Value Addition to Red Sediment Placer Sillimanite Using Microwave Energy and in Depth Structural and Morphological Characterization of Mullite

Abstract

This paper deals with the effect of microwave energy for mullite formation from placer sillimanite. A mullite formation is seen when 60 % SiC and 5% binder are used with the composite charge material, i.e. sillimanite (60%) and Al2O3 (40%). The maximum temperature of the microwave sintering furnace achieved is 1355°C at 2450 W microwave power. Addition of 10 % binder to the same charge material with 60% SiC, the furnace temperature achieved is 1384°C at microwave power 1900 W. Mullite is formed within 25 minutes from the sillimanite, under the above experimental conditions. Whereas under the similar additive conditions, the mullite formed from sillimanite in conventional furnace heating, it took 3 hours at 1300°C. XRD data show the mullite phase for both the products obtained from microwave sintering furnace and conventional furnace. FESEM image analysis shows the mullite formations, SiC fibrous cluster and alumina needles in microwave treated sample. Thus microwave heat source is much more effective for value addition to red sediment placer sillimanite to form mullite in compare to conventional furnace.

Share and Cite:

S. Srikant, S. Singh, P. Mukherjee and R. Rao, "Value Addition to Red Sediment Placer Sillimanite Using Microwave Energy and in Depth Structural and Morphological Characterization of Mullite," Journal of Minerals and Materials Characterization and Engineering, Vol. 11 No. 11, 2012, pp. 1055-1062. doi: 10.4236/jmmce.2012.1111110.

Conflicts of Interest

The authors declare no conflicts of interest.

References

[1] S. Tripathi and G. Banerjee, “Synthesis and Mechanical Properties of Mullite from Beach sand Sillimanite: Effect of TiO2,” European Journal Ceramic Society, Vol. 18, No. 14, 1998, pp. 2081-2087. doi:10.1016/S0955-2219(98)00149-6
[2] E. Fagury and R. Kiminami, “Al2O3/Mullite/SiC Powders Synthesized by Microwave-Assisted Carbothermal Reduction of Kaolin,” Ceramics International, Vol. 27, No. 7, 2001, pp. 815-819. doi:10.1016/S0272-8842(01)00035-9
[3] T. Ebadzadeh, M. H. Sarrafi and E. Salahi, “Microwave- Assisted Synthesis and Sintering of Mullite,” Ceramics International, Vol. 35, No. 8, 2009, pp. 3175-3179. doi:10.1016/j.ceramint.2009.05.013
[4] Y. Fang, Y. Chen and M. R. Silsbee, “Microwave Sintering of Fly Ash,” Material Letter, Vol. 27, No. 4-5, 1996, pp. 155-159. doi:10.1016/0167-577X(96)80007-3
[5] R. B. Rao and N. Patnaik, “Microwave Energy in Mineral Processing—A Review,” Journal of the Institution of Engi- neers (India)—Mining, Vol. 84, No. 2, 2004, pp. 56-61.
[6] C. A. Pickles, “Microwaves in Extractive Metallurgy: Part 1—A Review of Applications,” Minerals Engineering, Vol. 22, No. 13, 2009, pp. 1102-1111. doi:10.1016/j.mineng.2009.02.015
[7] E. T. Thostenson and T.W. Chou, “Microwave Processing: Fundamentals and Applications,” Composites Part A: Applied Science and Manufacturing, Vol. 30, No. 9, 1999, pp. 1055-1071. doi:10.1016/S1359-835X(99)00020-2
[8] D. E. Clark and W.H. Sutton, “Microwave Processing of Ceramic Materials,” Annual Review of Materials Science, Vol. 26, 1996, pp. 229-231. doi:10.1146/annurev.ms.26.080196.001503
[9] S. S. Srikant, P. S. Mukherjee and R. B. Rao, “Microwave Reduction of Placer Ilmenite Concentrate,” Mineral Processing Technology, 2011.
[10] H. Kozuka and J. D. Mackenzie, “Microwave Synthesis of Metal Carbides,” Ceramic Transactions, Vol. 21, 1991, pp. 387-394.
[11] A. C. D. Chaklader, S. D. Gupta, E. C. Y. Lin and B. Gutowski, “Al2O3/SiC Composites from Aluminosilicates Precursors,” Journal of the American Ceramic Society, Vol. 75, No. 8, 1992, pp. 2283-2285.

Copyright © 2024 by authors and Scientific Research Publishing Inc.

Creative Commons License

This work and the related PDF file are licensed under a Creative Commons Attribution 4.0 International License.