Takada, Y., Nakajima, H., Okuno, O. and Okabe, T. (2001) Released Ions and Microstructures of Dental Cast Experimental Ti-Ag Alloys. Dental Materials Journal, 20, 34-52.
https://doi.org/10.4012/dmj.20.34

has been cited by the following article:

• TITLE: Corrosion Behaviour of Zr-Ag Alloys for Dental Implant Application

  AUTHORS: Francesco Rosalbino, Daniele Macciò, Giorgio Scavino

  KEYWORDS: Zr-Ag Alloys, Corrosion Resistance, Open Circuit Potential, Potentiodynamic Polarization Curves, Electrochemical Impedance Spectroscopy (EIS)

  JOURNAL NAME: Materials Sciences and Applications, Vol.14 No.11, November 14, 2023

  ABSTRACT: The electrochemical corrosion behaviour of three Zr-Ag alloys (Zr-1Ag, Zr-3Ag and Zr-5Ag) was investigated. Open circuit potential, linear potentiodynamic polarization and electrochemical impedance spectroscopy (EIS) techniques were employed in aerated artificial saliva (pH = 4.0) at 37°C. Silver alloying additions are found to be effective in enhancing the corrosion resistance of zirconium in artificial saliva environment. In fact, Zr-Ag alloys exhibit higher open circuit potentials, larger breakdown potentials and higher impedance values as compared to cp Zr. This behaviour can be ascribed to the formation of a thicker and more stable passive film with increasing compactness, able to provide better protection against the corrosion attack.