Application of Hydrazine Hydrate in the Synthesis of Octa(aminophenyl)silsesquioxane (OAPS) Poss

Abstract

Octa(aminophenyl)silsesquioxane (OAPS) was prepared from octaphenyl silsesquioxane (OPS) in two steps, first nitration to obtain Octa(nitrophenyl)silsesquioxane (ONPS) then reduction by using the stable, inexpensive, and readily available hydrazine hydrate as the reducing agent in the presence of Iron(III)Chloride catalyst with a yield of around 87%. Hydrazine is a two-electron reducing agent whereas nitro group is a four-electron reduction process. The activated carbon serves as an adsorbent and electrical conductor enabling the reaction to occur by acting as a mediator between a two-electron reagent and a four-electron process. Adsorption provides a reducing potential and a supply of electrons from many hydrazines making possible the initial four-electron process even though each individual hydrazine is a two-electron donor. The product was characterized by FTIR and 1H NMR. The time period for preparation of ONPS from octaphenyl silsesquioxane was considerably shortened to avoid double nitration of the aromatic rings.

Share and Cite:

J. Koech, Q. Shao, F. Mutua and Y. Wang, "Application of Hydrazine Hydrate in the Synthesis of Octa(aminophenyl)silsesquioxane (OAPS) Poss," Advances in Chemical Engineering and Science, Vol. 3 No. 1, 2013, pp. 93-97. doi: 10.4236/aces.2013.31011.

1. Introduction

The growth of new materials with specially designed chemical, mechanical or physical properties is becoming increasingly important in many fields of practical application. In this respect, recent years have seen increased demand for organic-inorganic hybrid polymer materials in a wide range of applications [1]. These needs have been met with accelerated advances in polymer science and technology, taking benefit from nanophase technology geared towards enhancements to polymer materials. In order to accomplish the various practical requirements, a tailor-made material design is necessary, which includes direct control of both bulk and surface characteristics [2]. The nanostructures, degree of organization and properties that can be obtained from such materials certainly depend on the chemical nature of their components, but they also rely on the synergy between these components.

Polymer composites containing nanometer-size inorganic particles have received considerable attention from researchers in quest for materials with low density and much higher mechanical strength and stiffness compared to glass and carbon fiber filled counterparts [3]. A number of success stories give credence to the hypothesis that small quantities of, often less than 10 wt%, inorganic nanoparticles can contribute to significant increases in heat distortion temperature, stiffness, and toughness of the polymer [4]. This is often attributed to the predominant interfacial interactions between the nanoparticles and polymer chains, which is facilitated by very large interfacial area per unit volume [5]. To illustrate, single wall carbon nanotubes (SWNT) have surface area ~400 m2/g [5], fumed silica ~300 m2/g, and Polyhedral oligomeric silsesquioxane (POSS) ~406 m2/g [6]. In contrast to other nanofillers, such as layered silicates which are platy and carbon nanotubes which are cylindrical, the shape of the POSS molecules is isotropic. In addition, POSS molecules can be easily functionalized by chemically altering the R groups (Figure 1). This presents opportunities for copolymerization or grafting reactions with functional groups on polymer chains and for defining and controlling the nature of interactions between POSS molecules and the polymer chains. Some ramifications of such strong interactions are favorable rheological properties such as reduced shear viscosity, high glass transition, heat distortion temperatures, and improved mechanical properties of the nanocomposites.

Interest in Octa-aminophenyl polyhedral oligomeric silsesquioxane (OAPS) materials, shown in Figure 1, is based on the facts that the amino groups provide an excellent site for cross linking offering a unique opportunity for preparing truly molecularly dispersed nanocomposites [7,8]. POSS combine a hybrid inorganic-organic composition, Rn(SiO1.5)n, where R may be a range of organo-functional groups, while n is an even integer ≥4, with nano-sized cage structures having dimensions comparable to those of most polymeric segments or coils [9]. POSS chemical reagents are nanostructured with sizes of 1 - 3 nm and can be thought of as the smallest particles of silica possible. However, unlike silica or silicones, each POSS molecule may contain nonreactive organic substituent that makes the POSS nanostructure compatible with monomers or polymers.

POSS molecules have been easily incorporated into common polymers via copolymerization, grafting or blending [10]. Varieties of POSS-containing copolymers have been prepared using condensation, ring-opening metathesis and radical, both conventional, and atomtransfer, copolymerization techniques. Many varieties of substituent may be fixed onto the Si atoms at the corners of the cages to optimize polymer-POSS interactions and simultaneously to aid in the easy dissolution of the POSS moieties in common solvents for synthesis purposes. These groups may be incorporated into almost any conventional polymer and in a variety of different chain architectures. Thus, inorganic nature and multiple reactive functionalities of POSS make these compounds ideal for their use in the construction of organic–inorganic hybrid nanomaterials [11].

