Development of a New Bio-Based Insulating Fluid from Jatropha curcas Oil for Power Transformers

Abstract

The present work aims to develop a new vegetable insulating fluid for power transformers based on Jatropha curcas oil. Besides its technical benefits, Jatropha curcas oil has a socio-economic role by promoting income to rural families, contributing to the countryside development and avoiding rural exodus. Thus, the entire transformer oil production (extraction, processing, characterization and accelerated aging) was covered and a new process was developed. For oil extraction, the most suitable process was the solvent extraction (5 mL of hexane per gram of crushed non-peeled seeds during 30 minutes) with an oil yield of 32%. In raw oil processing stage, the degumming, with 0.4 g of phosphoric acid per 100 g of oil, at 70°C, was used to remove phosphatides. Then, free fatty acids were 96% neutralized with a sodium hydroxide solution (0.5% w/w) at room temperature. For the oil clarification, the combination of 5% w/woil of activated carbon and 1% w/woil of MgO resulted in a bright, odorless and clear oil with an acid number of 0.04 mgKOH·g1. The oil drying in a vacuum rotary evaporator, at 70°C, for 2 hours reduced the water content to 177 ppm. The processed oil was characterized following ASTM D6871 methods. This oil presented higher dielectric breakdown voltage (55 kV) than commercial transformer fluids (BIOTEMP®, EnvirotempFR3®, and Bivolt®), which increases transformer safety, capacity and lifetime. In addition, the processed oil has a lower viscosity than BIOTEMP® fluid, which can enhance the heat dissipation efficiency in the transformer. Moreover, the processed oil flash and fire points of 310°C and >340°C, respectively, confirm the great security of vegetable insulating fluids. The analyzed properties of the processed oil fulfill all the ASTM D6871, ABNT NBR 15422 and IEC 62770 specifications. Therefore, Jatropha curcas oil is a potential substitute formineral insulating fluids.

Share and Cite:

Evangelista Jr., J. , Coelho, F. , Carvalho, J. , Araújo, E. , Miranda, T. and Salum, A. (2017) Development of a New Bio-Based Insulating Fluid from Jatropha curcas Oil for Power Transformers. Advances in Chemical Engineering and Science, 7, 235-255. doi: 10.4236/aces.2017.72018.

1. Introduction

Nowadays, the constant search for sustainable economic development demands the rational use of resources and energy, including investment on renewable materials and greener processes [1] . In the electrical sector, this reality requires increasing the efficiency and safety in the generation and distribution of electricity. Thus, the concern about safety, reliability and performance of insulation materials used in power transformers has raised considerably [2] [3] [4] .

Mineral oils have been used for over a hundred years in power transformers to ensure electrical insulation and cooling. However, these oils are mainly obtained from petroleum products, a non-renewable resource that involves various political and socio-economic issues. In the last half of the last century, synthetic hydrocarbon fluids, silicone, and ester fluids were introduced, but, at that time, their use was limited [5] . Furthermore, mineral oils are non-biodegradable, high flammable (due its low flash point) and dangerous for the environment, since spills from leaks and equipment failure can contaminate the water and the soil [4] [6] [7] .

In this context, the development of alternative fluids has received great attention, especially vegetable insulating oils, produced from renewable sources. Comparing to mineral oils, bio-based oils are considered eco-friendly, since they are completely biodegradable, non-toxic and free of PCB (polychlorinated biphenyl), which simplifies the leaking protection and the further disposal. In addition, the higher flash and fire points (both greater than 300°C), compared to mineral oils, make the vegetable oils extremely safe, being classified as a Less-Flammable Dielectric Liquid, which requires no fire mitigation system and prevents the costly replacements caused by fires. Therefore, vegetable insulating fluids are not considered dangerous by international authorities such as Environmental Protection Agency (EPA) and Occupational Safety and Health Administration (OSHA) [5] [6] [8] [9] [10] [11] [12] .

Vegetable oils present higher dielectric breakdown compared to mineral oils, providing better insulation characteristics. In addition, these oils are not corrosive to copper and increase the insulation life of Kraft paper, since they present ability to absorb moisture of the paper and protect cellulose from thermal aging. Considering all these properties, vegetable oils can increase the transformer overloading capability, its performance, its useful life (about 40% higher), and can decrease its rates of failure. Its use requires no or just minor modifications and it is compatible with the existing electric power infrastructure [2] [5] [6] [13] [14] .

Considering the reasons discussed above, in the recent years, the use of insulating vegetable oils, in electrical transformers, is growing extensively. Currently, over 300,000 distribution transformers using vegetable oil are in service. Moreover, there are, globally, approximately 200 power transformers up to 200 MVA and 242 kV being energized and operating with bio-based fluids [10] . In 2006, one of the most important Brazilian energy provider company, Energy Company of Minas Gerais (CEMIG) has developed with ABB Brasil (Asea Brown Boveri), a global technology company in power and automation, the world’s first 145 kV power transformer, insulated by a vegetable oil. Since then, this and other transformers are operating normally, with a cost reduction of approximately 20% [15] . In 2014, Siemens has produced the world's first largescale transformer, at the 420 kV extra-high voltage level, that uses vegetable oil insulation instead of mineral oils. Thus, no fire, explosion or water hazard classification must be issued. As a result, this transformer can be installed and operated in densely populated areas or in zones subject to stringent environmental protection restrictions, like water conservation areas [10] .

Nevertheless, vegetable oils have some disadvantages, like higher viscosity and lower oxidative stability, when compared to mineral oils. Additionally, their price is subject to significant oscillation caused by the food market, since, generally, the feedstock is also used in edible oils [6] [16] . In this context, Jatropha curcas oil points out as a potential source for a new vegetable insulating fluid because of some beneficial characteristics over commercial fluids available. The oil has a low viscosity value and is non-edible, which avoids the food market competition [8] [17] .

