• TITLE: Study on the Influence of Alkali Activator Solutions on Strength Improvement of Pozzolan Calcium Hydroxide Binders

  AUTHORS: Asson Sifueli Malisa, Duwa Hamisi Chengula

  KEYWORDS: Alkali Activated Materials, Natural Pozzolan, Calcium Hydroxide, Geopolymer Binders, Material Properties, Compressive Strength,

  JOURNAL NAME: Journal of Geoscience and Environment Protection, Vol.10 No.12, December 30, 2022

  ABSTRACT: Alkali activated binder, commonly known as geopolymer cement, has replaced Portland cement in the production of mortar and concrete globally over the past few years. The density, particle size distribution, and specific surface area (SSA) are important physical parameters affecting strength and durability of alkali activated binders. This study carried out tests for physical and chemical properties of the natural pozzolan and calcium hydroxide and then determines the influence of alkali solution (sodium silicate and sodium hydroxide) on strength development of natural pozzolan calcium hydroxide binders. The particle size distribution (PSD), relative densities (RD), and specific surface areas (SSA) of powder natural pozzolan and calcium hydroxide materials and for the mixture of natural pozzolan and calcium hydroxide were determined by using Blaine air permeability apparatus. The optimum proportion of 75% natural pozzolan and 25% calcium hydroxide was obtained which produces the compressive strength of 7.5 MPa at 28 days cured paste. The mixture of natural pozzolan and calcium hydroxide were further grinded at three different finenesses and the particle size gradation, specific densities, specific surface areas and mean particles sizes for the mixture were determined. The compressive strength of alkali activated binders increased with increasing curing period and fineness. The maximum compressive strength for 28 days cured specimens was 26.1 MPa which was obtained at a solution of 8 moles sodium hydroxide concentration. The test results showed that natural pozzolan materials can be used to make geopolymer binders for mortars and concretes. The geopolymer binders for mortars and concretes reduce green gas emission from cement factory but also it can be used to produce durable mortar and concrete with comparable strengths with mortars and concrete made from conventional Portland cement.