Effect of Refining Parameters on Medium Density Fibreboard (MDF) Properties from Oil Palm Trunk

Zawawi Ibrahim, Astimar Abdul Aziz, Ridzuan Ramli, Anis Mokhtar, SiJoon Lee

.
Engineering & Processing Division, Malaysian Palm Oil Board, Selangor, Malaysia;.

DOI: 10.4236/ojcm.2013.34013                

Abstract

The properties of medium density fibreboard (MDF) made from oil palm trunk (OPT) as affected by refining pressure and preheating time were investigated. The OPT chips were refined in the MDF pilot plant by using four refining pressures (2, 4, 6 and 8 bar) and four different preheating time (100, 200, 300 and 400 seconds). The refined fibres were blended with 10% of urea formaldehyde with a board target density of 720 kg/m³. MDF boards were evaluated based on European Standard EN 622-5:2006 for thickness swelling (TS), internal bonding (IB), modulus of rupture (MOR) and modulus of elasticity (MOE). Analysis of variance (ANOVA) was used to analyze the significance of the factors. The results from this study indicated that refining pressure and preheating time are significant factors for all MDF properties. Low refining pressure and preheating time produced higher TS, lower MOR and MOE with poor bonding than those boards prepared from fibres refined at higher refining pressure and longer preheating time. OPT fibre treated with 8 bar produced good swelling resistance but detrimental on mechanical properties of the finish board. 6 bar steam pressure offered the highest value of mechanical properties (MOE, MOR and IB). Boards from intermediate refining condition (6 bar and 300 seconds) were found the better board properties having 14.58%, 0.73 N/mm², 38 N/mm² and 3597 N/mm² for TS, IB, MOR and MOE respectively.

Keywords

Oil Palm Trunk; Medium Density Fibreboard; Refining Pressure; Preheating Time

Conflicts of Interest

The authors declare no conflicts of interest.

