The Effect of Laminate Angles in Composite Substrates on the Performance of Rectangular Microstrip Antenna

Abstract

The performance of a microstrip antenna has been known sensitive to substrate’s dielectric properties, which is dependent on the angle of laminate layers inside a composite laminated substrate. Modal analysis in spectral domain is applied to investigate the resonant frequency and radiation pattern of rectangular microstrip antenna on composite substrates. It is shown that the substrate’s dielectric properties are dependent upon the laminate angles, i.e., upon the orientation of the antenna relative to the substrate’s fiber direction. For the same operating frequency, the antenna size on composite substrates is larger than that on isotropic substrates, and the far field pattern is also more directional.

Share and Cite:

Hung, C. and Yang, S. (2016) The Effect of Laminate Angles in Composite Substrates on the Performance of Rectangular Microstrip Antenna. Journal of Electromagnetic Analysis and Applications, 8, 261-270. doi: 10.4236/jemaa.2016.812024.

1. Introduction

Many studies of microstrip antenna design often assumed the substrate to be isotropic with uniform dielectric property. This “isotropic assumption” was made to conjecture the performance of a microstrip antenna attached on Kevlar composite substrate [1] and composite structure [2] . It has been known, however, that the resonant frequency of a microstrip antenna depends upon the substrate’s dimension (thickness) and material properties (permittivity and tangent loss). Yet little is known about the effects of composite substrate’s dielectric properties on antenna performance because of insufficient analytical models and/or numerical tools.

Composite laminated substrates have been widely used in aerospace structures, where continuous fiber/matrix layers stacking at suitable laminate angles can achieve desirable mechanical properties. Such substrates also facilitate embed- ding sensor/actuator and microstrip antenna to improve aerodynamic perfor- mance [3] . Previous studies of microstrip antenna in composite substrates were often by numerical methods, but none was able to predict the effects of different laminate angles on the substrate’s dielectric properties, and antenna performance.

The performance of a microstrip antenna attached on anisotropic layer is found to be strongly influenced by the substrate’s dielectric properties [4] [5] . A solution technique in frequency domain for analyzing electromagnetic wave propagation was developed to study an antenna embedded in composite laminated substrates [6] and to investigate the effect of dielectric overlay [7] . Recent study on microstrip antenna arrays on honey comb sandwich substrate [8] and composite laminated substrate [9] also validated that the antenna performance was sensitive to the substrate’s dielectric property―a function of the substrate’s laminate angles. Electromagnetic co-design by modeling the substrate structure is necessary [10] . Analytical solution would be desirable to conduct parametric study on substrate’s laminate angles affecting antenna performance.

2. Solution by Spectral Domain Analysis

Recent development of Conformal Load-bearing Antenna Structure (CLAS) by embedding microstrip antenna inside composite laminated substrates has been considered desirable. For a microstrip antenna with optical axis in y-direction on anisotropic substrate as illustrated in Figure 1, the permittivity matrix is

Figure 1. A microstrip antenna with its x-y-z axes of dimension (L ´ W) on the substrate with 1-2-3 axes in a laminate angle.

(1)

with dielectric constant along the fiber direction and along the other two normal axes, where, , and are the relative

permittivity, and in free-space. In isotropic substrates, the

optical axis (principal radiation direction) is normal to the antenna patch such that the permittivity matrix remains diagonal. In composite substrates, however, the antenna’s axes (x-y-z) may not necessarily be co-linear with any of the substrate’s principal axes ( 1-2-3 ). That leads to a non-diagonal permittivity matrix with 5 distinctive non-zero elements (permittivity), each being a function of the laminate angle θ. In spectral domain analysis [8] , the electromagnetic wave propagation of an antenna can be solved by using electric and magnetic Hertzian

potentials and. In vector form

and, where is the unit vector of coordinate transformation between the antenna’s x-y-z and the substrate’s 1-2-3 axes. The wave equations in terms of the Fourier transform pairs and can be written as

, (2a)

, (2b)

where, kx and kz are the Fourier variables of wave numbers with respect to x- and z-axis, respectively, is the operating frequency,

and.

By the solution technique in spectral domain [4] , the electric and magnetic fields of a substrate (denoted by superscript s) are represented by the Hertzian potentials,

(3a)

(3b)

( 3c )

and

( 4a )

(4b)

(4c)

The Hertzian potentials are obtained by solving Equations 2(a) and 2(b)

, ( 5a )

. (5b)

Similarly the solutions in the air medium (with superscript a) are

(5c)

(5d)

where and d is substrate thickness. The above coefficients, , , , and are determined by the boundary conditions. At the interface of ground plane leads to, and the coefficients, , and can be obtained by the 4 boundary equations in terms of the Hertzian potentials. Thus the tangential fields can be calculated by an algebraic equation of the immittance matrix and spectral current densities

(6)

The immittance matrix in Equation (6) is function of the laminate angle, substrate thickness d, dielectric constant along the fiber direction and along the other principal axes. Similar to previous work [4] , the spectral current densities can be solved by modal analysis. And the electromagnetic fields radiating in free space can then be determined by and,

(7a)

(7b)

(7c)

The size, resonant frequency, and the radiation pattern of a microstrip antenna on substrates of different laminate angles can then be calculated.

