• TITLE: Corrosion Resistance of Heat-Treated NST 37-2 Steel in Hydrochloric Acid Solution

  AUTHORS: David Abimbola Fadare, Taiwo Gbolarumi Fadara

  KEYWORDS: Heat Treatment; Corrosion Resistance; Hydrochloric Acid; NST 37-2 Steel

  JOURNAL NAME: Journal of Minerals and Materials Characterization and Engineering, Vol.1 No.1, January 26, 2013

  ABSTRACT: Corrosion of metal components constitutes a major challenge in many engineering systems, with appropriate design, proper material selection, and heat treatment as commonly used control strategies. In this study, the corrosion behaviour of heat-treated (annealed, normalised, hardened, and tempered) NST 37-2 steel in three concentrations (1.0, 1.5 and 2.0 M) of hydrochloric acid solution was investigated using weight loss and electrode-potential methods. Results showed that corrosion rate increased with increase in acid concentration. The decreasing order of corrosion resistance was Tempered > Annealed > Normalised > Hardened > Untreated. The surface pictures of the heat-treated and untreated samples showed uniform and pitting corrosion with the latter becoming more pronounced as concentration increased.