Synthesis and Characterization of Ag Nanoparticles Addition on BPSCCO Superconducting Thin Films ()
Received 10 January 2016; accepted 13 February 2016; published 16 February 2016
1. Introduction
Since the discovery of Bi-based superconducting systems, a tremendous amount of work concerning preparation, superconducting properties, and the structure of these compounds has been carried out [1] [2] ; a variety of potential applications of bulk materials as well as thin films in a number of cryoelectronic devices [3] - [5] have been reported. The BSCCO system mainly contains three phases in the general formula Bi2Sr2CanCun+1Oy (where n = 0, 1 and 2 refers to the number of CuO2 layers which yields 10, 85, 110 K transition temperatures, respectively) which commonly have a multiphase structure. Although it is difficult to obtain pure high Tc phase Bi-2223, it is still one of the important materials that have been investigated extensively.
Several physical and chemical techniques such as pulsed laser deposition (PLD), molecular beam epitaxy, R. F. sputtering, co-evaporation, spray pyrolysis technique and chemical vapor deposition (CVD) have been used to prepare superconducting thin films. The PLD method is known to be suitable for fabricating films with complex stoichiometry and become a potential method of fabricating high quality superconducting thin films suitable for electronic applications such as in Josephson junction based electronics and the second generation coated conductors. A significant effort has been done by researchers [5] -[8] to improve the critical temperature for textured and epitaxial HTSc films and the potential applications of thin films.
Recently, the effect of nano addition has been extensively studied to improve the superconducting properties such as nanoelements: (Ag, Au, etc.), nanooxides (SnO2, ZrO2, MgO, etc.) [9] and nanocompound: (NiFe2O4, BiFeO3, etc.) [10] . I. H. Gul et al. [11] studied the effect Ag2CO3 addition (0 - 25 wt%) on the Bi1.6Pb0.4Sr2Ca2Cu3O10 +δ (Bi-2223) and found the critical current density for the 25 wt% Ag doped samples increased by three times compared to the undoped sample. W. Abdeen, et al. [12] found that increasing the addition of nano-Ag up to x = 1.5 wt% enhanced the phase formation and improved the superconducting transition temperature and the critical current density Jc. R. Mawassi et al. [13] studied the effect of Ag nanoparticles addition on the superconducting properties of (Bi, Pb)-2223 phase. They found that the electrical and granular properties were greatly enhanced, indicating more efficient pinning mechanisms. An improvement of the critical current density of 229% was obtained with x = 0.6 wt% while the superconducting transition temperature is improved by 2.5%.
In this work, thin films of Bi (Pb)-Sr-Ca-Cu-O with Ag nanoparticles addition were post-annealed. The influence of optimal processing parameters on the formation of the superconducting single-phase (2223) oxide thin film in the Bi-based system was investigated. The samples were characterized by SEM, AFM, XRD and electrical resistance measurement.
2. Materials and Methods
Samples of Bi1.7Pb0.3Sr2Ca2Cu3O10 +δ with and without an addition of Ag nanoparticles were prepared by a conventional solid state reaction method. The stoichiometric amounts of high purity powders (99.999%) of Bi2O3, Pb3O4, Sr(NO3)2, CaO and CuO, Ag nanoparticles were added by weight percentages (0.0, 0.2, 0.4, 0.6, 0.8 and 1.0 weight %). The powders were mixed together by using of mill machine (SPEX Industries Inc.-USA), for a period of (10) minute followed by manually grinding of powder using agate mortar and pestle for a (15) minute, The mixture homogenization takes place by adding a sufficient quantity of 2-propanol to form a paste during the process of grinding for about 30 minutes. The mixture was grounded to a fine powder and then calcined in air by using a tube furnace at 810˚C for 24 h with a rate of 2˚C/min. The mixture then pressed into pellets of diameter 13 mm and thickness (2 - 3) mm by using hydraulic press type (SPECAC) under a pressure of 0.7 GPa. The pellets were sintered at 845˚C for 140 hr. These pellets were used as a target. BPSCCO target before and after addition of Ag nanoparticles was entered in vacuum chamber 10−2 mbar, and Q-switched Nd:YaG pulse laser operated at 1064 nm wavelength, 500 mJ/pulse, the distance between substrate and target 2 cm and 700 mJ pulse energy for frequency 5 Hz. All samples were grown at an optimal p-type Si (111) substrate at room temperature. The as-deposited thin films were annealed in a tube furnace under 2 lit/min oxygen flow at 800˚C for 1.5 h with heating and cooling rate of 5˚C/min. Resistance-temperature data were obtained by using four point probe DC method at a temperature range (77 - 300) K to determine the critical temperature (Tc). All samples were subjected to gross structural characterization by X-ray diffraction (XRD) (Shimadzu-6000, with Cu-Kα source). A computer program was used to calculate the lattice parameters, based on Cohen’s least square method. The surface morphology of the samples was carried out by scanning electron microscopy (SEM) performed by (FEI Co. system SN: 9922650-2013/Holland) and atomic force microscopy (AFM) type origin USA Model (AA300- CSPM).
