Yuan, Y., Yin, Y.T., Yu, D.D., Lin, H.D., Wang, J., Tang, B., et al. (2016) Effects of Compound Coupling Agents on the Properties of PTFE/SiO2 Microwave Composites. Journal of Materials Science: Ma-terials in Electronics, 28, 3356-3363. https://doi.org/10.1007/s10854-016-5929-8

has been cited by the following article:

• TITLE: Effects of Content of Chopped Glass Fibers on the Properties of Silica Filled PTFE Composites

  AUTHORS: Ying Yuan, Haodong Lin, Zehua Jiang, Zhifeng Chi, Minghao Yao, Shuren Zhang

  KEYWORDS: Polymers, Composite Materials, PTFE, Dielectric Properties, E-Glass Fiber

  JOURNAL NAME: Journal of Materials Science and Chemical Engineering, Vol.5 No.7, July 7, 2017

  ABSTRACT: In this work, the polytetrafluoroethylene (PTFE)-based composite substrates were manufactured by mixing, calendering, hot-pressing sintering. The composition of all the samples was PTFE, SiO2 and chopped E-glass fibers. The effects of content of E-glass fibers on the properties of the SiO2 filled PTFE composites were investigated, including density, water absorption, dielectric properties (εr, tanδ), coefficient of thermal expansion (CTE) and temperature coefficient of dielectric constant (τε). The compositions of inorganic materials mixture are (62 ? x) % SiO2 + x % E-glass fiber (x: mass ratio to composites, x = 0, 1, 1.5, 2, 2.5, 3). The results show that as the content of E-glass fibers is 2.5 wt.%, this composite obtains optimal properties, including excellent dielectric properties (εr~2.9123, tanδ~0.0011), acceptable water absorption of 0.075%, temperature coefficient of dielectric constant of 10 ppm/?C and coefficient of thermal expansion of 15.87 ppm/?C.