• TITLE: Variable Temperature Laser Light Scattering Microscopy (VTLLSM) Studies on 10-100 μm Size High Purity Gold and Commercial Grade Zinc Grains

  AUTHORS: P. Sita Rama Rao, P. B. V. Prasad, P. B. Shashikanth

  KEYWORDS: Variable Temperature, Laser Light Scattering Microscopy, Au and Zn Grains, Defects

  JOURNAL NAME: Materials Sciences and Applications, Vol.1 No.6, December 29, 2010

  ABSTRACT: The VTLLS microscopy studies were made on high purity gold and commercial grade zinc grains in a temperature range of 30-230?C. Differential area ω and surface activity Sa were estimated from photomicrographs. The ω vs dT/dt (rate of heating) curve was seen to differ from those of silver and titanium. The nature of curve between normalized ω and dT/dt was seen to be non-exponential. The characteristic relation between sectorized differential area ωsec and mean temperature was examined. The present study further establishes the simplicity and versatility of the VTLLS technique, in studying the defect-sub-structure of metal particles such as Au and Zn in presence of an imposed temperature gradient in a reasonable way. As such an attempt was made to connect the ω and defect-sub-structure related parameters.