El Mehdi, B., Mernari, B., Traisnel, M., Bentiss, F. and Lagrenee, M. (2003) Synthesis and Comparative Study of the Inhibitive Effect of Some New Triazole Derivatives towards Corrosion of Mild Steel in Hydrochloric Acid Solution. Materials Chemistry and Physics, 77, 489-496.
http://dx.doi.org/10.1016/S0254-0584(02)00085-8

has been cited by the following article:

• TITLE: Investigate the Corrosion Inhibition of Mild Steel in Sulfuric Acid Solution by Thiosemicarbazide

  AUTHORS: Fatma Mohamed Mahgoub, S. M. Al-Rashdi

  KEYWORDS: Acidic Medium, Adsorption, Inhibitor Mild Steel and SEM

  JOURNAL NAME: Open Journal of Physical Chemistry, Vol.6 No.3, July 20, 2016

  ABSTRACT: Corrosion inhibition of mild steel in 0.5 mol/L H2SO4 was investigated in the absence and presence of different concentrations of thiosemicarbazide. The inhibition efficiency of thiosemicarbazide was studied by electrochemical impedance methods, potentiodynamic polarization and scanning electron microscopy at different inhibitor concentrations. Inhibition efficiency, corrosion rate and surface coverage were evaluated at different concentrations of thiosemicarbazide. Electrochemical impedance plots indicated that the presence of the inhibitors increased the charge transfer resistance of the corrosion process, increasing the inhibition efficiency. Polarization curves showed that this compound acted as mixed type inhibitor. The results of the investigation showed that this compound had good inhibiting properties for mild steel corrosion in 0.5 M sulfuric acid. The adsorption isotherm studies showed that Thiosemicarbazide adsorbed chemisorbed and formed a stable surface complex on the mild steel surface. And Langmuir obeyed the adsorption isotherm. Scanning electron microscopy analysis shows that, the surface morphology of the polished mild steel in the presence of thiosemicarbazide as inhibitor is smoother surface as compared with polished mild steel specimen in the absence of inhibitor.