Jatropha curcasis an arboreal plant of rapid growth, which belongs to the Euphorbiaceae family, with height ranging from 3 to 5 m. Studies suggest its origins in tropical America where it was taken by Portuguese navigators to other tropical parts of the world [8] [18] [19] . Jatropha curcas seeds, which weights from 0.5 to 0.8 g, usually have 33% to 45% of shells and 55 to 66% of albumen. In these seeds, it can be found 7% of water, between 28% and 38% of oil and 55% of sugar, starch, albuminoids and mineral materials [17] . Studies show that the annual plant productivity, in spacing 3 × 3, can reach 3 to 4 t of oil per hectare [18] . The plant has several applications: in traditional medicine, soap produc- tion, lighting lamps, electric generators, fuel for stoves, insecticide and, because it has high nitrogen content, organic fertilizer [20] .

Jatropha curcas oil price does not compete on the food market, since the plant is non-edible and is not used for food and animal feeding [20] . The reason for this is that the plant contains a class of toxins known as phorbol esters, which concentration in the seeds depends on the soil and climatic conditions. Accord- ing to Ahmed and Salimon [21] , most part of phorbol esters present in the crude oil can be extracted with methanol before its processing. The same authors showed that the influence of degumming and deodorization was low, whereas the steps of neutralization and clarification (bleaching) led to significant reduction of phorbol esters. There is no study on negative influence of phorbol esters on the performance of vegetable insulating fluid and this issue was not addressed in this paper. The plant geographical distribution is quite wide due to its hardiness, resistance to long droughts, pests and diseases, and adaptable to climate change. It grows well in dry tropics areas and in humid equatorial areas and can withstand long periods of drought [22] . Therefore, Jatropha curcas is considered an agricultural alternative to arid and semi-arid regions, being used to recover degraded areas. In addition, this plant has a socio-economic rule by promoting adequate income to rural families (from the sale of seeds oil) and contributes to the countryside development, avoiding rural exodus.

Despite this potential, few works [8] [11] have addressed the use of Jatropha curcas oil as insulating fluids for power transformers. None of them covers the entire production process (extraction, processing and characterization). The existing works focus theirstudies onthe characterization of specific properties and there is no concern about the industrial oil production process.

In this context, the objective of this work was to develop a new bio-based insulating fluid based on Jatropha curcasoil, for power transformers use, since the oil obtained after its processing presents a lower viscosity than commercial vegetable fluids available associated to a low acid number and a high dielectric breakdown value, besides the advantages already cited. Therefore, the whole production route (extraction and processing) was developed aiming an industrial production. In addition, the processed oil and a commercial fluid, BIOTEMP®, were characterized and compared according to the American Society for Testing and Materials (ASTM) standard (ASTM D6871) requirements for new insulating vegetable oils.

2. Materials and Methods

Jatropha curcasseeds were obtained from a local Brazilian producer. Initially, they were separated into two groups: non-peeled seeds and peeled seeds. Both of these materials were dried in an oven, at temperatures between 60˚C and 80˚C, until the obtainment of constant mass. Then, the extraction step was carried out (mechanical extraction, Sohxlet extraction or solvent extraction by direct contact). The extracted oils were processed in four steps: degumming, neutralization, clarification and drying. The oils were characterized before and after processing.

2.1. Extraction

The peeled seeds were subjected to mechanical extraction and the resulting press cakes were subjected to chemical extraction by using a Soxhlet or by direct contact with hexane, as shown in Figure 1(a). For the non-peeled seeds, two routes were used: extraction by direct contact with solvent or mechanical extraction followed by Soxhlet extraction, as shown in Figure 1(b). The study to find the more appropriate conditions for oil extraction by direct contact with solvent from non-peeled seeds cake was not done because the oil content in this material is lower than peeled-seeds cake. In the extraction assays, it was used the best conditions found for the oil extraction from the peeled-seeds cake, which contains much more oil. After each extraction, for the separation of the obtained oils, vacuum filtration was carried out.

To evaluate the efficiency of the extraction processes, the percent yield was calculated as the ratio of the mass of oil obtained to the mass of seeds (non- peeled or peeled) used for the extraction, multiplied by 100.

The Jatropha curcas non-peeled and peeled seeds, as well as its seeds shells and crushed non-peeled seeds are shown in Figure 2.

2.1.1. Mechanical Extraction

The oils from dried Jatropha curcas non-peeled seeds and peeled seeds were extracted using a 15 t manual hydraulic press SIWA model CHARLOTT and the produced oils were filtered under vacuum.

(a) (b)

Figure 1.Oil extraction process from (a) peeled seeds and (b) non-peeled seeds.

Figure 2. Jatropha curcas. (a) non-peeled seeds; (b) peeled seeds; (c) shells; (d) crushed non-peeled seeds.

2.1.2. Soxhlet Extraction

To evaluate the amount of oil remaining in the cakes (non-peeled seeds and peeled seeds) resulting from the mechanical extraction, these cakes were crushed and contacted with hexane (4 mL per gram of solid) in the Soxhlet Oil and Grazes Extractor (Marconi MA004/8/50) at 80˚C, for two hours. Then, the solvent was recovered in a rotary evaporator at 80˚C under vacuum and the obtained oils were kept in an oven at 80˚C until constant mass.

2.1.3. Direct Solvent Extraction

Industrial plants usually combine mechanical and solvent extraction processes to extract oil from seeds [23] . Thus, in this work, the peeled seeds cake, which was mechanically extracted in the press (Figure 1(a)), was crushed and then mixed with hexane in a reactor at 25˚C ± 3˚C. Further, the mixture was filtered and the solvent recovered in a rotary evaporator at 80˚C, both under vacuum. The influence of the amount of hexane (2, 5 and 10 mL per gram of solid) used and of the contact time (5, 10, 15, 30 and 60 minutes) in the yield was studied and the obtained oils were characterized.

