pull-out test procedure being less than 5 min, the pre-conditioned samples were tested at standard lab conditions.

Sample Production and Curing
The pull-out specimens were produced by casting.Before casting fresh concrete into the moulds for the upper and lower concrete block, the impregnated carbon yarn was placed centrically and stretched in the form work.For this purpose, the yarn was threaded through openings in the front sides of both moulds and fixed by rubber fittings.After complete filling of the form works, the removable stainless steel frame, in particular its fixing to the concrete, was embedded into the blocks surface.
After casting, the concrete surface was sealed under a plastic foil.The specimens were demoulded after one day and stored at various conditions for six Materials Sciences and Applications more days until testing (see Table 2).

Analysis of Results
During pull-out tests, vs. force displacement curves were recorded.In order to exclude the effect of differing yarn circumferences (and therefore, of varying the bonding surfaces) on results, the measured force and displacement were transformed to shear stress vs. slip curves.Since the majority of tested yarns featured flat, elliptical cross-sections (with varying radii of their semiaxis) the dimensions of yarns were determined at the upper and lower sides of the test block.Thus, a hypothetical circumference u of a corresponding ellipse was calculated.The diameter or the shape of the yarn cross-scetion has to be chosen carefully due to the resulting contact area for further calculations.The shear stress τ was obtained by division of the pull-out force F by the contact area yielding from the hypothetical circumference, times the embedment length l of the yarn (Equation ( 2)).
For each curve, five discretionary values were determined in order to characterise the pull-out behaviour of the different yarn coatings (see Figure 3): • Maximum shear stress: τ max • Shear stress at slip of 0.5 mm: τ 0.5 mm • Shear stress at slip of 1.0 mm: τ 1.0 mm • Specific pull out work at slip of 0.5 mm: W 0.5 • Bond modulus as secant to the curve between τ 0.2 = 0.2 τ max and τ 0.7 = 0.7 τ max

Statistics
All measurements were performed at least in triplicate, except for T g measrements, which were in duplicate.The values are provided as mean ± standard deviation.Two-way analysis of variance (ANOVA) with a Tukey correction

Polymer
The determined glass-transition temperature (T g ) for dried specimen was not affected by the applied conditions in different aqueous and alkaline solutions (Table 3).The determination of T g was performed at least by two heating cycles (HC).
All polymers differ in their polar and total surface energy, due to their chemical composition, while their disperse surface energies are quite comparable, being in the range of 23 mN/m to 35 mN/m (see Table 4).The highest polar surface energy was measured for SBR3, with 29 mN/m, followed by acrylate (Ac1) at 22.0 mN/m, and poly-urethane (PU) with 21.6 mN/m.These polymers also exhibited the highest total surface energy.For these coatings, the contact angles of water were <45˚.The least polar surface energy was observed for Ac2 and SBR1, which exhibited the highest water contact angles with more than 70˚.
Nevertheless, all polymers can be classified as hydrophobic.

