Iron oxide nanoparticles were synthesized by precipitation method and supported on activated carbon. The catalyst thus obtained was characterized by various physicochemical techniques, and used for the liquid phase dehydrogenation/oxidation of octanol in a batch reactor at various temperatures in the range 30 °C - 60 °C. Maximum conversion of octanol to octanal was attained at 60 ° ;C in 30 min. However, with longer reaction time, the selectivity of the catalyst was found to change in favor of octene as a product. The catalyst could be recovered and reused multiple times without any decline in its catalytic performance.
The oxidation of alcohol is an important reaction which is used on industrial scale for the manufacture of chemicals [
An ideal oxidant for any large-scale oxidation reaction should be easily accessible, cheap and non-toxic. The best oxidant to fit this description is molecular oxygen [
If the stoichiometric oxidants are to be replaced by molecular oxygen, catalysts which are capable of activating molecular oxygen under mild reaction conditions and in solution phase are required. Noble metals can activate alcohols and molecular oxygen nearly at ambient conditions and produce the corresponding carbonyl compounds or carboxylic acids in high yields. The most commonly used catalysts consist of Pt or Pd as active components and Bi or Pb as promoters, on carbon and alumina supports. Ru and Rh are usually applied without promoters [
All the chemicals and reagents were of high purity grade (supplied by Scharlau, Spain) and used without any further purification. Nitrogen, oxygen and air were supplied by BOC Pakistan and further purified by specific filters (C.R.S.Inc.202268 & C.R.S.Inc.202223).
The crushed peanut shells were soaked in 50 weight % H3PO4 solution overnight at room temperature. The soaked sample was then loaded into a quartz tube and heated to 450˚C at a heating rate of 0.5˚C/min in tube furnace under nitrogen flow (40 mL/min) and then maintained at 450˚C for 60 min. The sample after cooling was washed in modified Soxhlet’s apparatus, and then dried. Finally, the sample was sieved through US standard sieve (80 and 100 Mesh).
0.5 M solution of ammonium hydroxide and 0.1 M solution of iron nitrate (cyclohexane/iron nitrate 100:0.25) were mixed in a 250 mL flask. Ammoniumhydroxide solution was added drop wise to iron nitrate solution while the resulting mixture was stirred vigorously. The mixture was then kept for 5 - 9 hours to allow for aging. Upon aging, the solution turned black indicating that iron oxide nanoparticles were formed. In the next step, 4.0 g of activated carbon was stirred with the solution of iron oxide nanoparticles in order to obtain 10 wt% iron oxide nanoparticles on activated carbon. The solution was filtered and the filter cake was dried at 70˚C overnight in an oven. Then it was calcined in muffle furnace by heating to 280˚C at a heating rate of 0.5˚C/min and then maintaining at the same temperature for 2 hours.
Catalytic activity of the catalyst was tested by carrying out the reaction in a three-necked batch reactor. 0.5 M aqueous solution of octanol (10 mL) and 100 mg catalyst was loaded into a reactor and sonicated at 60˚C in the presence of dry oxygen for 30 - 60 min. The reaction mixture was then analyzed by UV spectrophotometer (UV-1800, Shimadzu, Japan) by standard addition method, and GC (Clarus 580, PerkinElmer, USA) equipped with FID.
Iron oxide nanoparticles supported on activated carbon were characterized by SEM (JSM 5910, JEOL, Japan), XRD (X-ray diffractometer Rigaku D/Max-II, Cu tube, Japan), FTIR (Prestige 21 Shimadzu Japan in the range 500 - 4000 cm−1), and surface area and pore size analyzer (Quantachrome Nova 2200e, USA).
