Calogero, G., Di Marco, G., Cazzanti, S., Caramori, S., Argazzi, R., Di Carlo, A. and Alberto Bignozzi, C. (2010) Efficient Dye-Sensitized Solar Cells Using Red Turnip and Purple Wild Sicilian Prickly Pear Fruits. International Journal of Molecular Sciences, 11, 254-267.
http://dx.doi.org/10.3390/ijms11010254

has been cited by the following article:

• TITLE: The Effect of Electrolyte on Dye Sensitized Solar Cells Using Natural Dye from Mango (M. indica L.) Leaf as Sensitizer

  AUTHORS: T. J. Abodunrin, O. Obafemi, A. O. Boyo, T. Adebayo, R. Jimoh

  KEYWORDS: Dye-Sensitized Solar Cells, Dye Sensitizer, Electrolytes, M. indica L., Photocurrent Density, Fill Factor

  JOURNAL NAME: Advances in Materials Physics and Chemistry, Vol.5 No.6, June 16, 2015

  ABSTRACT: Dye-sensitized solar cells (DSSC) were fabricated with mango leaf dye extracts as natural dye sensitizers at pH value of 5.20 and temperature of 18.1°C. Methanol was used as dye-extracting solvent. DSSCs from dye extract of M. indica L. with KMnO4 electrolyte had the highest photocurrent density of 1.3 mA/cm2 and fill factor FF of 0.46 for the sun at its peak. Potassium permanganate (KMnO4) had a photocurrent density of 1.3 mA/cm2 and FF of 0.8 at sundown. Potassium Iodide (KI), Potassium Bromide (KBr) and Mercury Chloride (HgCl2) electrolytes had 0.2 mA/cm2, 0.08 mA/cm2 and 0.02 mA/cm2 photocurrent densities respectively. The fill factors of 0.09, 0.03 and 0.003 respectively for sun overhead while 0.08 mA/cm2, 0.01 mA/cm2 and 0.01 mA/cm2 were the values of photocurrent densities respectively at sundown. The fill factors were 0.02, 0.0006 and 0.003 respectively at sundown. The maximum power Pmax of the DSSCs were 0.5 mW/cm2, 0.10 mW/cm2, 0.01 mW/cm2 and 0.012 mW/cm2 respectively at 1300 h at 1630 h 0.9 mW/cm2, 0.14 mW/cm2, 0.005 mW/cm2 and 0.0015 mW/cm2 respectively.