3. Results and Discussion
X-ray diffraction pattern of samples with Ag nanoparticles addition (x = 0.0, 0.2, 0.4, 0.6, 0.8 and 1.0) are shown in Figure 1. It is more suitable for pointing out the presence of both Bi (Pb)-2223 and Bi (Pb)-2212 phases with Bi (Pb)-2223 being the dominant phase. To estimate the volume fraction of the present phases, we used the corresponding Bi-2212 and Bi-2223 peaks, in the following formulas [14] [15] :
![]()
Figure 1. X-Ray diffraction patterns of (Bi, Pb)-2223 thin films for different Ag nanoparticles addition.
Due to the annealing treatment of the films a crystalline order was established and an improvement of the films morphology, optimization of oxygen content and a change of the phase composition of the films have been obtained. It can be noticed that all films are well crystallized having an orthorhombic phase with c-axis oriented perpendicular to the film surface. The thermal treatment allows uniform diffusion Bi (Pb)-2223 materials on Si (111) substrate forming smoother films. With increasing Ag nanoparticles addition to 1.0 w% a slight angular shift and sharpness of some peaks such as H (004), H (0012), and H (220) have been noticed. This may attribute to the change in the oxygen content of the films. Such behavior was also obtained by Ishii et al. [9] and Ahmed [14] .
Thermal treatment of the films leads to facilitate growth, flattening, and density the material that produced much thinner films. The lattice constant of thin films was calculated using (hkl) values of the strong peaks in the XRD patterns with the aid of Bragg’s law. Increasing nano-Ag to x = 1.0 wt% slightly enhanced the lattice parameters. The length may be expanded or contracted with the change of the electrons into antibonding orbital. Indeed, the behavior of the lattice constant may attribute to the displacement of Ag ions inside the structure. The variations of lattice parameters indicate the intercalation of oxygen species. This change of a and c effect on the volume of the unit cell and then causes variation of the density. It can be observed that the density value of the prepared films increases with the decreasing of (V). The increase in volume (V) is attributed to a larger number of Cu-O layers in the unit cell with the addition of Ag nanoparticles. The lattice parameters, unit cell volumes and the ratio c/a for the prepared films are listed in Table 1.
The critical temperature measurement performed by four-probe resistance measurement. The dimensions of films were about: thickness (t) 190 ± 5 nm, the width of films (b) 1 cm and the distance between two probe points (d) 29.272 × 10−6 m. The value of the current flow in films is 1 mA. So the final equation for films resistivity is:
Figure 2 show typical electrical resistance versus temperature relationships of the films with different nano-Ag addition. The electrical resistance initially decreases with decreasing temperature and then rapidly drops for a further decrease in the temperature, achieving zero resistance at the critical transition temperature. All
![]()
Table 1. Lattice parameters and unit cell volumes of the prepared thin films with different Ag nanoparticles addition.
![]()
Figure 2. ρ-T plots for pure and Ag nanoparticles added Bi1.7 Pb0.3Sr2Ca2Cu3O10 thin film samples.
films show superconducting behavior and the transition temperature for the films has increased with increasing nano-Ag addition to x = 1.0 wt% except for x = 0.6 wt% which shows Tc less than 100 K as listed in Table 2, the transition from normal to superconducting state is not sharp, this may be attributed to the oxygen concentration fluctuation in grains, and the presence of inhomogeneity in the oxidation state of grains. The critical temperature of Bi-2223 materials is very much dependent on the oxygen concentration, it is interesting to notice that the resulting inhomogeneity in oxygen concentration would lead to variations in the structural parameters, such result was also obtained by Mua et al. [5] .
The superconducting transition width (ΔT) is equal to (Tc-T0), this small value is defined as the measure of the quality or purity of the sample. Because of the existence of percolate paths which shortens out the current [13] . Thus, it can be notice that the value of ΔT for all samples increases with the increasing of nano-Ag addition, especially for the sample x = 1.0 wt% which showed the highest value of the critical temperature, while the sample x = 0.6 wt% shows the lowest values of ΔT and Tc, Figure 3 illustrate the relation between the critical temperature and the nano-Ag addition concentration. The thickness of the thin film samples could have the effect on the results of the critical temperature, grains size and growth of the film because if a crystal has its wide planar c- axis of the surface in contact with another surface (e.g. silver substrate, secondary phases, free surface or another BSCCO crystal), it can reduce the surface energy with the potential for so adhere to the surface. This mechanism, presented to the system with planar constraints, such as a 2212-Ag film, will result in a textured sample, depending on the thickness of the superconducting layer [5] .