Extraction by direct contact with hexane was also carried out for the crushed non-peeled seeds (5 mL per gram of solid), for 30 minutes, at 25˚C ± 3˚C. These seeds were not previously subjected to mechanical extraction (Figure 1(b)). Then, the obtained oils were characterized.

To evaluate the efficiency of the extraction processes, the percent yield was calculated as the ratio between the mass of oil obtained and the mass of seeds (non-peeled or peeled) used for the extraction, multiplied by 100.

2.2. Processing

The initial methods applied in the crude oil processing were based on the standard industrial refining of vegetable edible oils [23] [24] . Afterwards, some adaptations to these methods were done in order to adjust Jatropha curcas oil properties to the ASTM D6871 standard requirements.

2.2.1. Degumming

The crude oil obtained from the extractions is mixed with other substances such as gums, phosphatides and proteins that are oil insoluble when hydrated. In order to remove them, the crude oil obtained from non-peeled seeds by direct contact extraction with the solvent, without previous mechanical extraction, was mixed with phosphoric acid (85 wt%), in a proportion of 0.4 g of this acid to 100 g of oil, at 70˚C for 10 minutes. Then, hot water was added and mixed for 10 more minutes. Finally, the mixture was centrifuged for phase separation, the aqueous whitish bottom phase, containing part of the before mentioned substances, being discarded.

2.2.2. Neutralization

In general, vegetable oils are constituted by triacylglycerol molecules, whose hydrolysis produces free fatty acids, which are responsible for the increase of the acidity of these oils. For this reason, these acids must be neutralized and removed.

The neutralization of free fatty acids was carried out by two different ways (alkali and dry neutralizations), according to Table 5 and Table 6.

In the first one, the oil, previously adjusted to the temperature test (90˚C), was vigorously mixed, for 30 minutes, with three different alkali solutions, NaOH, NaHCO3, and Na2CO3, with the same concentration (10% w/w), containing phenolphthalein. Afterwards, other experiments were carried out with NaOH 0.5 and 5.0% w/w, at 90˚C and NaOH 0.5% w/w, at room temperature (25˚C ± 3˚C), all containing phenolphthalein. The addition of each of these solutions to the oil was done until the mixture oil/solution turned into a pink coloration. Then, it was taken to a decanter funnel for removal of part of the alkaline solution. The material in the funnel was washed with water at 90˚C and the supernatant was centrifuged for the removal of the rest of the alkaline solution and of the soap that was formed.

Dry neutralization, by using an absorbent, was also tested. Initially, the alkali-impregnated solid was prepared. For each gram of solid, 2 g of NaOH was dissolved in methanol, as suggested by Filleti [25] . The amount of added solvent was the amount needed for solubilization of the alkali. Then, this solution was mixed with the solid adsorbent (activated carbon or silica gel). Next, the mixture was dried in an oven until complete removal of the solvent. After this, the degummed oil was mixed to 0.25 grams of alkali-impregnated solid per gram of oil, for 30 minutes, at 70˚C. Finally, the mixture was filtered under vacuum.

However, the use of activated carbon is preferable because the silica gel preparation was more complex. In addition, methanol is a reagent with a high toxicity. Thus, new experiments were carried out using water as solvent and activated carbon as absorbent solid. Different proportions of NaOH (1 and 2 g∙g−1solid) and solid (0.25 and 0.5 g∙g−1oil) were studied.

2.2.3. Clarification

In order to deodorize and remove pigments, soap, and other impurities, the clarification is commonly applied in edible oil refining [26] . Concerning the neutralized Jatropha curcas oil, which was very bright and odorless, but with an acidity number above the ASTM standard limit, the clarification was designed to remove impurities and, simultaneously, the remaining free fatty acids. Therefore, a series of tests were carried out by mixing the oil, in a proportion of 5 g of an specific solid (activated carbon, activated carbon impregnated with NaOH, silica gel, CaCO3, Na2CO3 or MgO) per 100 g of oil, for 30 minutes, at 90˚C, under vacuum. A mixture containing 5 g of activated carbon and 1 g of MgO for 100 g of oil was also evaluated. Finally, the clarified oil was filtered under vacuum with quantitative filter paper to remove the solids. After measuring the acid number of the resulting oils, the oil with lower acidity had its absorbance of yellow and red colors measured in order to evaluate the effectiveness of the clarification process in reducing the oil color. The measures were done using the UV-Visible Spectrophotometer Carry 50 (Varian).

2.2.4. Drying

The insulating vegetable oils are less susceptible to moisture than mineral oils [6] [27] ; however, the ASTM D6871 standard requires a maximum water content of 200 ppm. It is also known that vegetable oils are susceptible to degradation under oxygen and high temperatures which can lead to the production of free fatty acids, increasing the oil acid number [4] [7] [28] . Therefore, the oil drying should remove the water without increasing its acidity.

In this context, it was studied two oil processes: drying in an oven at 120˚C and in a rotary evaporator at 70˚C. A lower temperature was used in the second process since it was done under vacuum. In both processes, two times were evaluated: two and four hours.

2.3. Characterization

The characterization of the various obtained raw and processed Jatropha curcasoils, and the commercial oil, BIOTEMP®, was carried out according to ASTM D6871, for new natural (vegetable oil) ester fluids used in electrical apparatus [29] . It is also available, in the literature, specifications and test methods for unused natural esters in transformers from the International Electrotechnical Commission, the IEC 62770:2013, [30] . In Brazil, the standard ABNT NBR 15422, which is based on ASTM D6871 and IEC 62770:2013, establishes the requirements for new vegetable insulating oils [31] . ABNT stands for the Brazilian standards association, Associação Brasileira de Normas Técnicas. In Table 1, it can be seen a summary of the three standards used for vegetable transformer oils.

Table 1. Summary of the three standards for vegetable transformer oils.

