Effect of Heat Treatment on Mechanical Properties of Al-1.5Cu-9.5Zn-3Mg Rapidly Solidified Alloy

El Said Gouda, Emad Makboul Ahmed, Nabih Lotfi Tawfik
DOI: 10.4236/msa.2010.14031                

Abstract

Ribbons with the composition Al-1.5Cu-9.5Zn-3Mg were prepared by melt spinning technique. Microhardness and tensile strength were measured. The melt spun hardness and ultimate tensile strength values were as high as 291 HV and 660 MN/m2, respectively. Hardness values are relaxed to lower values on prolonged thermal annealing to around 50%. X-ray diffraction lines corresponding to Cu, Zn and Mg were disappeared for the as melt spun ribbons, which indicates a complete solubility of these element in Al matrix. On prolonged thermal annealing these alloying elements were precipitated.

Keywords

Microhardness, Rapid Solidification, UTS, Tensile Strength

Conflicts of Interest

The authors declare no conflicts of interest.

References

[1]	S. J. Maddox, “Review of Fatigue Assessment Procedures for Welded Aluminum Structures,” International Journal of Fatigue, Vol. 25, No. 12, 2003, pp. 1359-1378.
[2]	J. R. Davis, “Aluminum and Aluminum Alloys,” ASM International, Mate-rials Park, OH, 1998.
[3]	C. Zhou, X. Yang and G. Luan, “Investigation of Microstructures and Fatigue Properties of Friction Stir Welded Al–Mg Alloy,” Journal of Materials Chemistry and Physics, Vol. 98, No. 2-3, 2006, pp. 285-290.
[4]	B. Grushko E. Kowalska, B. Przepi and M. Surowiec, “An Investigation of the Al-Cu-Cr Phase Diagram: Phase Equilibria at 800-1000℃,” Journal of Alloys and Com-pounds, Vol. 417, No. 1-2, 2006, pp. 121-126.
[5]	D. R. Fang, Z. F. Zhang, S. D. Wu, C. X. Huang, H. Zhang, N. Q. Zhao and J. Li, “Effect of Equal Channel Angular Pressing on Tensile Properties and Fracture Modes of Casting Al-Cu Alloys,” Journal of Materials Science and Engineering A, Vol. 426, No. 1-2, 2006, pp. 305-313.
[6]	B. B. Straumal, B. Baretzky, A. A. Mazilkin, F. Phillipp, O. A. Kogtenkova, M. N. Volkov and R. Z. Valiev, “Formation of Nanograined Structure and Decompo-sition of Supersaturated Solid Solution during High Pressure Torsion of Al-Zn and Al-Mg Alloys,” Journal of Acta Materialia, Vol. 52, No. 15, 2004, pp. 4469-4478.
[7]	A. Bia?obrzeski, and E. Czekaj, “An Attempt to Use Alloy Synthesis in Evaluating the Corrosion Behaviour of Al- and Mg-Based Alloys,” Journal of Materials Processing Technology, Vol. 175, No. 1-3, 2006, pp. 27-32.
[8]	E. M. AbdelHady, N. L. Tawfik and E. S. Gouda, “Mechanical Properties of Some Al-Based Alloys with Heat Treatment,” Journal of Heat Treatment and Surface Engineering, Vol. 8, No. 1-2, 2007, pp. 39-45.
[9]	M. Kamal and E. S. Gouda, “Effect of Cooling Speed on Structure and Properties of Rapidly Solidified Pb-25wt.% Sn Alloy,” Journal of Radiation Effects and Defects in Solids, Vol. 162, No. 9, 2007, pp. 691-696.