To clarify that Ag nanoparticles plays an important role in enhancement the Bi (Pb)-2223 phase for thin film samples, also for checking the differences in the surface morphologies of the film, the surface morphology of different films was carried out by using AFM and SEM measurements, as shown in Figure 4, when bombing bulk samples for various additions of nano-Ag by PLD, the number of pulses applied to the metal target is 500 pulse. These samples show a clear feature of islands growth and nano-holes forming trenches between the growth islands, i.e. this mode may be correlated to the existence of clusters in the plasma [3] [16] , it is attributed to the different epitaxial growth modes with strong chemical bonds or weak physical interactions with Si (111). However, ex-situ films nucleation follows a Volmer-Weber mechanism of growth, adatom-adatom interactions
![]()
Table 2. Critical temperature transition width for different Ag nanoparticles addition thin films.
![]()
Figure 3. Ag nanoparticles concentration versus critical temperature Tc for all thin films.
![]()
Figure 4. AFM surface images of Bi (Pb)-2223 phase for different Ag nanoparticles addition, films were grown at 800˚C on Si (111) substrate.
are stronger than those of the adatom with the surface, leading to the formation of three-dimensional (3D) adatom clusters or islands [16] and after lateral grain growth and coalescence low angle grain boundaries remain which follow a zone improvement plan process leading to continuously reconstructed films, these results were in good agreement with that obtained by Obradors et al. [17] , and Vitug et al. [18] .
Characteristic of AFM for all films is the island structure, with an island diameter of typically 200 - 600 nm, separated by deep trenches consisting of nano-size holes, which can be clearly visualized under high magnification SEM as well. Moreover, a fluctuate of average surface roughness (RA) and root mean square (RMS) values can be observed in Table 3, adding Ag nanoparticles to the compound resulted in small size of the average diameter, reduction of the structural defects (twin boundaries, terrace breadth, and stacking faults) and chemical imperfections such as oxygen deficiencies inside the grains.
The SEM micrographs of the cross-sectional view for Bi1.7Pb0.3Sr2Ca2Cu3O10 and nano-Ag added films are shown in Figure 5. Superconducting grains are seen to be strongly connected with each other and the surface morphology of the films comprises of platelets and layered. The platelet-type features with some improvement to the grain alignment of samples are found in Ag nanoparticles added films which resulting the distribution of grains become uniform and homogenous microstructure, increasing the nano-Ag addition to x = 1% wt increases
![]()
Table 3. Average surface roughness, root mean square, and average diameter values for all films.
![]()
Figure 5. SEM micrographs of (Bi, Pb)-2223 phase for different Ag nanoparticles addition films.
the formation of randomly bigger platelet grains size on the surface (compact platelets), forms of needle (or rod) and flowers were also observed, this may be able to establish connectivity between grains. Therefore, the increase in Tc with the appropriate nano-Ag addition in the sample is associated with the enhancement of Bi (Pb)- 2223 phase formation, and form dense regions which improved links between grains.
Morphology of samples from SEM revealed that adding a noble element (Ag nanoparticle) is refers to advantage and promote in treatment and accelerated of Bi (Pb)-2223 grain phase formation in these samples. The difference in the grain size and the distribution of grains on the surface of the samples indicate the influence of replacing of Ag1+ and Pb2+ together for Bi-2223 on the morphology of the samples. The SEM image of high concentration such as 1.0 wt% of the nano-Ag specimen shows large size grains with thin plate-like and needle-like structures. These grain structures were aligned to make more dense and conductive sample. This result is in good agreement with the results obtained by Ahmed [14] .
4. Conclusion
This paper reports on the effects of Ag nanoparticle addition on the superconducting properties of Bi1.7Pb0.3Sr2Ca2Cu3O10 superconductor thin films that had been prepared via conventional PLD method by using high superconductor materials. 0.0 - 1.0 wt% of nano-Ag was added, by introducing nanoparticle within the structures of the films; the value of volume fraction, as well as Tc could be increased. The highest volume fraction of the Bi (Pb)-2223 phase 66.15% and the best value for Tc of 103.5 K have been obtained from the sample with 1.0 wt% addition as against 100 K for the non-added samples. The XRD pattern shows that the addition of nanoparticle does not change the crystallographic structure of the samples and remain in the orthorhombic unit cell.