For the flash and fire points determination, it was used the Cleveland Open Cup Tester (Hipperquímica). The kinematic viscosity was evaluated using the automatic Cannon Fenske viscometer (SCHOT CT52) and the dynamic viscosity was measured by using the rheometer AR-G2 (TA Instruments). Additionally, the dielectric breakdown measurement equipment RDT 06A (Electric Test Serta) was applied to measure this property. The water content was determined by the Karl-Fisher method, by using the apparatus Q349 (Quimis). The fatty acids content was determined by using the Gas Chromatograph HP5890 (Agilent) with the column SP-2380 (Supelco), following the ASTM standards D1983 and D2800. The coefficient of expansion and specific heat were measured following the ASTM standards D1903 and D2766, respectively. For the latter, the Differential Scanning Calorimeter DSC-60A (Shimadzu) was used.

2.4. Accelerated Aging

In electric power transformers, the insulating fluids can be submitted to extreme stress conditions, as high temperatures. It is know that the thermal stress combined with oxygen degrade the triglycerides and produce free fatty acids, which increase the oil acid number [4] [7] [28] [32] .

In this context, accelerating aging tests were done in order to evaluate the stability of the processed Jatropha curcas oil without antioxidants, and with 1% and 2% w/woil of tert-butylhydroquinone (TBHQ). This antioxidant is considered, in general, more effective than butylated hydroxyanisole (BHA) and butylated hydroxytoluene (BHT), other commonly antioxidants used in vegetable oils [33] . TBHQ is moderately soluble in oils and fats, and do not complexes with iron or copper. Tests with BHA and BHT were performed but the results were worst to the obtained with TBHQ in avoiding oxidation. Thus, these results will not be shown in this paper.

In the accelerated aging assays, 500 mL of each oils tested (around 500 mL) were added to erlenmeyer with 16 grams of Kraft paper and two meters of copper wire (1 mm diameter) shaped as a coil of one centimeter of diameter. Next, the systems were kept at 140˚C in a silicon oil bath for 5 days. Pneumatic compressors were used to bubble air in the oils inside the erlenmeyers, with a flow rate of 2 L∙min−1. The acid number, kinematic viscosities and fatty acids profile were measured of each one of the oils tested before and after aging.

2.5. Materials

For direct solvent extraction and Soxhlet extraction, reagent grade hexane was used. In the oil processing and characterization stages, the following analytical grade reagents from Synth, Merck and Sigma-Aldrich were used: sodium hydroxide, potassium hydroxide, phosphoric acid (85% w/w), magnesium oxide, sodium carbonate, sodium bicarbonate, calcium carbonate, methanol, Karl- Fischer reagent, silica gel, tert-butylhydroquinone (TBHQ), butylated hydroxytoluene (BHT) and butylated hydroxyanisole (BHA). Activated carbon from coconut husks was used during the oil processing tests. The commercial vegetable insulating oil used (BIOTEMP®) was gently donated by ABB Brazil.

3. Results and Discussion

3.1. Extraction

The seeds were peeled and 38%of the initial mass corresponded to the peels and 62% to the albumens, in accordance with literature values [17] . The yields of oil obtained by mechanical extraction were 8.4 and 20% for the non-peeled seeds and peeled seeds, respectively. These yields were low as expected for this kind of extraction. The average percentage of oil in the non-peeled seeds is 30% and in the albumen is 50% [34] [35] . Consequently, the cakes have a high residual oil value and an additional extraction was necessary.

The extraction of the remaining oil in the cakes was done using the Soxhlet equipment. Thus, combining mechanical and Soxhlet extraction resulted in a yield of 29% of oil for the non-peeled seeds and 37% for the peeled ones (albumens).

The yields for the extraction, by direct contact with hexane, of the remaining oil in the cakes from the mechanical extraction of the peeled seeds, were evaluated as a function of time and hexane proportion used (Table 2).

From the results, presented in Table 2, it can be observed that the oil yield was lower when used 2 mL of hexane per gram of cake. Probably, this can be attributed to the solvent saturation with oil, due to the low amount of solvent used.

For the other conditions evaluated, the maximum extraction was obtained around 30 minutes. For the proportion of 5 mL of hexane per gram of cake, the total yield in oil, by combining mechanical (20.0%) and direct contact with solvent (36.0%), was 48.8%. For the proportion of 10 mL of hexane per gram of cake, the total yield in oil was 50.4%. These results are as expected, once the oil content in albumens of Jatropha curcas is around 50%, as mentioned before. Therefore, considering the small increase in the oil yield by using twice as much solvent, the most adequate parameters for the direct solvent extraction are 5 mL∙g−1, as the ratio hexane/mass of cake, for 30 minutes, yielding 36% of oil.

Regarding the fatty acids composition (Table 3), it was not observed significant difference in the oils obtained by mechanical, Soxhlet and direct solvent extraction. In addition, the oils extracted from the non-peeled and the peeled seeds have similar fatty acids profiles, which are close to the literature values [22] [34] . Some small variation is probably related to the seeds origin, maturation state and seed sampling.

Table 2. Yields of oil obtained from the peeled seeds cake extraction by direct contact with hexane.

Table 3. Fatty acids composition of the oils extracted from the non-peeled seeds and peeled seeds by different methods.

Mech. = Mechanical extraction. *Oil extracted combining mechanical extraction and solvent extraction (Soxhlet) from non-peeled Jatropha curcas seeds.

By comparing the properties of the oils, obtained by three different extraction methods (Table 4), it can be observed that the oils mechanically extracted have a water content slightly higher than that of the oils extracted with solvent. The reason is that, in this process, no hexane, a hydrophobic solvent, is used. Thus, in the other processes, less water is extracted with the oil. The extraction using solvent (by Soxhlet or directly) results in oils with higher acid numbers, since the oil heating applied to remove the solvent, causes some degradation. In addition, the non-peeled seeds oils have a lower acidity than oils from peeled seeds, probably due to the presence of some antioxidant substances in the seed peels [36] [37] . Finally, it can be observed that the viscosity and the density of the obtained oils were not affected either by the extraction method or by the part of the seeds used (whole or peeled).

