S. Singhal, S. K. Barthwal, and K. Chandra, “Preparation and characterization of nanosize nickel-substituted cobalt ferrites (Co1?xNixFe2O4),” Journal of Solid State Chemistry, Vol. 178, pp. 3183–3189, October 2005.

has been cited by the following article:

• TITLE: Cation Distribution in Lithium Ferrite (LiFe5O8) Prepared via Aerosol Route

  AUTHORS: Sonal Singhal, Kailash Chandra

  KEYWORDS: Nano Particles, Saturation Magnetization, Coercivity, X-Ray Diffraction, Mössbauer Spectra

  JOURNAL NAME: Journal of Electromagnetic Analysis and Applications, Vol.2 No.1, January 28, 2010

  ABSTRACT: Nano size lithium ferrite was prepared through aerosol route and characterized using TEM, XRD, magnetic measurements and Mössbauer spectroscopy. The particle size of as obtained samples were found to be ~10 nm through TEM, that increases upto ~80 nm on annealing at 1200 oC. The unit cell parameter ‘a’ calculated using XRD, confirms the formation of ?-LiFe5O8. Room temperature Mössbauer spectra of as obtained sample of all the ferrites exhibited broad doublet suggesting super paramagnetic nature. This doublet further resolved into two doublets and assigned to the surface region atoms and internal region atoms of the particles. The annealed samples (1200 oC) show broad sextets, which were fitted with two sextets indicating different local environment of both tetrahedrally and octahedrally coordinated Fe-cation. Cation distribution obtained from the X-ray, magnetic and Mössbauer data confirms that the three fifth of the iron atom goes in to the octahedral site.