Photostructural changes and electrical switching are the well-known features of amorphous chalcogenides, also known as glassy semiconductors. Although the both phenomena were intensively studied experimentally and have a wide practical application, their nature is debated up to now. I propose a new approach that considers glass as a self-organizing system owing to characteristic instability of chemical bonding in the form of bond wave. The bond wave model is shown to be suitable for explanation of the observed effects in thin films under the action of light or electrical field, a result that opens a new way for understanding and managing the processes in glassy semiconductors.
Amorphous chalcogenides represent a relatively new class of materials, glassy semiconductors, whose discovery of sixty years ago [ 1 ] has created a puzzle of how can semiconductor exist in the non-crystalline state [ 2 ]. During the following intensive study, which was initiated in the Kolomiets’ laboratory [ 3 , 4 ], many principal features of these materials were soon established, electrical switching (ES) and photostructural changes (PSC) being the most popular from both experimental and practical points of view [ 5 ].
Despite of intensive experimental study for a more than half-century, the nature of PSC and ES remains under discussion. Here I propose not a next model but a principally new approach, which is based on understating glass as a self-organizing system [ 6 ]. To be more concrete, the bond wave model is used for explanation of the known experiments and for planning of the new ones, emphasizing the usage of information fields to control underlying processes.
This model stands on two supports: the theory of chemical bonding and the theory of self-organization. These two aspects are considered independently in glass community up to now. Chemical bonding is a very popular topic, beginning from the continuous random network after Zachariasen [ 7 ]; CRN represents an ideal glass structure composed from “normal” covalent bonds (CB), the same that exist in a related crystal. Self-organization is a fresher term in glass theory; it was introduced and developed by Boolchand et al. [ 8 , 9 ] to denominate the so-called “intermediate phase” realizing in a definite composition range of complex (two- and more component) glass-forming systems; it is attributed to the stress-free state of CRN considered in frames of the so-called “topological theory” of glass structure [ 10 - 12 ]. It should be noted, however, that such “self-organization” seems rather self-assembling [ 13 ] than classical self-organization introduced by Haken [ 14 , 15 ] and Prigogine [ 16 , 17 ] for understanding the processes of evolution and adaptation in non-equilibrium complex systems.
Classical self-organizing system is an ordered formation that interacts with its surrounding by means of dissipative patterns characteristic for this system―therefore the first name is “self”. A concrete state of such a system depends not only on the conditions (temperature, pressure, etc.) but also on the path, by which the system went to the point of observation. In this sense, self-organizing system possesses “memory”, a property that is reflected in glass theory as the “landscape” picture or the “fictive temperature” parameter. Nevertheless, self-organization in its classical sense has not been applied to the glassy state so far, excluding the author’s bond wave approach. This approach is based on the chemical bonding instability (when one and the same atoms can be linked by one or another bond of different parameters) and the collective character of this instability in the form of bond wave, which means the spatiotemporal correlation between elementary acts of the chemical bonds exchange. Bond waves are considered as the dissipative patterns characteristic for glass-forming substances. In
Bond wave means the appearance of sub-lattice of the Λ = λD period in common CRN. One can ask what is the need for alternative bonds and corresponding sub-lattice? The need for special “soft” bands/cuts containing some “weakened bonds”, which divide the stressed regions of CRN, was recognized
more that half-century ago [ 19 , 20 ]. Some later Ovshinsky has forwarded the concept of bond option as a necessary condition for realization of the non-crystalline state [ 21 ]. The most consistent and detailed investigation of the chemical bonding problem in the context of glassy state was made by Dembovsky, who went from hypothetical “quasimolecular defects” in 1981 [ 22 ] to hypervalent bonds (HVB), the latter being investigated intensively in typical inorganic glass formers by means of quantum-chemical method. Some examples are given in
Unfortunately, HVB was not found in SiO2 [ 27 ], and the HVB in GeO2, which is composed of 5- and 6-fold coordinated silicon atoms (Si5 and Si6) and 3-fold coordinated oxygen (O3) atom, was observed only when the calculation cluster was pressed by shifting of its boundaries [ 28 ]. Interestingly, Si6 was found in the case of complex SiO2-P2O5-Na2O system [ 29 ]; and, as concerns pure silica, there were found non-hypervalent “soft” 3c-4e (three-center, four-electron) bonds [ 30 ]. Therefore, hypervalency seems to be not so important property for glass formation as an ability for bond alternation itself, therefore, I use the term alternative bond (AB) for general description of self-organization in non-crystalline network.
