Zheng, Z., Huang, X.C., Li, Y., Yang, N.C, Wang, X.L. and Shi, M.W. (2012) Influence Factors of Internal Structure and Interfacial Compatibility of UHMWPE Fiber/SEBS Resin Composites: Processing Parameters, Structure of Fiber and Nature of Resin. Composites Part B, 43, 1538-1544.
http://dx.doi.org/10.1016/j.compositesb.2011.11.011

has been cited by the following article:

• TITLE: Study on the Properties of UHMW-PE Film

  AUTHORS: Zhongyan Du, Jihu Wang, Shaoguo Wen, Pengzhu Wang, Dongdong Zhang, Changle Yin

  KEYWORDS: UHMW-PE Film, Surface Modification, Surface Resistance, Contact Angle

  JOURNAL NAME: Advances in Materials Physics and Chemistry, Vol.5 No.8, August 21, 2015

  ABSTRACT: Some physicochemical properties of UHMW-PE film such as gas permeability, tensile strength, and corrosion resistance in acid with different immersion time, various concentrations and various solutions and rattler testing were studied. The obtained results showed that the values of gas permeability, tensile strength, elongation at break, and the temperature of dissociation at weight loss 5% was 546.57 cm3·m﹣2·24 h·0.1 MPa, 37.22 MPa, 368.00%, 360°C, respectively. In different concentration acid, the surface resistance of film accumulated to some extent with immersion time increasing, together with that the higher acid concentration was, the lower the surface resistance of film was. Moreover, the contact angle of films gradually increased with the acid concentration decreasing and the increase of immersion time. After wear testing, the mass of UHMW-PE film did not nearly change, while the contact angle became larger with the number of turning increasing and the value was more than 90°.