Olaseinde, O.A., Cornish, L.A., Merwe, J.V. and Olubambi, P.A. (2011) Electrochemical Behaviour of 2101 DSS with Ruthenium and 316 SS. The Proceedings of the 18th International Corrosion Congress, Perth, 1541-1548.

has been cited by the following article:

• TITLE: Effect of Ceramic Powder Coatings on Low Carbon Steel

  AUTHORS: Oluwatoyin Adenike Olaseinde, Benjamin Omotayo Adewuyi

  KEYWORDS: Steel, Corrosion, Coating, Ceramic

  JOURNAL NAME: Materials Sciences and Applications, Vol.7 No.5, May 5, 2016

  ABSTRACT: Effect of ceramic powder coating on low carbon steel samples was presented. Electrostatic deposition method was used to produce ceramic coatings on low carbon steels. The coatings were fabricated over a range of temperatures (100℃- 400℃). Detailed investigation on the corrosion behaviour, the hardness property and electrode potential of the fabricated and uncoated samples are reported. The ceramic materials used are locally available in Ondo-State Nigeria. The coating temperatures affect the rate of corrosion, the hardness property and the electrical resistivity of the coated steel sample. The sample coated at 300℃ with ceramic powder Y showed the best corrosion resistance in 0.5 M NaCl solution. The highest resistivity occurred in the sample coated at 300℃with ceramic powder Z. All the samples coated with ceramic powder Y had better corrosion resistance in 0.5 M NaCl than the one coated by sample Z.