Long-Term Stability
The long-term stability of the polymer was investigated by placing polymer film samples in three different aqueous solutions.The mass increased over the storage duration of 28 d for all conditions as in the case of static placement in water (Figure 4), NaOH (Figure 5), and cementitious solution (Figure 6).Surface topography was characterised by SEM-imaging, before and after incubation (Figure 7).All polymer films initially exhibited a smooth and clean surface, which is shown as an example for SBR3 in Figure 7(A).Generally, two different tendencies can be described: a pronounced increase in mass over the 28 days and a nearly constant mass level.This could be observed for all aqueous solutions.
For the exposure to water, swelling of the polymer film was determined by continuous increase in mass for SBR1.For the other polymers, the swelling level did not change significantly in comparison to the state attained during the first day of placement in water.This indicates an equilibrium between the elastic portions of the polymer network (restoring forces) and water (osmotic pressure), which diffuses into the rubber gaps of the investigated polymers [34] [35].After incubation and drying (day 29, dry), a decrease in mass compared to the initial weight was observed for all samples (see Table 5).This mass loss does not seem to be related to the previous swelling procedure.SBR2 exhibits the highest decrease in mass with 11.5%, compared to its initial mass, which was not expected when taking into account its inconspicuous swelling behaviour.on its surface (Figure 7(A)), but may exhibit some roughening after incubation (this is the case for SBR2, SBR3, PU, Ac1) and dehydration cracks (SBR1, SBR4).
Corresponding images are not shown.
For incubation in NaOH, the results are shown in Figure 5. Here, SBR4 as well as Ac2 exhibit a steady swelling over 28 days, while all other polymer films reach a constant mass increase of less than 20%.The increase in mass by 163% for SBR4 and 130% for Ac2 represents a combination of water absorption and precipitation of NaOH.Later ones (29 d) are identified by their increase in mass   [37].Interestingly, NaOH crystals also developed inside of dehydration cracks of the polymer film of SBR1, without causing a measurable increase in mass when measured after drying (Table 5).The other polymer films did not show any changes in surface morphology and had a smooth surface apart from some dehydration cracks.
Incubation in the cementitious solution yielded a considerable initial increase in mass by 5% to 20% in the wet state for all polymer films except SBR1 (Figure 6).Only for the acrylates, Ac1 and Ac2, there was a comparably small increase over 28 days.Also, SBR3 with 7.3% and PU with 12.0% exhibited the lowest final level of increase.These two polymer films got washed out, which resulted in a final decrease in mass after drying of −0.8% for SBR3, and −0.3% for PU.The other polymer films exhibited an increase in mass after incubation in the cementitious solution and subsequent drying of between 1.9% for SBR1 and 3.6% for Ac1 (Table 5).Additionally, incubation in the cementitious solution caused the most recognisable changes in surface morphology as visualised by SEM (Figures 7(B)-(H)).Different types of characteristic calcium silicate hydrate phases are visible: For the polymer films with the highest increase in mass over time (SBR1, Ac1, Ac2), a dense layer of crystals can be seen.Depending on the surface functionality and the swelling behaviour in the solution, the precipitated crystals differ in size and shape.The mineral on SBR1, which formed an almost closed surface layer, is presumably calcite (Figure 7(E)).The observed dumbbell-shaped crystals are comparable to those reported in the literature [38] [39].In comparison to the other polymer films, the degree of coverage is comparatively low.Caused by the swelling, the SBR1 polymer film exhibits a high number of dehydration cracks.The surface of PU films, incubated in the cementitious solution, is characterised by crystals of two different shapes.There are dumbbell-shaped crystals of different sizes built from needle-like crystals and spherulitic sponge-like crystals (Figure 7(H)).Compared to this, no dumbbell-shaped formations could be observed for Ac2.Instead, only needle-shaped and various elongated calcite crystals were found (Figure 7(C)).According to its low surface energy (Table 4), the low coverage by precipitates of the Ac2 polymer film led to the assumption of a low association of crystals to the surface.Only for SBR4 are there additional fine crystalline particles besides calcite (bottom crystals, needles, dumbbells), such as portlandite with its hexagonally shaped crystals [40], shown in Figure 7(D).
From the presented results, it can be concluded that swelling of the polymers causes an initial increase in mass between 5% and 25%.The swelling degree does Materials Sciences and Applications not show correlation to the polymers' contact angle to water and even high ionic strength liquids (NaOH, cementitious solution) do not significantly alter the swelling properties.In addition to swelling, the observed increase in mass is caused by mineral precipitates, which again do not relate to the polymer film surface chemistry nor to the surrounding liquids.Those mineral precipitates may influence the bonding interface between CF coating and concrete.