3. Resonant Frequency by Modal Analysis

For a rectangular microstrip antenna of dimension L ´ W, the base functions in modal analysis for solving Equation (6) can be selected as

, ( 8a )

, (8b)

and in spectral domain they are

, ( 8c )

, (8d)

where is the Dirac delta function. The antenna dimension can therefore be determined by the characteristic equation from Equation (6), and the electric field in space domain from Equations 7(a)-7(c) can be derived explicitly.

Consider the rectangular antenna from previous works [11] [12] : L = 1.0 cm and W = 0.2 cm on a substrate and thickness d = 0.158 cm to validate the modal analysis. Figure 2 shows the effect of substrate dielectric properties, represented by the substrate’s anisotropic ratio, on the resonant frequency at laminate angle. In the special case of isotropic substrate, GHz agrees very well with that given by [11] . For anisotropic substrate, however, the resonant frequency is monotonically decreasing

Figure 2. Resonant frequency of a microstrip antenna (L = 1.0 cm and W = 0.2 cm) on substrates, at different anisotropic ratios. Modal analysis results are validated by [11] on isotropic and by [12] on uniaxial substrates.

with increasing. GHz when while it is 4.9 GHz when. This result illustrates that the resonant frequency is strongly dependent on the substrate’s dielectric properties. In another special case, when, the substrate becomes uniaxial from mechanics view point, and the result also agrees very well with that in [12] . The resonant frequency remains monotonically decreasing at increasing. The above results show that the operating frequency of an antenna attached on isotropic, uniaxial or anisotropic substrate is significantly different because of the substrate’s permittivity. The frequency is in the range of 5 to 20 GHz depending on the substrate dielectric properties repre- sented by the anisotropic ratio.

In order to illustrate the effects of laminate angle on antenna performance, denote the size of a 2.4 GHz antenna on isotropic substrate by length and width. Figure 3(a) shows the effects of anisotropic ratio and laminate angle on a 2.4 GHz antenna of patch size L ´ W. The anisotropic ratio is found to have little influence on patch size, when; i.e., when, because the electromagnetic wave propagation is dominated by the dielectric properties along the laminate layer’s fiber direction. There are, however, large variations on antenna size, and similarly on resonant frequency, when or.

In addition, the laminate angle has profound impact on the patch size of a 2.4 GHz antenna. For a given size of rectangular microstrip antenna, Figure 3(b) shows that the resonant frequency is dependent upon the laminate angle. At, the resonant frequency is at about 1.8, 1.3, and 2.4 GHz, respectively, for, 0.75, and 1.0. For the substrate of, the antenna frequency is about 1.4 GHz at laminate angle, while it is 1.3 GHz at and 2.4 GHz at. Such significant differences in size and resonant frequency are critical to antenna design.

These results show that the laminate angle is critical to antenna performance. Electromagnetic wave propagation is very much influenced when, i.e.,. For all substrates with, the resonant frequency will deviate lower if mistakenly treating the substrate as isotropic. Antenna design without accounting for the substrate’s anisotropic nature of different ply angles can be erroneous.

4. Antenna Pattern by Modal Analysis

In addition to antenna size and resonant frequency, the effects of laminate angle on radiation pattern are even more sensitive. The far field patterns of an antenna operating at 2.4 GHz on y-z plane are shown in Figure 4. The radiation efficiency is scaled in the direction perpendicular to the microstrip patch, and the pattern of isotropic substrate (bold line) with the maxima in the normal direction is also plotted for reference. On composite substrates, however, the maxima will be shifted from the normal direction and is dependent on the laminate angle.

Figure 3. (a) The dimension of a 2.4 GHz microstrip antenna and (b) the resonant frequency of a given size antenna on the substrates of different anisotropic ratios and laminate angles.

Figure 4. The far field patterns of a 2.4 GHz microstrip antenna on composite substrates (d = 1.00 cm) of anisotropic ratio (a) η = 0.50 and (b) η = 0.75 at different laminate angles.

In Figure 4(a), the E-field pattern on substrate with and laminate angle has more radiation intensity than the other angles. The gain at about 70˚ elevation is about 5 dB higher than that at normal direction. At, the antenna pattern becomes omni-directional, but the patterns are very directional at all other laminate angles. With, the substrate becomes less anisotropic (approaching to isotropic substrate), the E-field patterns in Figure 4(b) have less ripples, but the effects of laminate angle on both the antenna resonant frequency and radiation pattern remain. Without accurate modeling, the prediction of antenna performance by assuming substrate of equal permittivity is seriously flawed. Microstrip antenna design on composite substrates with careful selection of substrate laminate angle can achieve better radiation efficiency.

