Mohamed, W.A., Rateb, N.M. andShakour, A.A. (2004) Performance of Copper Corrosion Inhibitors in a Museum Environment—A Comparative Study Using FTIR Spectroscopy. Metal 04: Proceedings of the International Conference on Metals Conservation, Canberra, 4-8 October 2004, 369-378.

has been cited by the following article:

• TITLE: Investigation of Aloe lateritia Gel as Corrosion Inhibitor for Mild Steel in 2 M HNO3 and 1 M H2SO4 Media

  AUTHORS: Lucas Paul, Revocatus L. Machunda

  KEYWORDS: Corrosion Inhibitor, Mild Steel, Potentiodynamic Polarization, Sulfuric Acid, Nitric Acid

  JOURNAL NAME: Journal of Minerals and Materials Characterization and Engineering, Vol.4 No.1, January 18, 2016

  ABSTRACT: Corrsion inhibition of Aloe lateritia gel for Mild steel in 2 M HNO3 and 1 M H2SO4 solutions was investigated by potentiodynamic polarization, Scanning electron microscopy (SEM) and Foutier transform infrared (FT-IR). Inhibition efficiency increased with the increase of the concentration of the gel. The optimal concentration of the gel gives maximum inhibition efficiency of 77.4% and 70.3% in 1 M H2SO4 and 2 M HNO3 respectively. Polarization plots shows that, the gel works as a mixed type inhibitor altering both cathodic and anodic reaction. SEM proves the uniform and pitting corrosion at the surface of Mild steel in 1 M H2SO4 and 2 M HNO3 respectively. Using FT-IR potential function groups from pure gel and some stretch shift was observed from corrosion product and some stretch shift from corrosion products was observed.