Evaluation of Yarn-Concrete Bond
Figure 8 describes the distinct dependence of the maximum shear stress τ max and the applied conditions for sample curing and testing (see Table 2).Depending on the temperature and the humidity of concrete curing, two trends are visible.
Firstly, with increasing temperature, the maximum shear stress decreases significantly.Secondly, with increasing humidity, the impact of temperature on maximum shear stress is markedly increased.A comparable trend was also observed for shear stress at a slip deformation of 1.0 mm τ 1.0 mm (data not shown).
The climate conditions during concrete curing and sample testing are a strengthening influence on bond behaviour of the chemistry of CF coating and its T g , since only few significant differences between the coatings have been identified.The influence of temperature will be discussed as a function of the present T g of the coatings under investigation.As presented in Table 3, the coatings SBR4 and Ac2 exhibit the highest T g of 32˚C and 39˚C, respectively.
The other coatings show lower T g values which let expect a lower mechanical resistance by these polymers, as they already passed out of the glassily condition.
For SBR4 and Ac2, the T g is not reached at room temperature, thus they do show the highest maximum pull out force at +20˚C and 65% relative humidity (Figure 8).Below the T g , the mechanical properties of a polymer can be seen as Figure 8. Shear strength τ max for various climatic conditions, such as 65% relative humidity (RH) and submersion in water; standard deviations are given.Materials Sciences and Applications constant.Therefore, for the coatings SBR4 and Ac2 with high T g (>20˚C), the τ max is on the same level for both +20˚C and −20˚C at 65% relative humidity.In comparison to this and caused by its relatively high T g of 33˚C, SBR4 continues to exhibit a good performance in the pull-out testing of wet samples at room temperature.However, τ max decreases by 78% in comparison to the specimens stored in the standard lab environment (+20˚C, 65\,\% RH).This could be explained by intense swelling of SBR4 in water caused by the destabilisation of the polymer network through water.The maximum shear stress of Ac2 decreased to 69% of the initial value as a result of the composite incubation in water.For this polymer as well, a high increase in mass of the film in NaOH was observed due to crystal formation on the polymer coating.For the room temperature with water storage and storage at 65% relative humidity, the lowest change of the maximum shear stress could be observed for SBR3 which exhibits the lowest increase in mass or swelling over 28 days in all incubation media (water, NaOH as well as cementitious solution).For various polymer systems, a relationship between the decrease in the glass transition temperature and the increase in humidity as well as swelling was found [41] [42].With respect to the mechanical performance of the coating polymers after incubation in water, a reduction of τmax was observed and obviously driven by the T g and affected by polymer swelling.
In contrast to the specimens stored at 65% RH, the maximum shear stress decreases pronouncedly as a result of incubation in hot water (95˚C with water incubation).These effects are clearly driven by the presence of water and its aggregate states.Therefore, for the water incubated samples, a freeze effect at −20˚C can be reasonably assumed due to the ice crystal formation of free water in the composite.The ice crystals were also formed in the interphase between concrete and impregnated yarn which intensified the bond between these components.Thus, a reinforcing effect is provided on the interfaces of multi-component systems, whereas the τ max was at least doubled, except for SBR4 with an increase of only 27%.For the associated pull-out work at −20˚C/wet, a significant effect of ice formation was recognised.It can be assumed that the ice crystal formation increases the rigidity and reduces the (fracture) toughness of yarn-concrete interphase.Thus, a more brittle/less viscous failure of bond mechanisms during pull-out occurs, accompanied by higher maximum shear stresses (see Figure 8).
For the determined bond modulus and therefore to describe the elastic properties of the composite, neither an influence of the T g of the polymers nor of the polar surface energy could be inferred.To further characterise the bond behaviour, the specific pull-out work at slip deformation of 0.5 mm W 0.5 between coated carbon yarn and concrete was calculated.At 95˚C, the values reached a minimum for both types of submersion, i.e. at 65% relative humidity and in water.It can be assumed that at this temperature, since T g is passed, a viscous slip deformation of polymer molecules occurs between carbon fibre and concrete.
The described, significant effect could be especially observed for all polymers (Ac1, SBR2, SBR3, and PU), whose T g was already exceeded at room tempera-Materials Sciences and Applications ture conditions.In this case, a decreased specific pull-out work was calculated at +20˚C/65% RH (data not shown).Thus, as Ac2 exhibits a high T g but a low polar surface energy (Table 4), it can be assumed that a high influence of the T g onto the specific pull-out work exists.This is consistent with the comparably high pull-out work of SBR4 at +20˚C/65% RH, which has the second highest T g .Here, a good impregnation by the coating as well as a good association of inorganic matrix onto the impregnated yarn could be observed.SBR4 serves as an example (Figure 9).
Furthermore, it has to be taken in account that a constant swelling of a polymer causes a reduction of water in the interface region between yarn coating and surrounding inorganic matrix material which is present during the hardening process of the concrete.Here, a lack of water is potentially weakening this interface by less hardened concrete, resulting in a decrease of the maximum shear stress, as shown for SBR1, SBR2 and SBR3.In this case, the glass-transition temperature is already passed and only the swelling effects have to be considered for the bond strength.

