H. Abe, et al., “Study of HAZ Cracking of Hot-Dip Galvanizing Steel Bridge,” IIWDoc. IX-1974-94.

has been cited by the following article:

• TITLE: Effect of Zinc Galvanization on the Microstructure and Fracture Behavior of Low and Medium Carbon Structural Steels

  AUTHORS: Ignatius C. Okafor, Ronald J. O’Malley, Kaushal R. Prayakarao, Heshmat A. Aglan

  KEYWORDS: Galvanized Steel; Liquid Metal Embrittlement; Microstructure; Elemental Mapping; Fracture Resistance; etc.

  JOURNAL NAME: Engineering, Vol.5 No.8, August 6, 2013

  ABSTRACT: Microstructure and fracture behavior of ASTM 572 Grade 65 steels used for wind tower applications have been studied. Steels of two carbon level chemistries designed for this grade were used in the study. Fracture toughness of the steels was studied using 3-point bend test on samples coated with zinc and not coated with zinc. Lower carbon steel showed higher resistance to fracture than medium carbon steel after zinc galvanization. SEM study suggests that zinc and zinc bath additives that migrated to crack tips are responsible for the loss in ductility. The phenomenon of Liquid Metal Embrittlement (LME) is suggested to have taken place. Zinc bath additives traced at crack zones are suggested to have migrated at the zinc galvanizing temperatures.