EXAFS Studies of Ruthenium Based Double Perovskite ALaMnRuO6 (A = Ca, Sr, Ba)
Rubina Shaheen, Javaid Bashir, Muhammad Nasir Khan
DOI: 10.4236/msa.2012.31004   PDF    HTML     5,058 Downloads   8,671 Views   Citations


Room and liquid nitrogen temperatures Mn K-edge extended X-ray fine structure (EXAFS) studies were carried out on powder samples of ALaMnRuO6 (A = Ca, Sr, Ba) perovskites. The EXAFS analysis of Mn K-edge spectra showed MnO6 octahedra are distorted. Among the three perovskites, the polyhedral distortion is highest for SrLaMnRuO6 (Δ = 1.4 × 10–3). For CaLaMnRuO6 (Δ = 0.5 × 10–3) and BaLaMnRuO6, (Δ = 0.7 × 10–3), the smaller values of distortion parameters indicate that the MnO6 octahedra are relatively regular and undistorted in the latter two systems. In SrLaMnRuO6, MnO6 distortion appears to be of orthorhombic (Q2) type whereas for CaLaMnRuO6 and BaLaMnRuO6, the distortion is of tetragonal or Q3 type. The Mn-O distances as determined from the EXAFS measurements, increases with the increase in the size of the divalent cation. No structural changes occurred in the local environment around Mn atom when the temperature was lowered from room to liquid nitrogen temperature.

Share and Cite:

R. Shaheen, J. Bashir and M. Khan, "EXAFS Studies of Ruthenium Based Double Perovskite ALaMnRuO6 (A = Ca, Sr, Ba)," Materials Sciences and Applications, Vol. 3 No. 1, 2012, pp. 24-29. doi: 10.4236/msa.2012.31004.

Conflicts of Interest

The authors declare no conflicts of interest.


