1. Introduction
Isothianaphthene is one of the most studied polymers among conductive polymers. The synthesis requires high experimental technique of ring closure reaction with suppression of side reaction of polymerization [1] - [17] . Protection of α-positon of the thiophene ring of the isothianaphthene unit with silyl group has been carried out. Vanderzande group synthesized an isothianaphthene sandwiched monomer between thiophene units for improving stability, and carried out electrochemical polymerization [5] [8] . Resultant polymer shows low-bandgap nature derived from isothianaphthene, and shows good redox property. Isothianaphthene based polymer also displays good electrochromic property [18] [19] [20] . While crystallinity of electrochemically synthesized polymers prepared in common organic solvent is high, control of morphology of main-chain structure is difficult. To date, we have carried out electrochemical polymerization in low- molecular-mass liquid crystal as an electrolyte solution. The polymer thus obtained reflects structure of liquid crystal electrolyte solution from molecular level to macroscopic level. However, a large quantity of liquid crystals needs to be applied for reaction medium. Further, multi-step synthesis is required for obtaining low molecular liquid crystals. Although reuse of the liquid crystal electrolyte solution is possible, purification is required. Hydroxypropyl cellulose (HPC) is a semi-natural polymer by modification with the propyl group [21] [22] [23] [24] . Hydroxypropyl cellulose (HPC) is an amphotropic polymer and acts as surfactant. Recently, HPC is used as a template or composite material [25] [26] [27] . HPC dissolves in both water and organic systems. Furthermore, HPC exhibits lyotropic liquid crystallinity in the water or organic solvent at appropriate concentration. To perform electrochemical polymerization in liquid crystal, monomer needs to be dissolved in the liquid crystal electrolyte solution. Many monomers are soluble only in organic solvents and have hydrophobic property. So, electrochemical polymerization of hydrophobic monomers needs to perform in organic solvent. HPC/organic liquid crystal medium can overcome this point. High concentrated HPC in DMF solution shows lyotropic liquid cry- stallinity, and hydrophobic organic monomers can dissolve in the HPC/DMF system. So, organic monomer can polymerize in the HPC/DMF. Moreover, HPC shows cholesteric liquid crystal having an optically activity with helical structure in organic solvents. The polymer prepared in this system is expected to be chiral polymer. Based on this consideration, we electrochemically synthesize an isothianaphthene based optically active low-bandgap polymer in HPC/DMF electrolyte solution.
2. Experimental
2.1. Materials
A monomer [thiophene]-[isothianaphthene]-[thiophene] was prepared by previously reported method [3] . Hydroxypropyl cellulose was obtained from Wako Pure Chemical Industries, Ltd. and used as supplied. Tetrabutylammonium perchlorate was obtained from Tokyo Chemical Industry Co., Ltd. and used as supplied. N,N-dimethylformamide was obtained from Nacalai Tesque, Inc. and used as supplied.
2.2. Electrochemical Polymerization
Electrochemical polymerization of a monomer [thiophene]-[isothianaphthene]- [thiophene], abbreviated as T-ITN-T, was carried out in hydroxypropyl cellulose (Figure 1). Constituents of electrolyte solution are summarized in Table 1. Firstly, tetrabutylammonium perchlorate (TBAP) (supporting salt) and monomer was dissolved in N,N-dimethylforma- mide (DMF) (Figure 2(a)). Next, hydroxypropyl cellulose was added to the electrolyte solution containing monomer and supporting salt (Figure 2(b)). The solution was stirred mechanically by glass rod for 1 min at room temperature (Figure 2(c)). A polarizing optical microscopy image of the lyotropic liquid crystal solution is shown in Figure 3. Then, electrochemical polymerization was carried out by using sandwich cell
Figure 1. Scheme of electrochemical polymerization of [thiophene]-[isothianaphthene]- [thiophene].
Table 1. Constituents of electrolyte solution.
a[thiophene]-[isothianaphthene]-[thiophene]; bHydroxypropyl cellulose; cTetrabutylammonium perchlorate.
Figure 2. Experimental diagram for preparation of electrolyte solution containing monomer.
Figure 3. Polarizing optical microscopy image of electrolyte solution.
method with two ITO glass electrodes (ITO = indium tin oxide) developed by our group previously. Direct current (dc) voltage of 2.5 V was applied across of the cell for 60 min. A thin film was deposited on an anode side of the electrode. After the electrochemical reaction, the sandwich cell was soaked into the water to remove the residual HPC from the film surface. After a 30 min, the sandwich cell was disassembled easily. The resultant was washed with water, and acetone to yield a thin film deposited on the ITO coated glass, abbreviated as P(T-ITN-T)/HPC.
2.3. Measurements
Optical texture observations were carried out by using an ECLIPS LV 100 high- resolution polarizing microscope (Nikon). Fourier Transform Infrared absorption was obtained with a FT-IR 4600 (Jasco) by using the KBr method. UV-vis absorption spectroscopy was carried out by using V-630 (Jasco). Cyclic voltammetory were carried out with a μAUTOLAB TYPE III (ECO Chemie). Electrolyte solution contained 0.1 M TBAP in acetonitrile. Circular dichroism spectroscopy was carried out with a J-720 (Jasco).
