Contribution to the Study of Hot Water Scaling Phenomenon in the South of Touristic Area in Agadir City ()
1. Introduction
The region of Souss Massa occupies an important place in the touristic industry of Morocco both by its natural and cultural riches as well as by its performance in the tourism sector. Agadir city remains the first destination of the Kingdom by a hotel capacity of 27,542 beds approximately. Touristic installations offer 16% of jobs in the region [1] . Agadir city has everything to meet its national and international visitors through offers and various products and adapted to the expectations of the customer. For this, it is imperative to make efforts to protect this sector at all levels: human resources, environment, etc.
Agadir city is served with water from groundwater sources. Wells and boreholes produce on average 250 l/s and superficial (stations for the treatment of Sidi Boushab 300 l/s and that of Tamri 700 l/s supplied respectively by the waters of the Dams Abdelmoumen and Moulay Abdellah. The hotel sector which has consumed 2265.103 m3 of water in 2014 [2] faces some problems relating to clogging of hot water pipelines due to the scaling phenomenon.
The present work has for object the identification and characterization of deposits of scale formed in hot water pipelines in the south of the touristic area of Agadir. The samples of scale have been carried out at different points. Well distributed according to the standardized methods. Several analytical techniques were used: elemental analysis CHNS-O, XRF, IR, DTA, TGA, XRD and SEM.
2. Materials and Methods
2.1. Site of the Study
Agadir city is located on the shore of the Atlantic Ocean near the foot of the western High Atlas Mountains. The collection of the Scale has been made at the level of different installations of hot water in the southern seaside touristic establishments of Agadir located at coordinates: (30.39, −9.59) (Figure 1). These samples are the same kind and have the same structure. We give below the results for a deposit collected in a hot water pipeline of a tourist unit.
2.2. Methods of Analysis
X-Ray Fluorescence (XRF) analyses are performed on a PAN Analytical Axios. The applied voltage is 60 kV with a current of 125 mA and Power 4.103 W.
Infrared spectroscopy (IR) analysis is carried out with Bruker FTIR-ATR vertex model 70, with a resolution of 4 cm−1 in 16 scans to collect the data in an interval ranging from 4.102 to 4.103 cm−1. The samples are placed directly on the ATR crystal (Diamond of reflection). The mode used is the “total reflectance attenuated” (ATR).
X-ray diffraction analysis was done using the appliance PAN Analytical using a diffractometer type X-Pert-Pro with an anode material of copper and a monochromator of Cu-Kα radiation (λ = 1.5406 Å). The applied voltage is 45 kV with a current of 40 mA at 25˚C. The sample morphologies are directly examined by scanning electron microscopy (SEM) using a FEG Zeiss Supra running at an accelerating voltage of 3 kV to limit load on the sample. The thermogravimetric analysis (TGA) and differential thermal analysis (DTA) were carried out on a thermal analyser (DTG-60), under air from 0˚C to 1100˚C to heating rate of 10˚C/min. The Elementary Analysis CHNS/O is carried out with 2000 Flash EA 1112, thermo Fisher Scientific. Software used: EAGER 300.
![]()
Figure 1. Agadir city location and water scale sampling sites in the city.
3. Results and Discussion
3.1. X-Ray Fluorescence Analysis
The qualitative analysis by X-ray fluorescence (XRF) was used to identify the chemical elements in the scale samples. Figure 2 shows the spectrums of major elements found in the hot water scale samples. According to the Figure 2(b), the calcium is the major element. It presents an intense peak at the wavelength 0.336 nm. It is followed by the Iron at 0.193 nm (Figure 2(a)), the Silicon at 0.713 nm (Figure 2(c)). Others elements such as Strontium, Sulfur, Chromium, Magnesium, Oxygen are also present with peaks of low intensities, and trace amount of other elements such as Nickel, Zinc, Phosphorus, Titanium, Manganese, Sodium, and Potassium.
XRF quantitative analysis results are presented in Table 1. They show that the scale consists mostly of calcium carbonate with a content which reached 92.98%. In addition, it was also observed that the loss on ignition for scale was found to be 44.33%. This high value of loss is caused mainly by decomposition of calcium carbonate with formation of calcium oxide (CaO) and carbon dioxide (CO2) according to the reaction [3] :
The calcium oxide (CaO) is the major oxide in scale samples. It represents 52.07 wt%. Other oxides are also detected with very low contents. The silica (SiO2) and magnesium
![]()
Figure 2. XRF spectrums of scale deposited in the hot water system.
oxide (MgO) present respectively a percentage of 1.10% and 0.94% in weight. Other oxides in state of traces have been detected like sulphuric oxide SO3 (0.32%), phosphorus pentoxide P2O5 (0.22%), sodium oxide Na2O (0.20%), iron oxide Fe2O3 (0.11%), aluminium oxide (Al2O3) (0.09%).
