Guilemany, J., Fernández, J., Delgado, J., Benedetti, A. and Climent, F. (2002) Effects of Thickness Coating on the Electrochemical Behaviour of Thermal Spray Cr3C2-NiCr Coatings. Surface and Coatings Technology, 153, 107-113. http://dx.doi.org/10.1016/S0257-8972(01)01679-6

has been cited by the following article:

• TITLE: Effect of Ceramic Powder Coatings on Low Carbon Steel

  AUTHORS: Oluwatoyin Adenike Olaseinde, Benjamin Omotayo Adewuyi

  KEYWORDS: Steel, Corrosion, Coating, Ceramic

  JOURNAL NAME: Materials Sciences and Applications, Vol.7 No.5, May 5, 2016

  ABSTRACT: Effect of ceramic powder coating on low carbon steel samples was presented. Electrostatic deposition method was used to produce ceramic coatings on low carbon steels. The coatings were fabricated over a range of temperatures (100℃- 400℃). Detailed investigation on the corrosion behaviour, the hardness property and electrode potential of the fabricated and uncoated samples are reported. The ceramic materials used are locally available in Ondo-State Nigeria. The coating temperatures affect the rate of corrosion, the hardness property and the electrical resistivity of the coated steel sample. The sample coated at 300℃ with ceramic powder Y showed the best corrosion resistance in 0.5 M NaCl solution. The highest resistivity occurred in the sample coated at 300℃with ceramic powder Z. All the samples coated with ceramic powder Y had better corrosion resistance in 0.5 M NaCl than the one coated by sample Z.