3. Results and Discussion
3.1. Polarizing Optical Microscopy Observation
The polymer thus obtained shows clear fingerprint texture under polarizing optical microscopy (POM) in Figure 4. The fingerprint pattern is derived from cholesteric liquid crystal of HPC helical aggregation, indicating occurrence of transcription of helical structure of HPC during the electrochemical polymerization. In this case, HPC acts as a helical template.
3.2. Fourier Transform Infrared Absorption
Fourier transform infrared (FT-IR) absorption spectroscopy measurements of
Figure 4. Polarizing optical microscopy (POM) image of obtained polymer film.
HPC (matrix), T-ITN-T (monomer) and P(T-ITN-T)/HPC are shown in Figure 5. HPC shows broad O-H vibration absorption around 3450 cm−1 due to hydroxyl group in the pyranose unit. Absorption band around 2960 cm−1 is due to CH2 and CH stretching vibration. The polymer shows absorption band at 3430 cm−1 due to the O-H stretching vibration of cellulose unis. This result revealed that the resultant material is composite of P(T-ITN-T) and HPC. HPC component cannot be separated after washing of the film with solvents.
3.3. UV-Vis Absorption
In situ UV-vis absorption measurements were carried out during cyclic voltammetry measurement. Change in the UV-vis of P(T-ITN-T)/HPC at various application potential are shown in Figure 6. The polymer shows absorption band at around 550 nm due to - transition of main chain. A new absorption band at 960 nm is derived from polaron band (radical cation) at oxidation process (Figure 6(a)). The absorption intensity of polaron band increases with application of voltages, indicating progress of electrochemical oxidation (doping). On the other hands, reduction process (Figure 6(b)) shows decrease of absorption intensity of the polaron band. The electrochemically reduced state at 0 V of the composite has a bandgap of 1.5 eV, which is in the range of low-bandgap conjugated polymers.
Changes in intensity of absorptions are repeatable through electrochemical doping/dedopoing (redox) process. To confirm the repeatable electrochromic property, change in absorption intensity at 550, 730 and 1030 nm upon repeating application of voltage between 0 and 1.0 V (vs. Ag/Ag+) was examined for 750 s
Figure 5. FT-IR spectra of hydroxypropyl cellulose (HPC) (black line), monomer (T-ITN-T) (blue line) and P(T-ITN-T)/HPC (red line).
Figure 6. UV-vis absorption spectra of P(T-ITN-T) at various applied potentials (vs. Ag/Ag+). Oxidation process (a) and reduction process (b).
at a scan rate of 50 mV/s (Figure 7).
3.4. Cyclic Voltammetry
Cyclic voltammetry (CV) analysis of P(T-ITN-T)/HPC was carried out at various scan rates of 10, 20, 30, 40, 50, 60, 70, 80, 90 and 100 mV/s. The CV result is shown in Figure 8. First oxidation wave indicates that the polymer film was oxidized and polarons (radical and cation) were generated. At reduction process, reduced wave was confirmed, indicating that the polymer film was reduced. The polymer film exhibits repeatable redox behavior in the applied potential range from 0 to 1.0 V (vs. Ag/Ag+).
3.5. Circular Dichroism Absorption
Circular dichroism (CD) absorption spectroscopy measurement was carried out for as prepared polymer film and reduced polymer film. The CD spectra of the film are shown in Figure 9. The reduced film was prepared by hydrazine vapor for 30 min. Reduction allows increase of the absorption band at around 400 nm due to decrease of fraction of polarons in the main-chain accompanied by
Figure 7. Time dependence of the UV-vis absorption intensity at 550, 730 and 1030 nm of P(T-ITN-T)/HPC film during repeated potential cycled between 0 and 1.0 V (vs. Ag/Ag+) for 750 s at a scan rate of 50 mV/s.
Figure 8. Cyclic voltammogram of P(T-ITN-T)/HPC at various scan rates of 10, 20, 30, 40, 50, 60, 70, 80, 90, and 100 mV/s vs. Ag/Ag+ reference electrode in 0.1 M/TBAP acetonitrile solution. TBAP = tetrabutylammonium perchlorate.
Figure 9. CD spectra of P(T-ITN-T). As prepared state (solid line) and reduced state (dashed line).
de-doping, indicating optical activity of the composite can be changed by the reduction.
4. Conclusion
Synthesis of a P(T-ITN-T)/HPC composite film by electrochemical polymerization in a HPC liquid crystal medium was successfully carried out. The POM observation for the composite film shows a fingerprint texture resembling the cho- lesteric liquid crystal and indicates that transcription of a helical structure of HPC is occurred. In situ UV-vis absorption spectra and cyclic voltammetry show that the polymer has repeatable electrochromic property. The CD spectroscopy measurements suggest that synthesis of the optical active composite is achieved from a monomer having no asymmetric carbon. The optical bandgap of P(T-ITN- T)/HPC is estimated to be 1.5 eV, which is in the range of low-bandgap conjugated polymers.
Acknowledgements
We would like to thank Tsukuba Research Center for Interdisciplinary Materials Science (TIMS).