Concluding, the mechanical extraction in a laboratorial scale resulted in low yields of oil. In addition, the solvent extraction did not affect substantially the oil properties. The oil extraction procedure used thereafter was the direct contact with hexane of crushed seeds, for 30 minutes, in a proportion of 5 mL of hexane per gram of non-peeled seeds. Through this procedure, it was obtained 32% of oil yield, a lower value than the obtained for peeled-seeds. However, the non-peeled seeds were chosen for ease of handling and due to the need of obtaining a significant amount of oil for subsequent processing study and characterization tests.

3.2. Processing

3.2.1. Degumming

The crude Jatropha curcas degumming was evidenced by the sedimentation of an aqueous emulsion, composed of hydrated phosphatides. The analysis of the acid number has shown that the acidity of the crude oil (6.8 mgKOH∙g−1) was reduced to 5.8 mgKOH∙g−1 with the degumming step, as expected, since part of the

Table 4. Properties of the oils obtained from the non-peeled and peeled seeds by mechanical, soxhlet and direct solvent extraction.

*not enough oil to make the test. Mech. = Mechanical extraction.

fatty acids is removed in the process. Consequently, the degumming facilitates the neutralization step by reducing the amount of alkali required.

3.2.2. Neutralization

It was observed a reduction in the oil acidity by the color change of phenolphthalein for the degummed oil (acid number = 5.8 mgKOH∙g−1) neutralizations performed at 90˚C with NaOH, NaHCO3, and Na2CO3 solutions, with the same concentration (10% w/w). However, an excessive formation of soap occurred for NaHCO3 and Na2CO3 solutions, which resulted in a significant loss of neutral oil and did not allow the phase separation. Thus, the acidity of the oil could only be measured for NaOH solution, as shown in Table 5. The reason for the excessive soap formation is the high acidity of the raw oil, once the seeds used in extraction had more than three years [38] [39] .

Then, other concentrations of NaOH solutions were investigated (5% and 0.5% w/w at 90˚C). In these cases, it is also observed an excessive formation of soap. In this way, it was done another experiment using NaOH 0.5% w/w at room temperature (25˚C ± 3˚C), in which 96% of the free fatty acids were neutralized and the soap, neutral oil and aqueous phase could be separated. For this reason, this condition was selected as the more adequate. The yield of this process was 83% but the resulting oil remained with acidity higher than the ASTM D6871 limit value (0.06 mgKOH∙g−1), requiring another neutralization stage.

Tests involving the dry neutralization (with the solids impregnated with NaOH) have facilitated the phase separation, reduced the neutral oil consumption and decreased the water consumption. First, it was tested methanol as solvent for the NaOH dissolution and the best result was obtained with impregnated silica. However, as mentioned, the use of activated carbon is preferable because the silica gel preparation was more complex. In addition, methanol is a reagent with a high toxicity. Then, water was used as solvent and activated carbon as absorbent solid.

As shown in Table 6, the condition of 2 g∙g−1 solid of NaOH and 0.5 g∙g−1 oil of activated carbon resulted in an oil with an acid number of 0.5 mgKOH∙g−1. However, this value is above the ASTM D6871 limit of 0.06 mgKOH∙g−1 and a second neutralization would be required.

Table 5. Alkali neutralization of the degummed oil (acid number = 5.8 mgKOH∙g−1).

*The oil and the alkali solution emulsified, which did not allow acid number measurement.

Table 6. Dry neutralization of the degummed oil (acid number = 5.8 mgKOH∙g−1).

3.2.3. Clarification

In view of the foregoing, the clarification was designed to clarify and neutralize the oil. The combination of 5%w/woil of activated carbon and 1%w/woil of MgO for the oil clarification (Table 7) resulted in a clarified oil with an acid number of 0.04 mgKOH.g−1. As stated in the ASTM D6871 standard, the oil should be bright and clear. Then, to evaluate the oil color before and after the clarification, absorbance of yellow and red colors of oils were measured (Table 8). After the clarification using conditions described above, the yellow and red colors absorbance were reduced to a third and a half, respectively, of the values measured before clarification. Visually, the clarified oil was brighter and clearer than the raw oil (Figure 3).

3.2.4. Drying

The clarified oil (water content = 488 ppm, acid number = 0.04 mgKOH∙g−1), when dried in the stove, had an increase in the acidity (Table 9). Thus, this process oxidized the oil and it was considered inappropriate for drying the oil, since it resulted in an acid number above the standard limit.

On the other hand, using a vacuum rotary evaporator, which reduces the oxygen pressure during the process and allows working in lower temperatures for the oil drying, it was obtained, for both two and four hours, an oil with a low water content and an acid number within the ASTM D6871 standard limits.

Figure 3. (a) Crude and (b) clarified Jatropha curcas oil.

Table 7. Clarification of the neutralized oil (acid number = 0.50 mgKOH∙g−1).

Table 8. Absorbance of yellow and red colors of the oil before and after clarification.

Table 9. Drying of the clarified oil (acid number = 0.04 mgKOH∙g−1).

3.3. Characterization

3.3.1. Standardized Properties

The processed Jatropha curcas oil, obtained after the extraction and processing stages, and the commercial oil, BIOTEMP®, were characterized following the test methods described in ASTM D6871 standard for Natural (Vegetable Oil) Ester Fluids Used in Electrical Apparatus. The results, shown in Table 10, clearly demonstrate that the properties of the processed Jatropha curcas oil meets the specifications of ASTM D6871, for vegetable transformer oil. As expected, the commercial fluid, BIOTEMP®, also meets the requirements.

It is worth to emphasize the lower values of the kinematic viscosities found for the processed oil compared to the ones determined for the BIOTEMP® fluid. In electrical power transformers, the insulating fluid also promotes heat dissipation, usually by natural convection. Thus, oils with lower viscosities can enhance heat dissipation efficiency, which can increase the transformer capacity and lifetime, in addition to more operational safety [2] [6] [9] [12] .

