Lang, Y.J., Zhou, G.X., Hou, L.G., Zhang J.S. and Zhuang, L.Z. (2015) Significantly Enhanced the Ductility of the Fine-Grained Al-Zn-Mg-Cu Alloy by Strain-Induced Precipitation. Materials and Design, 88, 625-631.
https://doi.org/10.1016/j.matdes.2015.09.023

has been cited by the following article:

• TITLE: Texture/Microstructural Evolution and Mechanical Properties of a Hot and Cold Rolled Al-Mg-Si-Cu Alloy

  AUTHORS: Yihan Wang, Lixin Zhang, Xiaohui Yang, Kai Li, Song Ni, Yong Du, Min Song

  KEYWORDS: EBSD, Microstructure, Texture Evolution, Mechanical Properties, ODFs

  JOURNAL NAME: Journal of Minerals and Materials Characterization and Engineering, Vol.5 No.4, July 7, 2017

  ABSTRACT: The evolutions of texture, microstructure as well as mechanical properties of an Al-Mg-Si-Cu alloy during hot and cold rolling were investigated by TEM, EBSD and X-ray diffraction in this study. The results revealed that formation of sub-grain boundaries and //RD fiber texture after hot rolling is beneficial to the increase of the elongation of the alloy. The shear texture of //RD fiber and γ-fiber occupies a dominant role during the hot rolling process, while the main texture during the cold rolling process is the rolling texture of β-fiber. β-fiber and τ-fiber texture components are identified as two main types of texture components during cold rolling, and the Brass component {011} is transformed into Goss component {011} with the increase of the deformation.