Evaluation of Reaction Mechanism for Photocatalytic Degradation of Dye with Self-Sensitized TiO 2 under Visible Light Irradiation

The dye-sensitized TiO2 method is one of the most promising methods for the visible-light-induced detoxification of pollutants. The reaction mechanism for photocatalytic degradation of orange II (OII) and rhodamine B (RhB) with self-sensitized TiO2 under visible light irradiation (λ > 400 nm) has been evaluated. Radical scavenger studies were carried out to investigate the active species involved in the photodegradation of 5 mg/L of initial concentration of OII and RhB at room temperature. The trapping effects of different scavengers results proved that the oxidation of OII and RhB mainly occurred by the direct oxidization of h and • 2 O − radicals, while the OH radicals played only a relatively minor role in the direct oxidization process.


Introduction
The dye-sensitization technique has been reported as an innovative technology that could play an important role in developing efficient and cost-effective semiconductor photocatalyst in the near future [1].It can extend the light absorption range, enhance photon harvesting efficiency, provide extra excited electron pairs from a dye and accelerate charge transfer, leading to a high efficiency of photoe-Open Journal of Inorganic Non-metallic Materials lectric conversion [2].The photo-sensitized mechanism of the dye-adsorbed TiO 2 under the visible light illumination can be simply expressed as follow: (1) the adsorbed dye is effectively excited to generate the electron/hole pair by the light illumination because of its narrower band gap in comparison with TiO 2 and (2) the photo-excited electrons are injected from the lowest unoccupied molecular orbital (LUMO) of adsorbed dyes into the conduction band (CB) of TiO 2 [3] [4] [5] [6].Park et al. [7] reported that the dye-sensitization can be applied for the self-degradation of dyes.Shang et al. [8] studied the photocatalytic degradation of rhodamine B by dye-sensitized TiO 2 under visible-light irradiation.The present study is intended to investigate the photocatalytic degradation reaction mechanism of orange II (OII) and rhodamine B (RhB) with self-sensitized TiO 2 under the visible light irradiation (λ > 400 nm) and the possible mechanism is discussed based on radical trapping experiments.

Chemicals and Materials
All reagents were of analytical grade and were used without further purification.
Orange II and rhodamine B used in this study were purchased from Nacalai Tesque.Ascorbic acid (AA), ammonium oxalate (AO) and t-butyl alcohol (TBA) were obtained from Wako Pure Chemicals.P-25 TiO 2 was purchased from Degussa Co. Ltd.Ultrapure water (18 MΩ cm) was prepared by an ultrapure water system (Advantec MFS Inc.).

Photocatalytic Activity and Detection of Reactive Oxygen Species
The photocatalytic activities of TiO 2 were evaluated by the degradation of OII and RhB under visible light irradiation at ambient temperature.Typically, 30 mL of dye solution and 20 mg of photocatalyst were added to a 35 mL Pyrex glass cell.The initial concentration of dye in all experiments was 5 mg/L and the appropriate quantity of the photocatalyst powder was magnetically stirred before and during irradiation.Before irradiation, the photocatalyst suspension con- O − radical scavenger).Different quantity of t-butyl alcohol, di-ammonium oxalate monohydrate [9] and ascorbic acid [10] were added into the dye solution prior to addition of catalysts.

Radical Scavenger Studies on TiO2 Using OII
To determine the possible degradation mechanism of Orange II by TiO 2 , different scavengers were introduced to quench the relevant active species.In this study, t-butyl alcohol (TBA), di-ammonium oxalate monohydrate (AO) and ascorbic acid (AA) were adopted to be the scavengers of hydroxyl radicals ( • OH), superoxide O − ) and holes (h + ), respectively.As shown in Figure 1, the photocatalytic degradation efficiency of OII (5 mg/L) with TiO 2 was about 100% after 6 h under visible light irradiation.The photodegradation of OII over the TiO 2 was affected slightly by the addition of TBA, demonstrating that • OH active species played a small role in the photocatalytic degradation of OII.However, the photocatalytic degradation efficiency of OII decreases significantly in the presence of AA, which indicates that • 2 O − is an important active species in the process of OII degradation.In addition, the photocatalytic activity of the TiO 2 was completely suppressed by AO, suggesting that h + can be also involved in the process of OII degradation.

Radical Scavenger Studies on TiO2 Using RhB
In order to investigate the active species involved in photodegrading RhB, scavenger studies were also carried out on TiO 2 .As shown in Figure 2, photocatalytic degradation of RhB over TiO 2 was retarded with the presence of di-ammonium oxalate monohydrate (AO) and ascorbic acid (AA).The results strongly indicated that h + , and   mainly via photogenerated holes, not via hydroxyl radical [12].Therefore, the presence of holes scavenger has decreased the most the photocatalytic degradation of RhB.The presence of TBA had little effect on the decolorization rate, indicating that RhB was almost not degraded by • OH.O O − is -0.33 V vs NHE [15], which is less negative than conduction band potential of TiO 2 (-0.5 V vs NHE) [16].