3.2. Elementary Analysis CHNS/O
The Elemental chemical Analysis CHNS/O has been conducted to determine the percentage of the mass of Carbon, Hydrogen, Nitrogen, Sulphur or Oxygen in the scale samples. Table 2 summarizes the analytical results obtained. It shows that the scale studied contains 49.68% of oxygen and 10.70% of carbon. These values correspond to mass proportions of oxygen (48%) and carbon (12%) in calcium carbonate molecules.
The hydrogen and sulphur elements are present with very low percentages which are respectively 0.35% and 0.17%. The nitrogen element has not been detected as seen at Table 2.
3.3. Infra-Red Analysis
The analysis by IR spectroscope has given the results presented in Figure 3. The spectrum has allowed to identify the absorption bands corresponding to the different vibration characteristics bonds in the scale sample. This spectrum shows characteristics bands of the
: bands at 700.36 cm−1, 713.30 cm−1, 854.68 cm−1, 1082.90 cm−1 and at 1479.01 cm−1 [4] [5] . In addition, the band near 1789 cm−1 pointed to the presence of carboxyl (COO−), which came from 
and the surface adsorption of ambient water [5] . The spectrum of the aragonite is characterized by a double peak at 700 and 713 cm−1 [6] . Compared to calcite, aragonite is less stable under ambient thermodynamic conditions. It has an orthorhombic crystal structure. Experimental parameters of structure found by Dickens and Bowen a = 4.9598 Å, b = 7.9641 Å, and c = 5.7379 Å [7] [8] .
3.4. Thermal Analysis
The thermal decomposition of sample is shown in Figure 4. DTA curve shows endothermic peaks in the region of 0 to 300˚C associated to the elimination of the surface
![]()
Table 1. Chemical composition of the scale samples in hot water system.
![]()
Table 2. Results of the elementary analysis CHNS-O of scale deposited.
![]()
Figure 3. Infrared spectrum of scale formed in hot water system.
![]()
Figure 4. Thermogravimetric and differential thermal analysis curves of scale hot water.
and lattice water. Whereas, the endothermic peak at 800˚C is attributed to the decomposition of calcium carbonate CaCO3 to CaO and CO2. TGA analysis curve show a total mass loss of 41%:8% loss of surface and lattice water between 0˚C to 300˚C and 33% at high temperature associated to the elimination of vapors such as CO2 generated by the decomposition of calcium carbonate. These observations are in agreement with the literature data (39% to 43% for a temperature between 500˚C and 700˚C and the 44% as theoretical value) [5] [9] .
3.5. X-Ray Diffraction Analysis
Figure 5 presents the XR diffractogram of studied scale. It also shows that the scale essentially consists of aragonite CaCO3 (JCPDS card No. 00-005-0453), with a presence of the Mg-calcite Mg0.06Ca0.94(CO3) (JCPDS card No.01-089-1306) which corresponds to the peak 2θ = 29.7033˚ [10] .
The peaks which include 2θ = 27.5˚, 33.5˚ and 45.9˚ correspond to the calcium carbonates of the aragonite type which is metastable to the ordinary temperature and which is formed at a temperature above 60˚C [11] [12] [13] [14] . With the exception of the peaks at 2θ = 29.7˚, 39.79˚ and 43.57˚, all the peaks in the spectrum correspond to the aragonite variety of calcium carbonate [15] [16] . According to Wray J.L and Danniel F., the pure crystals of aragonite are obtained at 70˚C, by precipitation of the soluble calcium salts and carbonate [17] . Indeed, the high temperature in the piping of the hot water favours the formation of aragonite [16] .
3.6. Scanning Electron Microscopy Analysis (SEM)
The scale samples analysis with the scanning electron microscopy (SEM) has given results as we can see at Figure 6. Micrographs obtained show that the scale structure is in the form of needles which confirms that it is composed of Calcium Carbonate CaCO3, type aragonite [14] [18] .
4. Conclusions
The use of various analytical techniques has allowed us to identify and characterize the solid deposits found in the internal walls of hot water pipes in the south of the touristic area of the Agadir city.
![]()
Figure 5. X-ray diffraction spectrum of hot water scale.
![]()
Figure 6. MEB micrographs of scale deposited in hot water system.
Quantitative analysis results showed that calcium carbonates amount exceeds 93 wt%. The carbonates anion has been well identified in the infra-red spectrum. The process of decomposition of calcium carbonates has been highlighted by the quantitative analysis by XRF. The calcium oxide CaO represents 52% of the scale weight. Thermal analysis results confirmed this result and showed the calcium carbonate decomposition process. The crystal structure of the scale is the aragonite variety as it has been determined by X-ray diffraction. Micrographs obtained by scanning electronic microscope confirm this structure.
Indeed, the scale deposited in the hot water system is mostly formed of calcium carbonate. Due to temperature, particles of calcium carbonate were crystallized under the aragonite variety. These results will allow us to focus our research of suitable inhibitors of scaling in order to prevent the deposit of scale in the hot water system in the touristic area in Agadir city.