TITLE:
Evaluation of Mechanical and Microstructural Properties of α-Brass Alloy Produced from Scrap Copper and Zinc Metal through Sand Casting Process
AUTHORS:
Edward E. Igelegbai, Oluwaseun A. Alo, Adefemi O. Adeodu, Ilesanmi A. Daniyan
KEYWORDS:
Alloys, Alpha-Brass, Etching, Metallographic, Sand Casting
JOURNAL NAME:
Journal of Minerals and Materials Characterization and Engineering,
Vol.5 No.1,
December
20,
2016
ABSTRACT: Cu-Zn alloy (Brass) is widely used as an industrial material because of its excellent characteristics such as high corrosion resistance, non-magnetism and good forging ability. This paper evaluates the mechanical and microstructure properties of α-brass alloy gotten from scrap copper and zinc metal, and compares the properties with normal α-brass billets. Five different compositions of the α-brass alloy (Cu-5%Zn, Cu-10%Zn, Cu-15%Zn, Cu-20%Zn, Cu-30%Zn) were produced from scraps of copper wire and zinc batteries casing respectively by method of sand casting. The parts of the cast rods were machined to a specification of 60 mm × 100 mm × 300 mm on a lathe to obtain tensile test specimens. After homogenization annealing, the samples were heated in an electric furnace at 500℃ for 3 hours. The samples were etched with ferric chloride solution for 20 seconds and sent for metallographic examination. The result of the hardness test shows variation in hardness of the cast Cu-Zn alloys with increasing zinc content. The ductility and elongation of the α-brass decrease with increasing zinc content. The colouration of the α-brass changed from red to yellow as the zinc content increases. In conclusion, hard brass can be obtained from recycled Cu and Zn as compared to normal brass billets.