Author(s)

Basem Tarek^1*, Eman EL-Shenawy², Ahmed El-Sabbagh¹, Mohamed A. Taha^1*

¹Design and Production Engineering Department, Faculty of Engineering, Ain Shams University, Cairo, Egypt.
²Plastic Deformation Department, Central Metallurgical R&D Institute (CMRDI), Cairo, Egypt.

To attain an enhanced combination of mechanical properties for low alloyed steel, the current study has been made to fulfill that growing need in the industry. Its results are introduced within this paper. One step Quenching and Partitioning (Q&P) heat treatment has been applied on Niobium-based microalloyed steel alloy with 0.2 %C, in the form of 2 mm thickness sheets. The target of this study is to investigate the viability of applying that significantly recommended, results-wise, heat treatment on the highly well-suited alloy steel samples, to achieve the main target of enhanced properties. A single temperature of 275°C was used as quenching and Partitioning temperature. Four Partitioning periods (30, 200, 500, and 1000 Seconds) were used for soaking at the same temperature. The results were analyzed in the light of microstructural investigation and mechanical testing. All applied cycles did not enhance the strength but moderately improved the ductility and toughness, mainly caused by the slightly high soaking temperature used. Niobium impact of grain refining was apparent through all cycles. The cycle of 500 Seconds Partitioning time obtained optimum values at that particular temperature. The 1000 Seconds Cycle obtained the worst combination of properties. A set of recommendations are set. More research is required at this point, where a lower Partitioning temperature is advised. In the light of the applied combination of parameters, the Partitioning period at such temperature is advised to be between 500 and 1000 Seconds. A high probability that periods closer to 500 than 1000 Seconds will produce better results. More research is needed between those two values of Partitioning time to precisely determine the optimum time at that temperature on that specific alloy.

Nb-Based Microalloyed Steel, Advanced High Strength Steel, Quenching and Partitioning, Retained Austenite, Martensite Transformation, Automotive Applications

Tarek, B. , EL-Shenawy, E. , El-Sabbagh, A. and Taha, M. (2021) Feasibility of 0.02% Nb-Based Microalloyed Steel for the Application of One-Step Quenching and Partitioning Heat Treatment. Materials Sciences and Applications, 12, 374-387. doi: 10.4236/msa.2021.128026.