Moreover, the dielectric breakdown voltage of the processed Jatropha curcas oil was significantly higher (55 kV) than the minimum ASTM6871 standard value (30 kV), and also higher than the commercial fluid tested (45 kV). This higher dielectric breakdown value can also increase the safety, lifetime and capacity of power transformers.

In Table 11, the processed Jatropha curcas oil is compared with commercial vegetable insulating fluids. It can be observed that the oil obtained in the present work has similar properties to the oils available in the market. However, it shows a higher value for dielectric strength. The values of flash and fire points, above 300˚C, corroborate the greater security of natural esters insulating fluids.

Table 10. Characterization of processed Jatropha curcas oil and BIOTEMP® and comparison with international standards.

*Property measured by a different test method from the ASTM D6871 standard.

Table 11. Commercial vegetable insulating fluid in comparison with the processed Jatropha curcas oil.

3.3.2. Dynamic Viscosity

Dynamic viscosity testing is not described in ASTM D6871 standard, but it can provide useful information about the rheological behavior of the fluid under shearing and under different thermal conditions. The dried raw and processed Jatropha curcas oils and BIOTEMP® presented a Newtonian behavior at temperatures of 10˚C, 25˚C and 100˚C within a shear rate range of 0.1 to 1000 s−1. In the temperature ramp test (Figure 4), the three oils showed similar profiles concerning the decrease of viscosity with increasing temperature. Above 100˚C, all the oils presented the same dynamic viscosity, but at lower temperatures, the Jatropha curcas oils were less viscous than the BIOTEMP® fluid, confirming the result obtained for the kinematic viscosity. The dried raw oil is significantly less viscous than the processed oil probably due to the elevated content of free fatty acids (smaller molecules) and residual hexane from the solvent extraction. The processed oil presents dynamic viscosities of 0.1212 Pa∙s−1, at 10˚C, 0.0606 Pa∙s−1, at 25˚C, and 0.0077 Pa∙s−1, at 100˚C.

3.3.3. Thermal Properties

In ASTM D6871 standard, there are no required values for the coefficient of expansion and for specific heat, for the vegetable insulating oils. However, this standard gives the typical values for these properties, which are expected to be found in vegetable insulating fluids (Table 12). Both the processed Jatropha curcas oil and the BIOTEMP® fluid tested presented values for the coefficient of expansion and for specific heat within the typical values.

3.4. Accelerated Aging

Fatty acids profiles of the oils submitted to accelerated aging are presented in Table 13. For the processed Jatropha curcas oil without antioxidant, this table shows that after the aging, the percentages of oil in the sample and polyunsaturated fatty acids in the oil have both decreased considerably. In addition, the aged oil without antioxidants presented a higher acid number and viscosity than the oil before aging, as shown in Table 14.

It is known that unsaturated fats are more prone to oxidation [13] . This oxidation increases the free fatty acids amount, because the triglyceride molecule cleavage, leads to hydrogenation of unsaturated fats, and polymerization of trig-

Figure 4. Dynamic Viscosity of the dried and processed Jatropha curcas oils and of BIOTEMP® oil.

Table 12. Thermal properties of the tested oils.

Table 13. Fatty acid profile of oils tested in accelerated aging.

Table 14. Viscosity and acid number of oils tested in accelerated aging.

lycerides [41] . Therefore, the increase in acidity and viscosity observed for the oil without antioxidant demonstrates that this oil was considerably oxidized during its accelerated aging. This result was expected and it confirms the necessity of adding antioxidants to the processed Jatropha curcas oil.

In this sense, it was studied the accelerated aging of the processed Jatropha curcas oil with 1% and 2%w/woil of TBHQ, a common antioxidant used in vegetable oils. As shown in Table 13 and Table 14, the addition of 1% w/woil of TBHQ was not able to prevent the oil oxidation and even cause a negative effect. On the other hand, the addition of 2% w/woil of TBHQ was able to prevent part of the Jatropha curcas oil oxidation during its accelerated aging. As shown in Table 13, reduction in the percentages of oil in the sample and polyunsaturated fatty acids in the oil were considerably smaller for the oil with 2% w/woil of TBHQ than that for the oil without antioxidants. In addition, acid number and viscosity determined for the oil with 2% w/woil of TBHQ after aging were both smaller than that found for the oil without antioxidants, as presented in Table 14.

4. Conclusion

The present work focused on the development of a new vegetable insulating fluid for power transformers based on Jatropha curcas oil. Regarding the oil extraction, the solvent extraction of crushed non-peeled seeds was chosen as the most feasible to an industrial production, with an oil yield of 32%. Further, the raw oil processing was studied. The degumming with phosphoric acid was efficient to remove phosphatides from the crude Jatropha curcas oil. With a NaOH solution (0.5%w/w) at room temperature, 96% of the free fatty acids were neutralized, while by dry neutralization, using activated carbon impregnated with NaOH, an eco-friendly alternative, 92% of the free fatty acids were neutralized. The oil clarification resulted in a bright, odorless and clear oil with an acid number of 0.04 mgKOH∙g−1. The oil drying was able to lower the water content to 177 ppm. Comparing this oil with the main commercial transformer fluids available (BIOTEMP®, Envirotemp FR3®, and Bivolt®), it presents higher dielectric breakdown voltage (55 kV). In addition, it has a lower viscosity than the BIOTEMP® fluid. Moreover, the processed oil flash and fire points of 310˚C and >340˚C, respectively, confirm the great security of vegetable insulating fluids. Preliminary accelerated aging tests showed the necessity of adding antioxidants to the processed Jatropha curcas oil to prevent its oxidation under high temperatures. Finally, it was found that the analyzed properties of the processed oil fulfill all the ASTM D6871, ABNT NBR 15422 and IEC 62770 specifications for new vegetable transformer oil. In conclusion, the Jatropha curcas oil developed in the present work is a great candidate for replacing mineral oils in power transformers.