Reaction Mechanism
Under visible light irradiation, a dye sensitized mechanism has been depicted in Figure 3 O − radical reacts with adsorbed dye to degrade it.The holes in the HOMO react with adsorbed OH − species to form • OH radical.However, the formation channel to • OH is minor under visible right [17], which is similar with the result shown in Figure 1 and

( )
Dye visible light dye e h Adsorbed dye e h TiO TiO e dye h ( )

Conclusion
The radical scavenger studies were carried out to investigate the active species involved in the photodegradation of orange II and rhodamine B with self-sensitized TiO 2 under the visible light irradiation (λ > 400 nm).Investigation of the photocatalytic mechanism showed that the TiO 2 self-sensitized degradation of OII and RhB under visible-light irradiation could be mainly attributed to the direct oxidization by h + and • 2 O − radicals, while the • OH radicals played only a relatively minor role in the direct oxidization process.The present work may provide deep insight into the photosensitization induced photocatalytic mechanism, and also offer new opportunities for their industrial application in the elimination of dye pollutants from wastewater.
taining dye was allowed to equilibrate for 30 min in the dark.The sample solution was irradiated with a LED lamp (TOSHIBA LDA14L-G/100W) in conjunction with a UV cut filter (Y-44, HOYA), which was positioned on the side of the reaction cell.The luminous intensity was measured by a UV radio meter (UD-400, TOPCON TECHNOHOUSE Co., Japan).The light intensity of the LED lamp after the filter was 5.3 mW/cm 2 .After the desired irradiation time, TiO 2 was separated through the 0.45 μm Advantec membrane filter.The TiO 2 powder could be almost removed by the filtration.The absorbance of the remnant dye was measured using a UV-visible spectrometry (UV-1650PC, SHIMADZU Co., Tokyo, Japan).The relative concentration (C/C 0 ) of the OII solution was calculated by the relative absorbance (A/A 0 ) at 485 nm according to Beer-Lambert law.A 0 and A are the absorbance of the OII solution at the beginning time (t 0 ) of Open Journal of Inorganic Non-metallic Materials visible light irradiation and at time t, respectively.C 0 and C are the concentrations of OII at the beginning of visible light irradiation and at time t, respectively.The photodegradation of RhB (5 mg/L) was similar to that of OII except that the detection wavelength was 554 nm.Radical scavenger studies were carried out to investigate the active species involved in the photodegradation of dye.The scavenging experiments of reactive oxygen species were similar to the photodegradation experiments.Three scavengers were selected, namely, t-butyl alcohol ( • OH radical scavenger), di-ammonium oxalate monohydrate (hole scavenger) and ascorbic acid ( • 2

• 2 O 2 O 2 O
photocatalytic degradation of MB was contributed by the photosensitizing of RhB toward TiO 2 .The electron ejected from HOMO to conduction band of TiO 2 could have been utilized for the reduction of surface adsorbed oxygen to produced • 2 O − [11].The photocatalytic degradation of RhB was retarded most significantly with the presence of AO, conveying that oxidation reaction occurred

Figure 1 .
Figure 1.Effects of different radical scavengers on OII degradation in presence of TiO 2 under visible light Irradiation.

Figure 2 .
Figure 2. Effects of different radical scavengers on RhB degradation in presence of TiO 2 under visible light irradiation.

Figure 3 (
Figure 3(a) demonstrates the valence band (VB) and conduction band (CB) levels and the band gap energy of orange II and rhodamine B and TiO 2 vs NHE reference electrodes.The energy bands of rhodamine B, orange II and TiO 2

Figure 3 . 2 O 2 O
Figure 3. Schematic (a) energy level diagram of TiO 2 with respect to potential of • 2 2 O O − and the HOMO-LUMO levels of dye and (b) mechanisms of self-sensitized TiO 2 reaction of superoxide radical ( ) • 2 O − and holes (h + ) formation under visible light

2 O
(b).Upon irradiation of visible light, a dye absorbs the light to create an electron and hole in the conduction and valence bands (LUMO and HOMO) Open Journal of Inorganic Non-metallic Materials of the dye[17].The electron in the LUMO then transfers to the CB of TiO 2 .The adsorbed molecular oxygen on the catalyst captures electron from the CB of TiO 2 to form • − .The oxidant ( )• 2

Figure 2 .• 2 O
Accordingto the results of the radical scavengers, OII and RhB were attacked by the super oxides, − and holes, h + for the degradation of dye.A possible degradation reaction mechanism is described below.