Nowadays, most large-scale aromatic amines are being produced by catalytic hydrogenation of the corresponding nitroarenes. With a large variety of catalysts (e.g. Ni, Cu, Co, Cr, Fe, Sn, Ag, Pt, Pd, Zn, Ti, Mo, metal oxides and sulphides) [12,13] and under a wide range of reaction conditions in most cases the corresponding amine is obtained quantitatively without the production of waste products [14,15]. Because of the exothermic nature of the reaction and the need for a closed high-pressure system, numerous safety precautions have to be taken.

Despite such optimistic outlook and well executed prior work, the cost of OAPS is exorbitantly high calling for ways of producing the same cheaply. One way of achieving this is by replacing the conventional method of synthesizing OAPS by use of Pd/C with hydrazine hydrate which is cheaply available.

This paper explores a novel synthesis of OAPS in two steps from octaphenyl POSS as shown in Figure 2. FirstOPS is subjected to nitration to obtain ONPS by use of fuming nitric acid. ONPS is then subjected to mild reduction using hydrazine hydrate to obtain OAPS.

2. Experimental Details

2.1. Materials

OPS was purchased from Laoning AM union composite materials Co. Ltd. Tetrahydrofuran and ethyl acetate were obtained through Donghua university chemical store, dried over molecular sieve prior to use. Other chemicals and reagents were also sourced through Donghua university chemical store and used as received.

2.2. Synthesis of Octanitrophenyl POSS

Octa(nitrophenyl)-POSS (ONP-POSS) was synthesized by adopting a procedure previously reported by Laine and coworkers with a number of modifications [16]. A 20 g of OP-POSS (19.4 mmol) was added in small portion to 135 mL fuming nitric acid while stirring at 0˚C. The resulting mixture was kept in an ice cold condition for an hour then at room temperature with constant agitation for 7h. The solution was then poured onto 150 g ice and a faintly yellow precipitate collected, washed with water (until pH~6.0) then with ethanol (200 mL × 2). The powder of ONP-POSS was obtained by filtration and dried under vacuum at 50˚C for 12 hrs. (yield 91%).

2.3. Synthesis of Octaaminophenyl POSS

Five grams of ONPS (3.86 mmol), 50 mg FeCl3, and 4 g active charcoal powder were charged into a three necked 250 mL round-bottomed flask equipped with a magnetic

Figure 1. Octa-aminophenyl POSS molecule.

Figure 2. Synthesis of OAPS.

stirrer and a condenser. THF (40 mL) was then added to the flask. The solution was stirred and heated to 60˚C under N2.

Hydrazine hydrate (16 mL) was added drop-wise into the mixture. The reaction was continued for 4h, and then the solution was cooled and filtered. The filtrate was combined with 25 mL of ethyl acetate and washed with water thrice. The organic layer was dried over Na2SO4 and poured into 1 L petroleum ether. The white precipitate was collected by filtration. The product was redissolved in the mixture of 15 mL THF and 25 mL ethyl acetate, and reprecipitated into 500 mL petroleum ether. The obtained powder was dried in vacuum at 50˚C. The yield of the off-white OAPS was 87%.

2.4. Measurement and Characterization

Fourier transform infrared (FTIR) spectra of the samples were recorded on a Nicolet 5700 FTIR (Thermo Fisher) in which KBr pellets were used for the powder samples of the synthesized monomer. 1H NMR spectra were recorded on a Bruker-400 spectrometer operating at 296.2 K with tetramethylsilane (TMS) as an internal reference. The spectra were referenced to the residual proton impurities in the CDCl3 at δ 7.27 ppm.

3. Discussion and Conclusions

The OAPS was prepared as depicted in Figure 2, and its structure was characterized. In the FTIR spectrum of ONPS (Figure 3(b)), the two strong peaks at 1350 and 1531 cm−1 are assigned to symmetric and asymmetric vN=O. These two peaks disappeared after reduction as shown in the FTIR spectrum of OAPS (Figure 3(c)), denoting that the reduction reaction was successful. New broad peaks appear at 3381 cm−1 with a shoulder at 3223 cm−1, which are assigned to vNH [17,18].

In the 1H NMR spectrum of OAPS (Figure 4(a)), no peak at 8 - 9 ppm corresponding to the protons in aromatic groups of ONPS was observed, while the aromatic hydrogen of OAPS were detected at higher magnetic field (7.8 - 6.0 ppm) due to the electron donor properties of amino groups on phenyl rings. This result indicated that the reduction reaction of nitro groups in ONPS by hydrazine hydrate was complete. The integration ratio of the peaks originating from protons in aromatic groups and amino groups of OAPS results indicated that one hydrogen atom per phenyl in OPS was substituted by nitro group forming ONPS, which was subsequently converted into amine group forming OAPS by reduction reaction. The Si-O-Si bonds in silsesquioxane cages of OAPS could be characterized by the stretching bands at 1119 cm−1 in FTIR spectrum (Figure 3) [17,19].