References

[1]	MPOB, “Malaysian Oil Palm Statistics 2012,” 32nd Edition, Malaysia Palm Oil Board, Ministry of Plantation & Commodities, Kajang, 2013.
[2]	S. Sumathi, S. P. Chai and A. R. Mohamed, “Utilization of Oil Palm as a Source of Renewable Energy in Malaysia,” Renewable & Sustainable Energy Reviews, Vol. 12, No. 9, 2008, pp. 2404-2421. http://dx.doi.org/10.1016/j.rser.2007.06.006
[3]	M. Z. Alam, A. A. Mamun, I. Y. Qudsieh, S. A. Muyibi, H. M. Salleh and N. M. Omar, “Solid State Bioconversion of Oil Palm Empty Fruit Bunches for Cellulose Enzyme Production Using a Rotary Drum Bioreactor,” Biochemical Engineering Journal, Vol. 46, No. 1, 2009, pp. 61-64.
[4]	R. Hashim, L. S. How, R. N. Kumar and O. Sulaiman, “Some of the Properties of Flame Retardant Medium Density Fibreboard Made from Rubberwood and Recycled Containers Containing Aluminium Trihydroxide,” Bioresource Technology, Vol. 96, No. 16, 2005, pp. 1826-1831. http://dx.doi.org/10.1016/j.biortech.2005.01.023
[5]	M. Jawaid, H. P. S. Abdul Khalil, K. P. Noorunisa and A. Abu Bakar, “Hybrid Composites Made from Oil Palm Empty Fruit Bunches/Jute Fibres: Water Absortion, Thickness Swelling and Density Behaviour,” Journal of Polymers and the Environment, Vol. 19, No. 1, 2010, pp. 106-109.
[6]	C. Xing, S. Wang and G. M. Pharr, “Nanoindention of Juvenile and Mature Loblolly Pine (Pinus taeda L.) Wood Fibres as Affected by Thermomechanical Refining Pressure,” Wood Science and Technology, Vol. 43, 2009, 615-625.
[7]	D. Krug and E. Kehr, “Influence of High Pulping Pressures on Permanent Swelling-Tempered Medium Density Fibreboard,” Holz als Rohund Werkstoff, Vol. 59, 2001, pp. 342-343.
[8]	E. Roffael, B. Dix and T. Schneider, “Thermomechanical (TMP) and Chemo-Thermomechanical Pulps (CTMP) for Medium Density Fibreboard (MDF),” Holzforschung, Vol. 55, No. 2, 2001, pp. 214-218.
[9]	L. H. Groom, L. Mott and S. M. Shaler, “Relationship between Fibre Furnish Properties and the Structural Performance of MDF,” 33rd International Particleboard/ Composite Materials Symposium Proceedings, Washington State University, Pullman, Washington DC, 13-15 April 1999, pp. 89-100.
[10]	N. Laemsak and M. Okuma, “Development of Boards Made from Oil Palm Frond II: Properties of Binderless Boards from Steam-Exploded Fibers of Oil Palm Frond,” Journal Wood Science, Vol. 46, No. 4, 2000, pp. 322-326. http://dx.doi.org/10.1007/BF00766224
[11]	Z. Gao, X. Wang, H. Wan and G. Brunette, “Binderless Panels Made with Black Spruce Bark,” BioResources, Vol. 6, No. 4, 2011, pp. 3960-3972.
[12]	Anon, “BS EN 622-5:2006. European Standard Fibre-boards Specifications. Part 5. Requirements for Dry Process Boards (MDF),” CEN (European Committee for Standardization), London, 2006.
[13]	J. Xu, R. Widyorini, H. Yamauchi and S. Kawai, “Development of Binderless Fibreboard from Kenaf Core,” Journal of Wood Science, Vol. 52, No. 3, 2006, pp. 236-243. http://dx.doi.org/10.1007/s10086-005-0770-3
[14]	C. Xing, S. Wang and G. M. Pharr, “Nanoindention of Juvenile and Mature Loblolly Pine (Pinus taeda L.) Wood Fibres as Affected by Thermomechanical Refining Pressure,” Wood Science and Technology, Vol. 43, No. 7-8, 2009, pp. 615-625. http://dx.doi.org/10.1007/s00226-009-0266-1
[15]	C. Xing, J. Deng, S. Y. Zhang, B. Riedl and A. Cloutier, “Properties of MDF from Black Spruce Tops as Affected by Thermomechanical Refining Conditions,” Holz als Rohund Werkstoff, Vol. 64, No. 6, 2006, pp. 507-512.
[16]	J. A. Velasquez, F. Ferrando and J. Salvado, “Binderless Fibreboard from Steam Exploded Miscanthus sinensis: The Effect of Grinding Process,” Holz als Rohund Werkstoff, Vol. 60, No. 4, 2002, pp. 297-302.
[17]	J. Xu, G. Han and S. Kawai, “Development of Binderless Particleboard from Kenaf Core Using Sream-Injection Pressing,” Journal of Wood Science, Vol. 49, No. 4, 2003, pp. 327-332. http://dx.doi.org/10.1007/s10086-002-0485-7
[18]	H. E. Hsu, W. Schwald and J. A. Shields, “Chemical and Physical Changes Required for Producing Dimensionally Stable Wood-Based Composites,” Wood Science and Technology, Vol. 22, No. 3, 1988, pp. 281-289. http://dx.doi.org/10.1007/BF00386023
[19]	H. Okamoto, S. Sano, S. Kawai, T. Okamoto and H. Sasaki, “Production of Dimensionally Stable Medium Density Fibreboard by Use of High Pressure Steam Pressing,” Mokuzai Gakkaishi, Vol. 40, No. 4, 1994, pp. 380-389.
[20]	H. A. Aisyah, M. T. Paridah, M. H. Sahri, A. A. Astimar and U. M. K. Anwar, “Properties of Medium Density Fibreboard (MDF) from Kenaf (Hibiscus cannabinus L.) Core as Function of Refining Conditions,” Composite Part B, Vol. 44, No. 1, 2013, pp. 592-596.
[21]	D. Hull and T. W. Clyne, “An Introduction to Composite Materials,” Cambridge University Press, Cambridge, 1996. http://dx.doi.org/10.1017/CBO9781139170130
[22]	N. Ayrilmis, “Effect of Tree Species on Technological Properties of Medium Density Fibreboard,” M.Sc. Thesis, Institute of Natural Science, Istanbul University, Fatih/ Istanbul, 2000.
[23]	C. Xing, S. Wang, G. M. Pharr and L. H. Groom, “Effect of Thermo-Mechanical Refining Pressure on the Properties of Wood Fibers as Measured by Nano-indentation and Atomic Force Microscopy,” Holzforschung, Vol. 62, No. 2, 2008, pp. 230-236.