Dai, X.Y., Xia, C.Q. and Liu, C.B. (2006) The Effect of Sc for the Structure Properties of Al-Zn-Mg-Cu-Zr Alloy. Rare Metal Materials and Engineering, 35, 913-916.

has been cited by the following article:

• TITLE: Effect of Minor Cr Additions on Dispersed Phase and Properties of Al-Zn-Mg-Cu-Zr Alloys

  AUTHORS: Xingzhi Liao, Yanxi Li, Pengxuan Dong, Kanghua Chen

  KEYWORDS: Al-Zn-Mg-Cu-Zr Alloys, Chromium, Dispersed Phase, Property

  JOURNAL NAME: Journal of Materials Science and Chemical Engineering, Vol.8 No.2, January 22, 2020

  ABSTRACT: The influences of Cr on dispersed phase and properties of Al-Zn-Mg-Cu-Zr alloys were investigated by mechanical testing, slow strain rate stress corrosion, intergranular corrosion, combined with optical microscope, scanning electronic microscope, transmission electronic microscopy (OM, SEM, TEM). Research shows that: with the increase of element Cr, the recrystallization and grain growth had been inhibited, the strength, toughness and corrosion resistance of the alloy increased first and then decreased; when added 0.1 wt% Cr element, the properties of the alloy are the best. The main reasons of that were as below: when added 0.1 wt% Cr element, (Al,Cr)3(Zr,Yb) appeared, that cohered with the matrix. When added 0.18 wt% Cr element, (Al,Cr)3(Zr,Yb) and Al18Mg3Cr2 had been found, making adverse effects on alloys. This work studied the effect of Cr content on recrystallization and grain growth in order to get a new super high strength aluminum alloy.