[1] R. H. Mitchell, “Perovskites: Modern and Ancient,” Almaz Press, Thunder Bay, Canada, 2002.
[2] B. Raveau, “The Perovskite History: More than 60 Years of Research from the Discovery of Ferroelectricity to Colossal Magnetoresistance via High Tc Superconductivity,” Progress in Solid State Chemistry, Vol. 35, No. 2-4, 2007, pp. 171-173. doi:10.1016/j.progsolidstchem.2007.04.001
[3] K. Kuepper, M. C. Falub, K. C. Prince, V. R. Galakhov, I. O. Troyanchuk, S. G. Chiuzbaian, M. Matteucci, D. Wett, R. Szargan, N. A. Ovechkina, Y. M. Mukovskii and M. Neumann, “Electronic Structure of A- and B-Site Doped Lanthanum Manganites: A Combined X-Ray Spectroscopic Study,” The Journal of Physical Chemistry B, Vol. 109, No. 19, 2005, pp. 9354-9361. doi:10.1021/jp044447w
[4] A. J. Millis, “Lattice Effects in magnetoresistive Manganese perovskites,” Nature, Vol. 392, No. 6672, 1998, pp. 147-150. doi:10.1038/33017
[5] P. M. Woodward, T. Vogt, D. E. Cox, A. Arulraj, C. N. R. Rao, P. Karen and A. K. Cheetham, “Influence of Cation Size on the Structural Features of Ln1/2A1/2MnO3 Perovskites at Room Temperature,” Chemistry of Materials, Vol. 10, No. 11, 1998, pp. 3652-3665. doi:10.1021/cm980397u
[6] J. Guan, S. E. Dorris, U. Balachandran and M. Liu, “The Effects of Dopants and A: B Site Nonstoichiometry on Properties of Perovskite-Type Proton Conductors,” Journal of the Electrochemical Society, Vol. 145, No. 5, 1998, pp. 1780-1786. doi:10.1149/1.1838557
[7] M. T. Anderson, K. B. Greenwood, G. A. Taylor and K. R. Poeppelmeier, “B-Cation Arrangements in Double Perovskites,” Progress in Solid State Chemistry, Vol. 22, No. 3, 1993, pp. 197-233. doi:10.1016/0079-6786(93)90004-B
[8] D. M. A. Melo, F. M. M. Borges, R. C. Ambrosio, P. M. Pimentel, C. N. da Silva Jr. and M. A. F. Melo, “XAFS Characterization of La1?xSrxMnO3?δ Catalysts Prepared by Pechini’s Method,” Chemical Physics, Vol. 322, No. 3, 2006, pp. 477-484. doi:10.1016/j.chemphys.2005.09.008
[9] A. J. Millis, B. I. Shraiman, R. Mueller, “Dynamic JahnTeller Effect and Colossal Magnetoresistance in La1?xSrxMnO3,” Physical Review Letters, Vol. 77, No. 1, 1996, pp. 175-178. doi:10.1103/PhysRevLett.77.175
[10] V. Krishnan, G. Bottaro, S. Gross, L. Armelao, E. Tondello and H. Bertagnolli, “Structural Evolution and Effects of Calcium Doping on Nanophasic LaCoO3 Powders Prepared by Non-Alkoxidic Sol-Gel Technique,” Journal of Materials Chemistry, Vol. 15, No. 20, 2005, pp. 2020-2027. doi:10.1039/b502470f
[11] E. Quarez, F. Abraham and O. Mentré, “Synthesis, Crystal Structure and Characterization of New 12H Hexagonal Perovskite-Related Oxides Ba6M2Na2X2O17 (M=Ru, Nb, Ta, Sb; X=V, Cr, Mn, P, As)” Journal of Solid State Chemistry, Vol. 176, No. 1, 2003, pp. 137-150. doi:10.1016/S0022-4596(03)00379-7
[12] R. O. Bune, M. V. Lobanov, G. Popov, M. Greenblatt, C. E. Botez, P. W. Stephens, M. Croft, J. Hadermann and G. V. Tendeloo, “Crystal Structure and Properties of Ru-Stoichiometric LaSrMnRuO6,”Chemistry of Materials, Vol. 18, No. 10, 2006, pp. 2611-2617. doi:10.1021/cm052371q
[13] J.-W. G. Bos and J. P. Attfield, “Structural, Magnetic, and Transport Properties of (La1+xSr1-x)CoRuO6 Double Perovskites,” Chemistry of Materials, Vol. 16, No. 9, 2004, 1822-1827. doi:10.1021/cm0497733
[14] A. Callaghan, C. W. Moeller and R. Ward, “Magnetic Interactions in Ternary Ruthenium Oxides,” Inorganic Chemistry, Vol. 5, No. 9, 1966, pp. 1572-1576. doi:10.1021/ic50043a023
[15] Y. Maeno, H. Hashimoto, K. Yoshida, S. Nishizaki, T. Fujita, J. G. Bednorz and F. Lichtenberg, “Superconductivity in a Layered Perovskite without Copper,” Nature, Vol. 372, No. 6506, 1994, pp. 532-534. doi:10.1038/372532a0