The reduction of aromatic nitro compounds with hydrazine or hydrazine hydrate, illustrated in Figure 5, represents a special variation of the catalytic reduction, where hydrazine is the source of the hydrogen. The hydrogen can be generated by a variety of H-transfer catalysis [13]. Especially with the use of noble metal catalysts, such as Pd, Pt or Ru, but also with the application of Ni, Cu or Fe, the catalytic hydrazine reduction gives high yields comparable to or better than the catalytic hydrogenation.

The following chemical reaction illustrates the mechanism by which hydrazine hydrate is broken down by catalytic iron to release hydrogen ions in the presence activated carbon.

In the past, the relatively high costs for hydrazine hydrate and for the noble metal catalysts prevented this reduction method from being applied at an industrial scale. However, there are two main reasons which are currently enhancing the preference of this catalytic Htransfer reduction: 1) It has been observed repeatedly that several cheap iron(III) compounds exhibit an appreciable activity with regard to catalytic H-transfer [20]; 2) In cases where the catalytic hydrogenation is not the method of choice, this method offers a safe as well as an ecologically and economically beneficial alternative, above all for small product volumes in chemical manufacture, where the reaction can be carried out in multiuse batches under normal pressure.

Conclusions

Hydrazine hydrate catalytic reduction under iron(III) chloride/activated carbon provides an efficient and relatively cheap method for the production of OAPS. Iron(III) chloride is directly involved in the reaction as active centre where as the activated carbon acts as the anchorage which helps in adsorption of hydrazine and transfer of electrons to nitro groups ensuring a smooth reaction progress, it basically acts as a stabilizer. Hydrazine is a convenient reductant because the by-products are typically

Figure 3. FTIR spectrum of (a) OPS, (b) ONPS and (c) OAPS.

Figure 4. HNMR spectrum of (a) OAPS, (b) ONPS and (c) OPS.

Figure 5. Catalytic reduction of ONPS to obtain OAPS.

nitrogen gas and water (Figure 5).

The direct reaction of hydrazine and nitroaromatics does not occur because of a mismatch in the electronic requirements, a two-electron reductant and a four electron oxidant. Activated carbon facilitates the reaction by providing a pool of electrons from adsorbed hydrazine. It serves as an adsorbent and electrical conductor. The rate determining step is oxidation of hydrazine at the carbon surface.

4. Acknowledgements

The authors gratefully acknowledge Zhang Yao for his tireless help in the execution of the experiments.

Conflicts of Interest

The authors declare no conflicts of interest.