Acknowledgements

The authors are very grateful to FAPEMIG (Fundação de Amparo à Pesquisa do Estado de Minas Gerais) for the financial support and to all members of the Separation Operations and Processes group from the Department of Chemical Engineering at UFMG who made this work possible.

Conflicts of Interest

The authors declare no conflicts of interest.

References

[1] Herrero, M. and Ibá, E. (2015) Green Processes and Sustainability: An Overview on the Extraction of High Added-Value Products from Seaweeds and Microalgae. The Journal of Supercritical Fluids, 96, 211-216.
[2] Bertrand, Y. and Hoang, L. (2004) Vegetable Oils as Substitute for Mineral Insulating Oils in Medium-Voltage Equipments. Session Cigre, 1-6.
[3] British Consulate (2014) Smart Grid—Enabling Energy Efficiency and Low-Carbon Transition.
https://www.gov.uk/government/uploads/system/uploads/attachment_data/
file/321852/Policy_Factsheet_-_Smart_Grid_Final__BCG_.pdf
[4] Xu, Y., Qian, S., Liu, Q. and Wang, Z. (2014) Oxidation Stability Assessment of a Vegetable Transformer Oil under Thermal Aging. IEEE Transactions on Dielectrics and Electrical Insulation , 21, 683-692.
https://doi.org/10.1109/TDEI.2013.004073
[5] Oommen, T.V. (2002) Vegetable Oils for Liquid-Filled Transformers. IEEE Electrical Insulation Magazine, 18, 6-11.
https://doi.org/10.1109/57.981322
[6] Rafiq, M., Lv, Y.Z., Zhou, Y., Ma, K.B., Wang, W., Li, C.R., et al. (2015) Use of Vegetable Oils as Transformer Oils—A Review. Renewable and Sustainable Energy Reviews, 52, 308-324.
[7] Wilhelm, H., Feitosa, L., Silva, L., Cabrino, A. and Ramos, L. (2015) Evaluation of In-Service Oxidative Stability and Antioxidant Additive Consumption in Corn Oil Based Natural Ester Insulating Fluid. IEEE Transactions on Dielectrics and Electrical Insulation, 22, 864-868.
https://doi.org/10.1109/TDEI.2015.7076786
[8] Garba, Z.N., Gimba, C.E. and Emmanuel, P. (2013) Production and Characterization of Biobased Transformer Oil from Jatropha curcas Seed. Journal of Physical Science, 24, 49-61.
[9] Pukel, G.J., Schwarz, R., Schatzl, F., Baumann, F. and Gerstl, A. (2009) Environmental Friendly Insulating Liquids—A Challenge for Power Transformers. Cigre 6th Southern Africa Regional Conference.
[10] Rycroft, M. (2014) Vegetable Oil as Insulating Fluid for Transformers. Energize, 37-40.
[11] Sitorus, H.B., Beroual, A., Setiabudy, R. and Bismo, S. (2014) Comparison of Streamers Characteristics in Jatropha curcas Methyl Ester Oil and Mineral Oil under Lightning Impulse Voltage. IEEE 18th International Conference on Dielectric Liquids (ICDL), Bled, 29 June-3 July 2014, 1-4.
https://doi.org/10.1109/icdl.2014.6893090
[12] Tenbohlen, S., Koch, M., Vukovic, D., Weinläder, A., Baum, J., Harthun, J. and Dyer, P. (2008) Application of Vegetable Oil-Based Insulating Fluids to Hermetically Sealed Power Transformers. Cigre Session, 42, 24-29.
[13] Jeong, J.I., An, J.S. and Huh, C.S. (2012) Accelerated Aging Effects of Mineral and Vegetable Transformer Oils on Medium Voltage Power Transformers. IEEE Transactions on Dielectrics and Electrical Insulation, 19, 156-161.
https://doi.org/10.1109/TDEI.2012.6148514
[14] Marulanda, A.R., Artigas, M.A., Gavidia, A., Labarca, F. and Paz, N. (2008) Study of the Vegetal Oil as a Substitute for Mineral Oils in Distribution Transformer. Transmission and Distribution Conference and Exposition: Latin America, Bogota, 13-15 August 2008, 1-6.
https://doi.org/10.1109/tdc-la.2008.4641781
[15] Mendes, J.C. (2008) BIOTEMP® óleo Vegetal da ABB Aplicacao em Transformadores de Potência em Alta Tensao. CEPEL, Cigré-Brasil, ABB, Rio de Janeiro.
[16] Ranawana, S., Ekanayaka, C.M.B., Fernando, M.A.R.M. and Perera, K.A.R. (2008) Analysis of Insulation Characteristics of Coconut Oil as an Alternative to the Liquid Insulation of Power Transformers. IEEE Region 10 and the 3rd international Conference on Industrial and Information Systems, Kharagpur, 8-10 December 2008, 1-5.
https://doi.org/10.1109/iciinfs.2008.4798493
[17] Pereira, C. de S.S. (2009) Avaliacao de diferentes tecnologias na extracao do òleo de Pinhao-Manso (Jatropha curcas L). Ph.D. Thesis, Universidade Federal Rural do Rio de Janeiro, Rio de Janeiro.
[18] de Arruda, F.P., De Macedo Beltrao, N., Pereira de Andrade, A., Pereira, W. and Soares Severino, L. (2004) Cultivo de Pinhao manso (Jatropha curcas) como alternativa para o semiárido nordestino. Revista Brasileira de Oleaginosas e Fibrosas, 8, 789-799.
[19] Nery, A.R., Rodrigues, L.N., Silva, M.D., Fernandes, P.D., Chaves, L.H., Dantas Neto, J. and Gheyi, H.R. (2009) Crescimento do pinhao-manso irrigado com águas salinas em ambiente protegido. Revista Brasileira de Engenharia Agrícola e Ambiental, 13, 551-558.
