Tsujikawa, S., Ishihara, Y. and Shinohara, T. (1993) Failure Analysis of Stress Corrosion Cracking of Type 304 Steel Tubing for Hot-Water Use in Kusatsu Town, Gunma Prefecture. Zairyo-to-Kankyo, 42, 20-26.
https://doi.org/10.3323/jcorr1991.42.20

has been cited by the following article:

• TITLE: Corrosion in Tap Water and Hot Water Supply Facilities of Stainless Steel Type 304 Pipes

  AUTHORS: Noriyuki Tanaka, Shigeru Sato, Ippei Watanabe, Yutaka Yamada, Osamu Sakurada

  KEYWORDS: Stainless Steel, Corrosion Resistance, Tap water, Residual Chlorine, Corrosion Potential

  JOURNAL NAME: Materials Sciences and Applications, Vol.9 No.1, January 10, 2018

  ABSTRACT: We performed corrosion case study and corrosion tests to assess the corrosion resistance of stainless steel type 304 pipes in tap water and hot water facilities. Circulating test equipment used for corrosion tests and two types of sample, plates and straight pipe specimens, were examined under different conditions of residual chlorine concentration in the test water. The results of case study analysis indicated that high degrees of pitting corrosion occurred on straight pipes with inner diameter