References

[1] E. Markovic, K. Constantopolous and J. G. Matisons, “Polyhedral Oligomeric Silsesquioxanes: From Early and Strategic Development through to Materials Application,” Applications of Polyhedral Oligomeric Silsesquioxanes, 2011, pp. 1-46.
[2] S. Lucke and K. Stoppek-Langner, “Polyhedral Oligosil Sesquioxanes (POSS)—Building Blocks for the Development of Nano-Structured Materials,” Applied Surface Science, Vol. 144-145, 1999, pp. 713-715. doi:10.1016/S0169-4332(98)00912-X
[3] S.-W. Kuo and F.-C. Chang, “POSS Related Polymer Nanocomposites,” Progress in Polymer Science, Vol. 36, No. 12, 2011, pp. 1649-1696. doi:10.1016/j.progpolymsci.2011.05.002
[4] K. Pielichowski, et al., “Polyhedral Oligomeric Silsesquioxanes (POSS)-Containing Nanohybrid Polymers,” Supramolecular Polymers Polymeric Betains Oligomers, Vol. 201, 2006, pp. 225-296. doi:10.1007/12_077
[5] I. A. A. C. Esteves, et al., “Determination of the Surface Area and Porosity of Carbon Nanotube Bundles from a Langmuirian Analysis of Sub- and Supercritical Adsorption Data,” Carbon, Vol. 47, No. 4, 2009, pp. 948-956. doi:10.1016/j.carbon.2008.11.044
[6] R. A. Mantz, et al., “Thermolysis of Polyhedral Oligomeric Silsesquioxane (POSS) Macromers and POSS-Siloxane Copolymers,” Chemistry of Materials, Vol. 8, No. 6, 1996, pp. 1250-1259. doi:10.1021/cm950536x
[7] G. Z. Li, et al., “Viscoelastic and Mechanical Properties of Epoxy/Multifunctional Polyhedral Oligomeric Silsesquioxane Nanocomposites and Epoxy/Ladderlike Polyphenylsilsesquioxane Blends,” Macromolecules, Vol. 34, No. 25, 2001, pp. 8686-8693. doi:10.1021/ma011117q
[8] C. Ramirez, et al., “Selection of a Precursor of a Monofunctional Polyhedral Oligomeric Silsesquioxane Reacted with Aromatic Diamines,” Journal of Applied Polymer Science, Vol. 92, No. 3, 2004, pp. 1576-1583. doi:10.1002/app.20101
[9] W. A. Reinerth, et al., “POSS (TM)/Polymer Blends for Gas Separation,” Abstracts of Papers of the American Chemical Society, Vol. 222, 2001, p. U429.
[10] E. G. Shockey, et al., “Functionalized Polyhedral Oligo-silsesquioxane (POSS) Macromers: New Graftable POSS Hydride, POSS Alpha-Olefin, POSS Epoxy, and POSS Chlorosilane Macromers and POSS-Siloxane Triblocks,” Applied Organometallic Chemistry, Vol. 13, No. 4, 1999, pp. 311-327. doi:10.1002/(SICI)1099-0739(199904)13:4<311::AID-AOC847>3.0.CO;2-1
[11] D. Neumann, et al., “Synthesis and Characterization of an Isocyanate Functionalized Polyhedral Oligosilsesquioxane and the Subsequent Formation of an Organic—Inorganic Hybrid Polyurethane,” Journal of the American Chemical Society, Vol. 124, No. 47, 2002, pp. 13998-13999. doi:10.1021/ja0275921
[12] M. Lauwiner, R. Roth and P. Rys, “Reduction of Aromatic Nitro Compounds with Hydrazine Hydrate in the Presence of an Iron Oxide/Hydroxide Catalyst. III. The Selective Reduction of Nitro Groups in Aromatic Azo Compounds,” Applied Catalysis A: General, Vol. 177, No. 1, 1999, pp. 9-14. doi:10.1016/S0926-860X(98)00247-6
[13] M. Lauwiner, P. Rys and J. Wissmann, “Reduction of Aromatic Nitro Compounds with Hydrazine Hydrate in the Presence of an Iron Oxide Hydroxide Catalyst. I. The Reduction of Monosubstituted Nitrobenzenes with Hydrazine Hydrate in the Presence of ferrihydrite,” Applied Catalysis A: General, Vol. 172, No. 1, 1998, pp. 141-148. doi:10.1016/S0926-860X(98)00110-0
[14] M. Benz and R. Prins, “Kinetics of the Reduction of Aromatic Nitro Compounds with Hydrazine Hydrate in the Presence of an Iron Oxide Hydroxide Catalyst,” Applied Catalysis A: General, Vol. 183, No. 2, 1999, pp. 325-333. doi:10.1016/S0926-860X(99)00069-1
[15] M. Benz, A. M. van der Kraan and R. Prins, “Reduction of Aromatic Nitrocompounds with Hydrazine Hydrate in the Presence of an Iron Oxide Hydroxide Catalyst: II. Activity, X-Ray Diffraction and M?ssbauer Study of the Iron Oxide Hydroxide Catalyst,” Applied Catalysis A: General, Vol. 172, No. 1, 1998, pp. 149-157. doi:10.1016/S0926-860X(98)00111-2
[16] S. G. Kim, et al., “Synthesis of Amino-Containing Oligophenylsilsesquioxanes,” Polymer, Vol. 46, No. 12, 2005, pp. 4514-4524. doi:10.1016/j.polymer.2005.02.036
[17] Y. Ni and S. Zheng, “A Novel Photocrosslinkable Polyhedral Oligomeric Silsesquioxane and Its Nanocomposites with Poly (Vinyl Cinnamate),” Chemistry of Materials, Vol. 16, No. 24, 2004, pp. 5141-5148. doi:10.1021/cm049463k
[18] R. Tamaki, et al., “Octa (Aminophenyl) Silsesquioxane as a Nanoconstruction Site,” Journal of the American Chemical Society, Vol. 123, No. 49, 2001, pp. 12416-12417. doi:10.1021/ja011781m
[19] R. Tamaki, J. Choi and R. M. Laine, “A Polyimide Nano-composite from Octa (Aminophenyl) Silsesquioxane,” Chemistry of Materials, Vol. 15, No. 3, 2003, pp. 793-797. doi:10.1021/cm020797o
[20] U. Schwertmann and R. M. Cornell, “Iron Oxides in the Laboratory: Preparation and Characterization,” 2nd Edition, Wiley-VCH, Weinheim, 2000.

Copyright © 2024 by authors and Scientific Research Publishing Inc.

Creative Commons License

This work and the related PDF file are licensed under a Creative Commons Attribution 4.0 International License.