Received 5 December 2015; accepted 13 March 2016; published 16 March 2016

ABSTRACT

This paper outlines the synthesis of maghemite from raw iron waste obtained in an iron mill dumpsite around Ogun state, Nigeria. Magnetite was synthesized from the ferrous precursor obtained by digesting the iron waste with concentrated H₂SO₄. Transformation of magnetite to maghemite was done by heating the magnetite obtained in an oven at 200˚C. To determine the absorption capacity of the synthesized maghemite sample, a stock solution of As(III) was used for the absorption. Absorption spectrum shows higher absorption of γ-Fe₃O₄ at higher concentration of As(III). Maximum absorption obtained is 14 mg/g. Estimated yield of γ-Fe₃O₄ was 32%; however a low, further study promises to improve the yield value. The study shows γ-Fe₃O₄ to be a good absorbent for heavy metals.

Keywords:

Atomic Absorption, Maghemite, Arsenic, Iron Waste

1. Introduction

Iron oxide generally exists in different structures and forms with different useful applications ranging from geological to nanoscale technology; the most common however are α-Fe₂O₃ (hematite), γ-Fe₂O₃ (maghemite), Fe₃O₄ (magnetite) and Fe_1−xO (wustite); the less commonly found are β- and ε-Fe₂O₃ [1] . Maghemite has the same crystalline structure like Fe₃O₄ (magnetite). Main distinct features of maghemite are the presence of vacancies in Fe position with symmetry reduction. These basic polymorphs, the cubic bixbyite structure “beta” and orthorhombic structure “epsilon”, as well as nanoparticles of all forms, have been synthesized and extensively investigated in recent years [2] . Out of all these polymorphs, magehmite is the iron oxides currently most studied, which exhibits ferrimagnetic behavior below 1000 K due to the super exchange integrals competition between tetrahedral and octahedral sites and lately, it has found considerable uses in magnetic resonance imaging, magnetic recording media, fabrication of biocompatible magnetic fluids, and electrochromic devices [1] [3] . Much focus has been given to it resulting in the modification in the growth, crystal structure, magnetic and electrical properties

However, a present review of the various synthesis methods available for maghemite nanoparticles growth shows co-precipitation, thermal decomposition, hydrothermal synthesis, microemulsion, sonochemical synthesis, and sonochemical as the most common methods; other methods such as electrochemical synthesis, laser pyrolysis techniques are not common [4] . Considering the present and the future prospect of maghemite crystals, it becomes highly needful to develop a simple, cheap and sustainable method for the synthesis of maghemite nanoparticles.

Metals are natural components of the environment including soil but they are of great concern when they are being added continuously. Nigeria as a country has a lot of iron mining and other allied iron processing companies. Unfortunately, only few of these companies have a standard way of disposing their waste iron scrap. This has a devastating effect on the environment with a long-term impact [5] [6] . The aim of this study is to carry out an absorption study on Arsenic stock solution using synthesized maghemite from the iron scrap which has an absorbent.

2. Experiment Details

2.1. Preparation of Ferrous Precursor

Experiment was carried out according to Legodi et al. (2007) [7] . Iron scrap obtained from a factory dumpsite in Ogun state, Nigeria was grinded and sieved to obtain a fine iron particle. 60 g of this sieved iron water was digested with 300 ml of concentrated H₂SO₄ until a turbid solution was observed and further heated to dryness. This was used as a ferrous precursor.

2.2. Preparation of Maghemite from Ferrous Precursor

20 g of the ferrous precursor was added to 120 ml of deionized water. The mixture was stirred gently. A green precipitate solution of Fe²⁺ was formed and filtered off. 25% NH₄OH, prepared by making up 25 ml of concentrated ammonia in a 100 ml standard flask with deionized water was added to the filtrate and allow to age for 20 hours and filtered before washing with deionized water. On drying, a crystalline, fine, black particle of magnetite was obtained. Finally, the magnetite obtained above was oven heated at 200˚C for two hours according to the equation below (Equation (2.2)). Maghemite particles, with a light brown coloration were obtained. The experiment was performed inside a glove box to prevent any possible oxygen contamination

(2.1)

(2.2)

2.3. Sorption Experiment

Two batches (A and B) of various standards, 10, 20, 30, 40, 50, 100, 200, 300, 400, 500, and 1000 ppm of As(III) solution was prepared. Batch A was taken as the standard solutions with which the amount of As(III) sorbed were referenced 0.5 g of the maghemite particles synthesized was weighed into each concentration of the second batch and stirred vigorously in a mechanical stirrer until complete dispersion was observed. Atomic absorption spectrophotometry was used in determining the actual concentration of As(III) in both batches.

3. Result and Discussion

The absorption data obtained for both batches are tabulated as in Table 1 and Table 2.

The concentration of As(III) in the stock after the absorption was also determine and the result is presented in Table 3. Using the Equation (3.1) below, the amount of As absorbed by the maghemite sample can be evaluated. The amount Q_sorbed, is also tabulated below:

(3.1)

where Q_sorbed is the amount of maghemite iron adsorbed, v is the volume of the stock solution taken for analysis, C_i is the initial concentration of the As(III), C_f is the final concentration of the As(III) after the absorption and m is the mass of the maghemite sample used for the absorbtion experiment (Table 3).

A plot of Q_sorbed (mg/g) against concentration of arsenic (ppm) (see Figure 1) was used to determine the linear absorption of the maghmite samples. It could be seen that Q_sorbed is directly proportional to the concentration of standard implying that more heavy metals such As, Cr, Hg, Pb, etc. could be easily removed with the method. Such heavy metals are found to be inherently laden in companies discharged waste and other heavy industrial waste dump. This technology can be improved to treat discharge waste of heavy metal and make them environmentally friendly.

Yield Calculation

Mass of iron waste used 60 g

Mass of ferrous Precursors obtained after digestion 70 g

Residue obtained after washing with excess water and filtering 50.22 g

This implies that Mass of Fe³⁺ that’s dissolved 70 g - 50.55 g 19.78 g

Mass of Magnetite obtained after drying 9.02 g

From the equation of reaction (2.1 above),

3 moles of Fe³⁺ (168 g/mol) 2 moles of Fe₃O₄ (233 g/mol)

⟹ Number of moles of Fe₃O₄ produced = [(19.78 g ´ 3 mol)/168 g∙mol⁻¹]/3 mol

⟹ Experimentally, 0.118 mole of Fe₃O₄was obtained

⟹ 27.376g (Molar mass of Fe₃O₄ ⟹ 232 g∙mol⁻¹)

Percentage yield of Fe₃O₄ = ⟹ 32.96%

One mole Fe₃O₄ (232 g/mol⁻¹) ⟹ one mole of (160 g∙mol⁻¹) γ-Fe₂O₃

⟹ 9.02 g of Fe₃O₄ ⟹ [9.02 g ´ 160 g∙mol⁻¹]/232 g∙mol⁻¹ ⟹ 6.220 g

Percentage of γ-Fe₂O₃ ⟹ ⟹ 68.95%

4. Conclusion

It has been shown that maghemite can be successfully synthesized from waste iron by transforming the magnetite obtained from the ferrous precursor. Sorption experiment proved maghemite to be a good absorbent for As(III). Other heavy metals such as Cr, Pb, etc. were however not studied. The absorption was low at lower concentration (10, 20, 30, 40, 50 ppm). More As(III) were sorbed at higher concentration. Experimental yield obtained for mghmite finally synthesized was low (32%). We believe that this can be improved with more studies. Heavy metals present in most water, waste and other environmental surfaces can be successfully removed at a low cost and pollution reduction.