Conclusion
After incubation in water or water-based alkaline solutions, the glass-transition temperature of polymers under investigation does not change.Polymers which exhibit a contact angle for water < 45˚C show a high polar surface energy.After one week of incubation in aqueous solutions, most of the investigated systems reached an equilibrium state of mass increase.For some polymers, however, a further swelling in different solutions was observed, which concurs with residues or crystal growth verified via SEM images.A distinct relationship between the maximum shear stress measured in the yarn pull-out test and the glass-transition temperature and its swelling could be observed.The higher the glass-transition Figure 9. Scanning electron microscope image of a pull-out test specimen: pulled out SBR4 coated CF yarn with residues of inorganic matrix.
temperature, the higher the bond strength between the investigated polymer coated yarn and concrete matrix that gets reduced by high humidity.Another highly relevant parameter is the specific pull-out work, which together with the obtained complete force-slip curve, makes the single fibre pull-out test a key tool to examine the quality of polymer coatings of carbon yarns with respect to their bond to the concrete matrix in textile reinforced concrete.Based on the results of this study, the thermo-mechanical characteristics are more important than ever for the carbon fibre reinforced concrete.Therefore, pursuing studies will be done in the field of thermo-mechanical properties of coatings on yarns as well as in the field of high-temperature resistant coatings.
of 20 mm were incubated for 1 d, 3 d, 7 d, 14 d, 21 d, and 28 d in different aqueous solutions at room temperature (RT) without renewal of the medium and an initial liquid volume of 50 mL.A double determination of mass was performed and the mean value was calculated.Initial mass of the single disk-shaped polymer films was determined in the dry state and compared with the wet and swollen samples during and after storage.The samples were rinsed with distilled water and gently dried with a lint-free tissue before measuring their weight.After 28 d, all samples were dried overnight at 40˚C and weighed to determine their mass degradation.These values are indicated as 29 d, dry.

Figure 2 .
Figure 2. Schematic representation of the pull out test.

Figure 3 .
Figure 3. Scheme of stress-slip curve obtained from yarn pull-out tests.

Figure 4 .
Figure 4. Mass increase resulting from the incubation of polymers in water.

Figure 5 .
Figure 5. Mass increase resulting from the incubation of polymers in aqueous NaOH.

Figure 6 .
Figure 6.Mass increase resulting from the incubation of polymers in cementitious aqueous solution.
[28]ticizer 10 Materials Sciences and ApplicationsCalculation of the total surface energy and the polar and disperse portions was then determined according to the method developed by Owens, Wendt, Rabel and Kaelble[28][29] [30]:

Table 2 .
Conditions for sample curing pull-out tests, day 7 measurements.

Table 3 .
T g of all polymers under investigation determined by DSC of polymer films by multiple heating cycles (HC).

Table 4 .
Contact angles (CA) and polar and disperse parts of surface energy γ of the polymer films made of Ac1, Ac2, PU, SBR1,

Table 5 .
Changes in polymer mass due to incubation for 28 d and drying at 29 d.Materials Sciences and Applications after drying (29 d, dry) compared to the original state, supplemented via SEM investigations (images are not shown in this article).For both polymer films, a complete covering with crystalline precipitates was observed.These NaOH crystallite stacks exhibited a length around 20 -25 µm and a width of approximately