Iron oxide nanoparticles (8 - 15 nm) were supported on activated carbon having particle size of 149 - 177 µm (U.S. Mesh). FT-IR spectra reveal that the surface functional groups of activated carbon are: O-H, N-H (3100 - 3500 cm−1), C-H aromatic compound (3000 - 3100 cm−1), C-H aliphatic compound (2800 - 3000 cm−1), C=O and C-O (1640 - 1750 cm−1). FT-IR of iron oxide nanoparticles supported on activated carbon shows characteristic peaks for aliphatic phosphate stretch at 1050 cm−1 and 2300 cm−1 and for hematite at 470 cm−1 and 570 cm−1 as shown in
BET surface area of activated carbon is 1253.78 m2/g and pore volume is 0.71 cc/g while the surface area of iron oxide nanoparticles supported on activated carbon is 1235.67 m2/g and pore volume is 0.69 cc/g. The decrease in surface area results probably from the blockage of surface pores of activated carbon by iron oxide nano particles. XRD results of activated carbon, and iron oxide nanoparticles supported on activated carbon are shown in
To assess the activity of the catalyst, liquid phase dehydrogenation/oxidation of octanol to octanal was carried out in a batch reactor in the presence of the catalyst under conditions as depicted in Scheme 1.
The results obtained for the reaction carried out under various conditions are presented in
The experimental data reveals that the kinetics of dehydrogenation/oxidation of octanol to octanal over iron oxide nanoparticles supported on activated carbon follows Langmuir-Hinshelwood mechanism. Rates of dehydrogenation/oxidation of octanol at various partial pressures of oxygen were calculated and subjected to analysis through various equations to investigate whether the reaction is kinetically or diffusion controlled. A reaction is kinetically controlled when its activation energy is above 25 kJ/mol. Activation energy of 51.1 kJ/mol for the
Catalyst | Pressure (Torr) | Temperature (˚C) | Duration (minutes) | *Conversion (%) | Rate of reaction (% conv/g/min) | Selectivity (%) | |
---|---|---|---|---|---|---|---|
Octanal | Octene | ||||||
AC | 190 | 60 | 60 | 3.2 | 0.05 | 0 | 100 |
Fe2O3/AC | 38 76 114 152 190 | 60 | 60 | 15.7 39 55.5 78 97.5 | 0.26 0.65 0.925 1.30 1.62 | 100 100 98 95 85 | 0 0 2 5 15 |
152 | 30 40 50 60 | 60 | 36 45 55.2 78 | 0.6 0.75 0.92 1.30 | 100 100 98.5 95 | 0 0 1.5 5 | |
152 | 60 | 20 30 40 50 | 52.1 61.9 72.4 78 | 0.86 1.03 1.20 1.30 | 100 100 98 96.4 | 0 0 2 3.6 |
a) Reaction conditions: 10 mL of substrate solution, 0.1 g catalyst; b) *(calculated from remaining alcohol).
reaction in focus as calculated by using Arrhenius equation (
The Langmuir-Hinshelwood equation for weak molecular adsorption is
The experimental data when fitted into Equation (1) gave a sharp linearity, with a regression value of 0.997, as shown in
The data was then analyzed through L-H kinetic equation for the dissociative adsorption as given below:
The data when fitted into Equation (2) did not give a sharp trend as shown in
Equation (3) was not applicable to the experimental data, i.e., the data could not be fitted into Equation (3). Hence, we were led to conclude that the reaction proceeded with L-H mechanism for weak adsorption in comparison to L-H mechanism for dissociative adsorption.
The catalyst was recycled and reused several times to test its reusability and life span. After five successive runs, no decrease in the catalytic activity of the catalyst was found. The results of these trials are shown in
The catalytic activity of iron oxide nanoparticles supported on activated carbon was investigated for the liquid
phase oxidation of octanol to octanal under various reaction conditions. The catalyst showed maximum selectivity for octanal at lower temperature and lower partial pressure of oxygen. The optimal conditions for the desired conversion were found to be: reaction duration (60 min), partial pressure of oxygen (152 Torr), temperature (60˚C), catalyst (100 mg), and 0.5 M aqueous solution of substrate (10 mL). The kinetic studies showed that the reaction proceeded with first order kinetics, and followed Langmuir-Hinshelwood mechanism for weak molecular adsorption. To conclude, the catalyst has all the characteristics of being a truly heterogeneous one; it can be easily recovered by simple filtration and reused several times without loss of catalytic activity.