Ren, J., Fu, H., Ren, T. and Yuan, W. (2009) Preparation, Characterization and Properties of Binary and Ternary Blends with Thermoplastic Starch, Poly(lactic acid) and Poly(butylene adipate-co-terephthalate). Carbohydrate Polymers, 77, 576-582.
https://doi.org/10.1016/j.carbpol.2009.01.024

has been cited by the following article:

• TITLE: Porous Electrospun Nanofiber from Biomass-Based Polyester Blends of Polylactic Acid and Polybutylene Succinate

  AUTHORS: Manisara Phiriyawirut, Kanokwan Sarapat, Sutasinee Sirima, Anrasee Prasertchol

  KEYWORDS: Electrospinning, Polymer Blend, PLA, PBS, Nanofiber

  JOURNAL NAME: Open Journal of Polymer Chemistry, Vol.9 No.1, February 2, 2019

  ABSTRACT: We studied the electrospinning process of the blend of polylactic acid (PLA) and polybutylene succinate (PBS). The blend PLA/PBS ratio 95/5, 90/10, 85/15 and 80/20 wt% were prepared by dissolved in mixture of solvent between dichloromethane (DCM) and N, N-dimethylformamide (DMF) at ratio 3/1. The suitable condition for electrospun of the blend was 17% wt concentration, 16 kV and 18 cm projection distance. The round fiber with pore on the surface was observed. Increasing content of PBS in the blend impact to the diameter of fibril decreased from 1350, 1290, 1210 and 1170 nm, respectively; while the pore on the surface changes from circle to oval shape. Regarding the thermal properties, blending of PBS increases the glass transition temperature (Tg) of PLA without affect to the melting temperature (Tm) of the electrospun nanofibers. The best tensile properties of PLA/PBS nanofibers were achieved at blend ratio of 95/5, and Young’s modulus is increased comparing to those of the pure electrospun fibers.