https://doi.org/10.1590/S1415-43662009000500007
[20] Sato, M., Bueno, O. de C., Esperancini, M.S.T. and Frigo, E.P. (2009) A cultura do Pinhao-manso (Jatropha curcas L.): Uso para fins combustíveis e descricao agronOmica. Revista Varia Scientia, 7, 47-62.
[21] Ahmed, W.A. and Salimon, J. (2009) Phorbol Ester as Toxic Constituents of Tropical Jatropha curcas Seed Oil. European Journal of Scientific Research, 31, 429-436.
[22] Araújo, F.D.S., Chaves, M.H. and Araújo, E.C.E. (2007) Caracterizacao do óleo de pinhao-manso (Jatropha curcas L.). Embrapa Meio-Norte, Congresso Internacional de Agroenergia e Biocombustíveis, 1, Teresina. Energia de resultados: palestras e resumos. Teresina: Embrapa Meio-Norte, 2007.
[23] Gunstone, F.D., Harwood, J.L. and Dijkstra, A.J. (2007) The Lipid Handbook with CD-ROM. CRC Press, Boca Raton.
[24] De Greyt, W. and Kellens, M. (2000) Refining Practice. Edible Oil Processing. Blackwell, Danvers, MA, 79-128.
[25] Filleti, W. (2000) Refino a Seco de óleo de Soja. Ph.D. Thesis, Campinas State University, Campinas.
[26] De Greyt, W. (2013) Edible Oil Refining: Current and Future Technologies. Edible Oil Processing. John Wiley & Sons, Ltd., Hoboken, 127-151.
https://doi.org/10.1002/9781118535202.ch5
[27] Tenbohlen, S. and Koch, M. (2010) Aging Performance and Moisture Solubility of Vegetable Oils for Power Transformers. IEEE Transactions on Power Delivery, 25, 825-830.
https://doi.org/10.1109/TPWRD.2009.2034747
[28] Thanigaiselvan, R., Raja, T.S.R. and Karthik, R. (2015) Investigations on Eco Friendly Insulating Fluids from Rapeseed and Pongamia Pinnata Oils for Power Transformer Applications. Journal of Electrical Engineering & Technology, 10, 2348-2355.
https://doi.org/10.5370/jeet.2015.10.6.2348
[29] ASTM (2008) ASTM D6871: Standard Specification for Natural (Vegetable Oil) Ester Fluids Used in Electrical. ASTM.
[30] IEC (2013) IEC 62770: Fluids for Electrotechnical Applications-Unused Natural Esters for Transformers and Similar Electrical Equipment. International Electrotechnical Commission, Switzerland.
[31] Associacao Brasileira de Normas Técnicas (ABNT) (2006) ABNT NBR 15422:2006-Insulating Vegetable Oil for Electrical Apparatus. Brazil.
[32] Gómez, N.A., Wilhelm, H.M., Santos, C.C. and Stocco, G.B. (2014) Dissolved Gas Analysis (DGA) of Natural Ester Insulating Fluids with Different Chemical Compositions. IEEE Transactions on Dielectrics and Electrical Insulation, 21, 1071-1078.
https://doi.org/10.1109/TDEI.2014.6832250
[33] Fani, M. (2015) Antioxidantes—Tipos e Mecanismos de Acao. Revista Aditivos & Ingredientes, 36-57.
[34] Freire, L.M.S., Bicudo, T.C., Rosenhaim, R., SinfrOnio, F.S.M., Botelho, J.R., Carvalho Filho, J.R., et al. (2009) Thermal Investigation of Oil and Biodiesel from Jatropha curcas L. Journal of Thermal Analysis and Calorimetry, 96, 1029-1033.
https://doi.org/10.1007/s10973-009-0055-y
[35] Shah, S., Sharma, A. and Gupta, M.N. (2004) Extraction of Oil from Jatropha curcas L. Seed Kernels by Enzyme Assisted Three Phase Partitioning. Industrial Crops and Products, 20, 275-279.
[36] Igbinosa, O.O., Igbinosa, I.H., Chigor, V.N., Uzunuigbe, O.E., Oyedemi, S.O., Odjadjare, E.E., et al. (2011) Polyphenolic Contents and Antioxidant Potential of Stem Bark Extracts from Jatropha curcas (Linn). International Journal of Molecular Sciences, 12, 2958-2971.
https://doi.org/10.3390/ijms12052958
[37] Oskoueian, E., Abdullah, N., Saad, W.Z., Omar, A.R., et al. (2011) Antioxidant, Anti-Inflammatory and Anticancer Activities of Methanolic Extracts from Jatropha curcas Linn. Journal of Medicinal Plants Research, 5, 49-57.
[38] Zeldenrust, R.S. (2012) Alkali Refining: Edible Oil Processing. AOCS Lipid Library.
http://lipidlibrary.aocs.org/OilsFats/content.cfm?ItemNumber=40319
[39] O’Brien, R.D., Farr, W.E. and Wan, P.J. (2000) Introduction to Fats and Oils Technology. AOCS Press.
[40] Gomez, N.A., Abonia, R., Cadavid, H. and Vargas, I.H. (2011) Chemical and Spectroscopic Characterization of a Vegetable Oil Used as Dielectric Coolant in Distribution Transformers. Journal of the Brazilian Chemical Society, 22, 2292-2303.
[41] Yao, S., Li, J., Li, L., Liao, R. and Zhou, J. (2014) Comparison Analysis to Thermal Aging Properties of Vegetable and Mineral Insulating Oils. International Conference on High Voltage Engineering and Application (ICHVE), Poznan, 8-11 September 2014, 1-4.
https://doi.org/10.1109/ICHVE.2014.7035397

Copyright © 2024 by authors and Scientific Research Publishing Inc.

Creative Commons License

This work and the related PDF file are licensed under a Creative Commons Attribution 4.0 International License.