[16] M. P. Attfield, P. D. Battle, S. K. Bollen , S. H. Kim, A. Powell and M. Workman, “Structural and Electrical Studies of Mixed Copper/Ruthenium Oxides and Related Compounds of Zinc and Antimony,” Journal of Solid State Chemistry, Vol. 96, No. 2, 1992, pp. 344-359. doi:10.1016/S0022-4596(05)80268-3
[17] P. D. Battle, T. C. Gibbs, C. W. Jones and F. Studer, “Spin-Glass Behavior in Sr2FeRuO6 and BaLaNiRuO6: A Comparison with Antiferromagnetic BaLaZnRuO6,” Journal of Solid State Chemistry, Vol. 78, No. 2, 1989, pp. 281-293. doi:10.1016/0022-4596(89)90109-6
[18] P. D. Battle, C. W. Jones and F. Studer, “The Crystal and Magnetic Structures of Ca2NdRuO6, Ca2HoRuO6, and Sr2ErRuO6,” Journal of Solid State Chemistry, Vol. 90, No. 2, 1991, pp. 302-312. doi:10.1016/0022-4596(91)90147-A
[19] E. Granado, Q. Huang, J. W. Lynn, J. Gopalakrishnan and K. Ramesha, “Crystal Structures and Magnetic Order of La0.5+dA0.5-dMn0.5+eRu0.5-eO3 (A = Ca, Sr, Ba): Possible Orbital Glass Ferromagnetic State,” Physical Review B, Vol. 70, No. 21, 2004, pp. 214416.1-214416.7.
[20] R. I. Das, J.-Q. Yan and J. B. Goodenough, “Ruthenium Double Perovskites: Transport and Magnetic Properties,” Physical Review B, Vol. 69, No. 9, 2004, pp. 094416.1-094416.16.
[21] J. Bashir, R. Shaheen and M. N. Khan, “Structural Characterization of SrLaMnRuO6 by Synchrotron X-Ray Powder Diffraction and X-Ray Absorption Spectroscopy,” Solid State Sciences, Vol. 10, No. 5, 2008, pp. 638-644. doi:10.1016/j.solidstatesciences.2007.10.011
[22] K. Shahzad, R. Shaheen, M. Nasir Khan and J. Bashir, “Crystal Structure and Valence State of Mn in BaLa-MnRuO6,” Journal of Physics D: Applied Physics, Vol. 41, No. 17, 2008, p. 175413. doi:10.1088/0022-3727/41/17/175413
[23] M. N. Khan?, R. Shaheen and J. Bashir, “Neutron, Synchrotron X-Ray Diffraction and X-Ray Absorption Studies of CaLaFeMnO6 Double Perovskite,” Solid State Sciences, Vol. 10, No. 11, 2008, pp. 1634-1639. doi:10.1016/j.solidstatesciences.2008.02.007
[24] S. S. Pillai, S. N. Jammalamadaka and P. N. Santhosh, “Magnetotransport Properties of Ba2MnRuO6 and LaBa-MnRuO6,” Magnetics, IEEE Transactions, Vol. 43, No. 6, 2007, pp. 3076-3078. doi:10.1109/TMAG.2007.892568
[25] N. Binstead, J. W. Campbell, S. J. Gurman and P. C. Stephenson, “SERC Daresbury Laboratory EXCALIB and EXBACK Programs,” 1990.
[26] N. Binstead, J. W. Campbell, S. J. Gurman and P. C. Stephenson, “SERC Daresbury Laboratory EXCURV92 Programme,” 1991.
[27] S. J. Gurman, N. Binsted and I. Ross, “A Rapid, ExactCurved-Wave Theory for EXAFS Calculations,” Journal of Physics C: Solid State Physics, Vol. 17, No. 1, 1984, p. 143.
[28] T. Shibata, B. A. Bunker and J. F. Mitchell, “Local Distortion of MnO6 Clusters in the Metallic Phase of La1-x-SrxMnO3,” Physical Review B, Vol. 68, No. 2, 2003, pp. 024103.1-024103.10.
[29] J. Kanamori, “Super Exchange Interaction and Symmetry Properties of Electron Orbitals,” Journal of Physics and Chemistry of Solids, Vol. 10, No. 2-3, 1959, pp. 87-98. doi:10.1016/0022-3697(59)90061-7
[30] G. Matsumoto, “Study of (La1?xCax)MnO3. I. Magnetic Structure of LaMnO3,” Journal of the Physical Society of Japan, Vol. 29, No. 3, 1970, pp. 606-615. doi:10.1143/JPSJ.29.606
[31] B. K. Teo, “EXAFS: Basic Principles and Data Analysis,” Springer Verlag, New York, 1986.
[32] D. E. Sayers, E. A. Stern and F. W. Lytle, “New Technique for Investigating Noncrystalline Structures: Fourier Analysis of the Extended X-Ray—Absorption Fine Structure,” Physical Review Letters, Vol. 27, No. 18, 1971, pp. 1204 -1207. doi:10.1103/PhysRevLett.27.1204

Copyright © 2024 by authors and Scientific Research Publishing Inc.

Creative Commons License

This work and the related PDF file are licensed under a Creative Commons Attribution 4.0 International License.