As to the wavy-like sub-lattice in CRN (
The previous application of the bond wave model for interpretation of glass features [ 31 - 36 ] have concerned macroscopic properties, in which the 3D (volume) effects due to the Λ-lattice prevail. In the present case of films, the coexistence of 2D and 3D effects becomes essential. In addition, the two types of surfaces, a “free” surface (opposite to the substrate) and the “boundary” surface between substance and substrate, should be considered.
The state of bond wave at the free surface of a sample is unclear now. One can suppose the ripple-like surface waves like those observed on the river surface when wind blows. Really, the ripples of the Λ ≈ 700 nm period were observed in the Se-S glass after the action of femtosecond laser [ 37 ]. The problem is that self-organized laser-induced ripples exist in non-glass forming substances too, for example in polycrystalline Ti [ 38 , 39 ]; the phenomena itself was have been discovered as far as in 1965 [ 40 ]. Therefore, let us consider how can the bond waves characteristic for glass-forming substances interact with the film substrate. The possible effects are shown schematically in
One should remember that film is prepared in “hot” conditions, when the initial temperature is much higher than the glass transition temperature; in any case the incoming particle energy is very high. Therefore, the growing films can produce dissipative patterns in the form of 3D bond waves, which interact with
a relatively cold substrate and then frozen on it at the end of the process. Interactions of two types seems to be essential. First is the “chemical” interaction since substrate composition can be amiable, neutral or hostile for the wavefront of the forming bond wave, so the wave orients in a conforming direction (
The well-known fact is that properties of fresh (as-prepared) and annealed films can differ significantly. It is also known that the angle of evaporating influences on the following film behavior [ 41 ]. Such facts concerning film history become quite clear when considering film as the self-organizing system owing to formation of bond waves during its preparation. For example, when film is prepared in extreme conditions, such as flash evaporation onto the cooled surface, the film body has no a time to generate bond wave before solidifying―only the fragments of wavefronts are frozen in the solid film (
A mutual feature of both photostructural changes (PSC) and electrical switching (ES) is their development under the action of external energy sources, namely, laser irradiation for PSC and electric field for ES. Note that classical self-organizing systems realizes only in the streams of energy, matter (not necessarily) and information. The latter stream in the form of information field [ 15 ] gives the direction in which such a system evolves; in our case the direction in which bond wave propagates. The streams of information and energy can have the same nature, e.g., thermal source ensures both temperature-dependent formation of alternative bonds with their collective movement through CRN and the bond wave direction by temperature gradient, grad T. For example, let us consider the fracture of glassy rod from the point of view that fracture denudes the wavefronts of bond wave(s) that had developed before solidification.
There are two features observed in
Note that the energy stream not necessary be the information stream at the same time, and vice versa. We have observed just the information action of weak magnetic field on viscosity of softening (T > Tg) selenium glass [ 42 , 43 ]. The field is “weak” in the sense that the elementary energy of magnetic field was incommensurably low relatively to that of thermal energy ( μ B H ≪ k T for H ≈ 250 Oe and T ≈ 300K), so thermal motion should destroy all the field induced effects. Nevertheless, a giant change of viscosity was indicated: up to 6 times in alternating magnetic field, when changing the field direction at resonance conditions (50 Hz field frequency versus 310 K sample temperature) [ 43 ].
PSC are so rich and diverse that it is impossible to consider them in one way from phenomenological point of view. A concrete effect depends on the film composition, thickness and history; on the illumination conditions (energy, intensity, time, polarization, etc.); other factors being also important (substrate, impurities, atmosphere, etc.). As a result, one can observe both classical “darkening”, i.e., the red-shift of the optical absorption edge, and “bleaching” (blue-shit), both expansion and construction of the illuminated region, as well as various anisotropic effects (see ref. [ 44 ] for introducing review). Therefore, I propose not a unified model for PSC but a unified bond wave approach by which a specific understanding of each concrete case can be achieved, and the following experiments can be planned.
