M. Abdel-Baki, F. El-Diasty and F. A. A. Wahab, “Optical Characterization of xTiO2-(60 ? x)SiO2-40Na2O Glasses: II. Absorption Edge, Fermi Level, Electronic Polarizability and Optical Basicity,” Optics Communications, Vol. 261, No. 1, 2006, pp. 65-70. doi:10.1016/j.optcom.2005.11.056

has been cited by the following article:

• TITLE: Spectroscopic Studies of 50Bi2O3-(50 - x)B2O3-xSm2O3 Glasses System

  AUTHORS: Suwat Rakpanich, Jakrapong Kaewkhao, Kittipun Boonin, Jeongmin Park, Hong Joo Kim, Pichet Limsuwan

  KEYWORDS: Samarium; Luminescence; Optical Properties; Density

  JOURNAL NAME: New Journal of Glass and Ceramics, Vol.3 No.1, January 29, 2013

  ABSTRACT: Sm3+ doped bismuth borate glasses of the composition (50 - x)B2O3:50Bi2O3:xSm2O3 (where x = 0.00, 0.50, 1.00, 1.50, 2.00 and 2.50 mol%) have been synthesized by conventional melt quenching technique. In order to understand the role of Sm2O3 inbismuth borate glasses, the density, the molar volume, the refractive index and the optical absorption were investigated. The results show that density, molar volume and refractive index of glasses increased with increasing Sm2O3 concentration. The increase of molar volume with Sm2O3 concentration is due to increase of non-bridging oxy- gen (NBOs) in the glass matrices. The optical absorption spectra were measured in the wavelength range 300 - 1100 nm and the optical band gaps were determined. It was found that the optical band gap decreased with the increase of Sm2O3 concentration. Moreover, the X-rays luminescence of Sm2O3 glasses samples were measured and shows emission band at 4G5/2→6H5/2 (569 nm),4G5/2→6H7/2 (598 nm),4G5/2→6H9/2 (641 nm) and4G5/2→6H11/2 (705 nm).