5. Conclusions

1) An electromagnetic model in spectral domain has been applied to investigate the effects of substrate’s laminate angle on antenna performance. The non-diagonal permittivity matrix from different laminate angles comes from the fact that the fiber direction of the laminate layer may not necessarily align with the antenna’s optical axis. Modal analysis shows that the laminate angle has strong influence on antenna design. The resonant frequency of a rectangular microstrip antenna is very much different from that on isotropic or uniaxial substrates. The antenna size deviates lower at all laminate angles, except when the substrate is isotropic from mechanics view point.

2) Analyses show that the resonant frequency, and hence the length ratio Liso/ L, varies at different laminate angles, and the variations are more noticeable as thickness increases. The far field patterns show that the maxima will not always be in the normal direction and is dependent on the laminate angle. The performance of a microstrip antenna on composite substrate is very much different from that on isotropic substrate.

Acknowledgements

This work was supported in part by the National Science Council, Taiwan, under NSC100-2221-E006-098-MY3.

Conflicts of Interest

The authors declare no conflicts of interest.

References

[1] Yao, L. and Qiu, Y.P. (2009) Design and Fabrication of Microstrip Antennas Integrated in Three Dimensional Orthogonal Woven Composites. Composites Science and Technology, 69, 1004-1008.
https://doi.org/10.1016/j.compscitech.2009.01.013
[2] You, C.S., Hwang, W. and Eom, S.Y. (2005) Design and Fabrication of Composite Smart Structures for Communication, Using Structural Resonance of Radiated Field. Smart Materials and Structures, 14, 441-448.
https://doi.org/10.1088/0964-1726/14/2/019
[3] Yang, S.M., Hung, C.C. and Chen, K.H. (2005) Design and Fabrication of a Smart Layer Module in Composite Laminated Structures. Smart Materials and Structures, 14, 315-320.
https://doi.org/10.1088/0964-1726/14/2/003
[4] Yang, S.M. and Hung, C.C. (2009) Modal Analysis of Microstrip Antenna on Fiber Reinforced Anisotropic Substrates. IEEE Transactions on Antennas and Propagation, 57, 792-796.
https://doi.org/10.1109/TAP.2009.2013443
[5] Hung, C.C. (2009) Design and Analysis of Rectangular Microstrip Patches Embedded in Electromagnetically Anisotropic Composite Laminates. IEEE International Workshop on Antenna Technology, Santa Monica, 2-4 March 2009, 1-4.
https://doi.org/10.1109/IWAT.2009.4906881
[6] Yang, S.M. and Hung, C.C. (2015) The Effect of Dielectric Overlay on Microstrip Antenna Embedded in Composite Laminated Substrates. International Journal of Numerical Modelling: Electronic Networks Devices and Fields, 28, 155-163.
https://doi.org/10.1002/jnm.1993
[7] Yang, S.M. and Hung, C.C. (2015) On the Performance of Microstrip Antenna Embedded in Composite Laminated Substrates. International Journal of Numerical Modelling: Electronic Networks Devices and Fields, 28, 371-380.
https://doi.org/10.1002/jnm.2012
[8] Son, S.H., Eom, S.Y. and Huang, W.B. (2008) Development of a Smart-Skin Phased Array System with a Honeycomb Sandwich Microstrip Antenna. Smart Materials and Structures, 17, 5012.
https://doi.org/10.1088/0964-1726/17/3/035012
[9] Yang, S.M., Huang, C.H. and Hong, C.C. (2014) Design and Analysis of Microstrip Antenna Arrays in Composite Laminated Substrates. Journal of Electromagnetic Analysis and Applications, 6, 115-124.
https://doi.org/10.4236/jemaa.2014.66011
[10] Zhou, J., Huang, J., Song, L., Zhang, D. and Ma, Y. (2015) Electromechanical Co-Design and Experiment of Structurally Integrated Antenna. Smart Materials and Structures, 24, 1-11.
https://doi.org/10.1088/0964-1726/24/3/037004
[11] Itoh, T. and Menzel, W. (1981) A Full-Wave Analysis Method for Open Microstrip Structures. IEEE Transactions on Antennas and Propagation, 29, 63-68.
https://doi.org/10.1109/TAP.1981.1142520
[12] Nelson, R.M., Rogers, D.A. and d’Assuncao, A.G. (1990) Resonant Frequency of a Rectangular Microstrip Patch on Several Uniaxial Substrates. IEEE Transactions on Antennas and Propagation, 38, 973-981.
https://doi.org/10.1109/8.55607

Copyright © 2024 by authors and Scientific Research Publishing Inc.

Creative Commons License

This work and the related PDF file are licensed under a Creative Commons Attribution 4.0 International License.