Let us consider the so-called giant photo-expansion as an example. The phenomenon of a relatively large (5%) expansion of the As2S3 film irradiated by the sub-gap (2.0 eV) laser with the formation of smooth “lens” on the irradiated surface region was discovered 1994 [ 45 ]. Later Tanaka et al. [ 46 ] have proposed a general “geometric” picture and a “microscopic” model to explain this phenomenon. I agree with the picture, when the sub-gap light can excite a relatively deep cylinder, which then is pulled out from the film body―but not with the model that considers elementary processes in the region of about 1 - 10 nm. To my opinion, to create an object of a regular form and a relatively large dimension (the lens diameter is ~1 - 10 μm) a collective feedback between the excited microscopic regions should exist.
To understand the phenomena let us apply the bond wave model, as it is shown in
under it has another sub-structure than surrounding, thus, this is not only the form effect―the region below the lens should have different properties (optical, etc.) than the residual film body.
Now let us consider the deviations from this picture. It is known that lenses not always appear under laser illumination of the film surface. For example, the Ga10Ge2S65 film was also expanded after illumination, but its surface looked like a peeling skin: no lenses and even no ripples were observed there [ 47 ]. This is a result of an extra high light energy employed: the photons of h ν ≫ E g cannot penetrate the film, and even if alternative bonds are generated on the surface, they cannot organize even 2D bond wave, only a randomly damaged and thus expanded region is formed.
In the other work [ 48 ], when the band gap illumination (hν ≈ Eg) was applied to the GeS2-Ga2O3 film, no lens or pillow appear, instead, a pulled cylinder was observed. The applied light also cannot create a deep excited well, however, it acts more gently than in the previous case of the super-gap irradiation. Therefore, the newly generated alternative bonds are firstly organized into 2D bond waves on the film surface. For further self-organization into 3D bond wave there needs a space for its spreading―and the excited region provide it by means of extraction of the material from the inferior layer. The cylinder grows during illumination in the direction of the energy source. After cessation of illumination the “extracted” cylinder freezes because of the freezing of 3D bond wave that was formed it.
Interestingly, various reliefs (lenses, cylinders, needles, hollows, etc.) can be obtained also by electron beam [ 49 ], thus, the nature of the energy source is not very essential for formation of the self-organizing patterns in glassy films.
ES is the phenomenon of a sharp increase of conductivity of non-crystalline chalcogenide film when approaching the critical value of the electric field intensity, the so-called threshold voltage, Vth. The following negative-resistance state can be either reversible, when at the coming down side of income impulse the film returns to its initial high-resistant state, or transforms into a new low-resistance state, which means formation of a crystalline channel between the electrodes. The first case is known as the threshold switching (TES), and the latter is known as the memory switching (MES). The latter is of a great practical importance because of its usage in the digital technology for writing, storage and recording of information, a fact that is probably leads to recognition Ovshinsky, who was the designer of first memory cells, the father of electrical switching phenomenon. Nevertheless, one should not forget that the discovery of MES in 1968 [ 50 ] was published of 5 years later the TES discovery in 1963 by Russian scientists Kolomiets & Lebedev [ 51 ].
Both TES and MES have the negative-resistance state, after which the following return (TES) or crystallization (MES) finish the cycle. The end depends on the crystallization ability of a substance. For example, in the Ge-Se-Bi system it is possible to obtain both TES and MES in different ranges of Bi concentration, (Bi is known to be the crystallization agent) [ 52 ]. In frames of the bond wave model one can propose the following scheme of the ES process.
The initial film state is considered as the frozen bond waves; in
current, and so on; this is the positive-feedback process that provides the negative-resistance state (
Then two ways open. If the heating is strong and/or crystallization ability of a substance is high, the mostly active strings create the superheated region which then crystallizes with the formation of a low-resistant channel (
A unified approach for understanding photostructural changes and electrical switching in glassy semiconductors is proposed. This approach is based on the notions about self-organization and the model of bond wave, the latter being spatiotemporal correlation between elementary acts of bond exchange with participation of alternative bonding states. This approach/model gives opportunity to explain the peculiarities of the both phenomena and opens a new way for an effective management of underlaying processes by means of information fields.